RESUMEN
Starch [(C6H10O5) n ]-stabilized bismuth sulfide (Bi2S3) nanoparticles (NPs) were synthesized in a single-pot reaction using bismuth nitrate pentahydrate (Bi(NO3)3·5H2O) and sodium sulfide (Na2S) as precursors. Bi2S3 NPs were stable over time and a wide band gap of 2.86 eV was observed. The capping of starch on the Bi2S3 NPs prevents them from agglomeration and provides regular uniform shapes. The synthesized Bi2S3 NPs were quasispherical, and the measured average particle size was â¼11 nm. The NPs are crystalline with an orthorhombic structure as determined by powder X-ray diffraction and transmission electron microscopy. The existence and interaction of starch on the NP's surface were analyzed using circular dichroism. Impedance spectroscopy was used to measure the electronic behavior of Bi2S3 NPs at various temperatures and frequencies. The dielectric measurements on the NPs show high dielectric polarizations. Furthermore, it was observed that the synthesized Bi2S3 NPs inhibited bacterial strains (Bacillus subtilis, Escherichia coli, Pseudomonas aeruginosa, and Staphylococcus aureus) and demonstrated substantial antibacterial activity.
RESUMEN
Silicon nanowires grown using the vapor-liquid-solid method are promising candidates for nanoelectronics applications. The nanowires grow from an Au-Si catalyst during silicon chemical vapor deposition. In this paper, the effect of temperature, oxide at the interface and substrate orientation on the nucleation and growth kinetics during formation of nanogold silicide structures is explained using an oxide mediated liquid-solid growth mechanism. Using real time in situ high temperature transmission electron microscopy (with 40 ms time resolution), we show the formation of high aspect ratio ( approximately 15.0) aligned gold silicide nanorods in the presence of native oxide at the interface during in situ annealing of gold thin films on Si(110) substrates. Steps observed in the growth rate and real time electron diffraction show the existence of liquid Au-Si nano-alloy structures on the surface besides the un-reacted gold nanostructures. These results might enable us to engineer the growth of nanowires and similar structures with an Au-Si alloy as a catalyst.