RESUMEN
STATEMENT OF PROBLEM: Several additively and subtractively manufactured resin-based materials indicated for interim and definitive fixed dental prostheses have been launched. However, knowledge of the bond strength of these materials to different implant abutment materials is limited. PURPOSE: The purpose of this in vitro study was to evaluate the shear bond strength (SBS) of additively and subtractively manufactured resin-based materials to different implant abutment materials. MATERIAL AND METHODS: One hundred and ten disk-shaped specimens (Ø3×3 mm) were fabricated either additively from 2 resins indicated for definitive use (Crowntec; AM_CT and VarseoSmile Crown Plus; AM_VS) and 1 resin indicated for interim use (FREEPRINT temp; AM_FP) or subtractively from a nanographene-reinforced polymethyl methacrylate (G-CAM; SM_GC) and a high-impact polymer composite (breCAM.HIPC; SM_BC). After allocating 2 specimens from each group for scanning electron microscope evaluation, the specimens were divided according to the abutment material (CopraPeek; polyetheretherketone, PEEK and Dentium Superline Pre-Milled Abutment; titanium, Ti) (n=10). All specimens were airborne-particle abraded with 50-µm aluminum oxide. After applying a resin primer (Visio.link) to PEEK and an adhesive primer (Clearfil Ceramic Primer Plus) to Ti specimens, a self-adhesive resin cement (PANAVIA SA Cement Universal) was used for cementation. All specimens were stored in distilled water (24 hours, 37 °C), and a universal testing device was used for the SBS test. SBS data were analyzed with 2-way analysis of variance and Tukey honestly significant difference tests, while the chi-squared test was used to evaluate the difference among the abutment-resin pairs in terms of failure modes (α=.05). RESULTS: The interaction between the material type and the abutment type and the main factor of material type affected the SBS (P<.001). SM_BC-PEEK and SM_GC had the lowest SBS followed by SM_BC-Ti, whereas AM_VS-PEEK had the highest SBS (P≤.001). AM_CT-Ti had higher SBS than AM_FP-PEEK (P=.026). SM_GC had the lowest and AM_VS had the highest SBS, while AM_CT and AM_FP had higher SBS than SM_BC (P≤.004). The distribution of failure modes was significantly different among tested material-abutment pairs, and only for AM_CT among tested materials (P≤.025). Most of the material-abutment pairs had a minimum of 80% adhesive failures. CONCLUSIONS: Regardless of the abutment material, additively manufactured specimens had higher bond strength and one of the subtractively manufactured materials (SM_GC) mostly had lower bond strength. The abutment material had a small effect on the bond strength. Adhesive failures were observed most frequently.
RESUMEN
This study aimed to evaluate the effect of airborne particle abrasion with different particles on the surface free energy, roughness, and biaxial flexural strength of a feldspathic ceramic by comparing it with hydrofluoric acid etching, the standard surface treatment, and polishing. Square-shaped feldspathic ceramic specimens (12 mm × 12 mm × 1.2 mm) were divided into subgroups as airborne particles abraded with alumina (AO3a, AO3b, AO25, AO50a, AO50b, AO90, AO110a, AO110b, AO120a, and AO120b), silica (SO50a, SO50b, SO100, and SO100/200), or nutshell granule (NS100/200), hydrofluoric acid etched, and polished (n = 12). Surface free energy (n = 5), roughness (n = 5), biaxial flexural strength (n = 12), and Weibull moduli (n = 12) were investigated. Data were evaluated with 1-way ANOVA and Tukey HSD tests, and possible correlations were investigated with Pearson's correlation (α = 0.05). SO100/200 mostly had lower surface free energy (p ≤ 0.011), and polishing and etching led to higher surface free energy than AO3a, AO3b, and AO120a (p ≤ 0.031). Polished, SO100, and SO50b specimens mostly had lower roughness and AO125 had the highest roughness (p ≤ 0.029). SO100/200 mostly had lower biaxial flexural strength (p ≤ 0.041), and etched specimens had higher biaxial flexural strength than AO120a, AO120b, and SO50b (p ≤ 0.043). AO3b had the highest (33.56) and AO120b had the lowest (11.8) Weibull modulus. There was a weak positive correlation between the surface free energy and the biaxial flexural strength (r = 0.267, p = 0.011). A larger particle size mostly resulted in higher roughness, which was also affected by the particle shape. Most of the test groups had similar biaxial flexural strength to that of the hydrofluoric acid-etched group. Therefore, for tested feldspathic ceramic, airborne particle abrasion with tested parameters may be a suitable alternative without causing any further damage.
RESUMEN
STATEMENT OF PROBLEM: Additive and subtractive manufacturing have become alternative technologies for fabricating occlusal devices. However, knowledge of the long-term stability of occlusal devices fabricated using these recent technologies is limited. PURPOSE: The purpose of this in vitro study was to evaluate the cameo and intaglio surface stability and variability of additively, subtractively, and conventionally manufactured occlusal devices after 18 months of storage. MATERIAL AND METHODS: A standard tessellation language (STL) file of a dentate maxillary typodont was used to design a master occlusal device. The STL file of this design was used to fabricate occlusal devices additively either with a digital light processing (AM-1) or a continuous liquid interface production (AM-2) printer, subtractively with 2 different 5-axis milling units (SM-1 and SM-2), and conventionally (TM-HP) (n=10). STL files of each device's cameo and intaglio surfaces were generated using a laboratory scanner after fabrication and after 18 months of storage in a moist environment. These generated files were imported into an analysis software program (Geomagic Control X) to analyze the dimensional stability of tested devices by using the root mean square method. The average deviation values defined the variability of measured changes over time. Cameo and intaglio surface deviations were analyzed using the Kruskal-Wallis and Dunn tests, while the variability of measured deviations was analyzed with 1-way analysis of variance and the Tukey HSD tests (α=.05). RESULTS: Significant differences were observed among tested devices when the intaglio surface deviations and the cameo surface variability were considered (P<.001). SM-2 had significantly higher intaglio surface deviations than AM-1, SM-1, and AM-2 (P≤.036). Among the test groups, AM-1 had the greatest cameo surface variability (P≤.004). CONCLUSIONS: SM-2 resulted in lower intaglio surface stability than the additive and the other subtractive manufacturing technologies, while AM-1 led to the highest cameo surface variability among the test groups.
RESUMEN
BACKGROUND: There is limited knowledge on the fabrication trueness and fit of additively or subtractively manufactured complete-arch implant-supported frameworks in recently introduced polymers. PURPOSE: To evaluate the trueness and marginal fit of additively or subtractively manufactured polymer-based complete-arch implant-supported frameworks, comparing with those of strength gradient zirconia frameworks. MATERIALS AND METHODS: A typodont model with 4 implants (left first molar (abutment 1), left canine (abutment 2), right canine (abutment 3), and right first molar (abutment 4)) was digitized (ATOS Core 80 5MP) and an implant-supported complete-arch framework was designed. This design file was used to fabricate frameworks from 5 different materials: strength gradient zirconia (SM-ZR), high impact polymer composite (SM-CR), nanographene-reinforced PMMA (SM-GR), PMMA (SM-PM), and additively manufactured temporary resin (AM) (n = 10). These frameworks were digitized and each scan file was virtually segmented into 4 regions (abutments, occlusal, overall without occlusal, and overall). The surface deviations at these regions, and linear and interimplant distance deviations were evaluated (Geomagic Control X). Marginal gaps were evaluated according to triple-scan protocol after seating frameworks on the model with the 1-screw test. Data were statistically analyzed (α = 0.05). RESULTS: Surface deviations of all regions differed among tested materials (p ≤ 0.001). AM frameworks mostly had surface deviations that were similar to or lower than those of other materials (p ≤ 0.031), except for the occlusal surface, where it mostly had higher deviations (p ≤ 0.013). Abutment 4 of SM-CR had higher linear deviations than abutment 2 (p = 0.025), and material type did not affect the linear deviations within abutments (p ≥ 0.171). Interimplant distance deviations differed within and among materials (p ≤ 0.017), except for those between abutments 1 and 2 among materials (p = 0.387). Marginal gaps of subtractively manufactured materials differed among abutments, while those of abutments 3 and 4 differed among materials (p ≤ 0.003). AM frameworks mostly had lower marginal gaps at abutments 3 and 4 (p ≤ 0.048). CONCLUSIONS: Although there was no clear trend among tested materials for measured deviations, marginal gaps of additively manufactured resin were mostly lower than those of subtractively manufactured materials and did not differ among abutment sites. Nevertheless, the differences in measured deviations among materials were small and marginal gaps were within the previously reported acceptability thresholds.
RESUMEN
OBJECTIVES: To evaluate the fabrication trueness of additively manufactured maxillary definitive casts with various tooth preparations fabricated with different 3-dimensional (3D) printers and print orientations. METHODS: A maxillary typodont with tooth preparations for a posterior 3-unit fixed partial denture, lateral incisor crown, central incisor and canine veneers, first premolar and second molar inlays, and a first molar crown was digitized with an industrial scanner. This scan file was used to fabricate definitive casts with a digital light processing (DLP) or stereolithography (SLA) 3D printer in different orientations (0-degree, 30-degree, 45-degree, and 90-degree) (n = 7). All casts were digitized with the same scanner, and the deviations within each preparation site were evaluated. Generalized linear model analysis was used for statistical analysis (α = 0.05). RESULTS: The interaction between the 3D printer and the print orientation affected measured deviations within all preparations (P ≤ 0.001) except for the lateral incisor crown and canine veneer (P ≥ 0.094), which were affected only by the main factors (P < 0.001). DLP-90 mostly led to the highest and DLP-0 mostly resulted in the lowest deviations within posterior tooth preparations (P ≤ 0.014). DLP-30 led to the lowest deviations within the first premolar inlay and DLP-45 led to the lowest deviations within the central incisor veneer preparation (P ≤ 0.045). CONCLUSIONS: Posterior preparations of tested casts had the highest trueness with DLP-0 or DLP-30, while central incisor veneer preparations had the highest trueness with DLP-45. DLP-90 led to the lowest trueness for most of the tooth preparations. CLINICAL SIGNIFICANCE: Definitive casts with tooth preparations fabricated with the tested DLP 3D printer and the print orientation adjusted on tooth preparation may enable well-fitting restorations. However, 90-degree print orientation should be avoided with this 3D printer, as it led to the lowest fabrication trueness.
Asunto(s)
Diseño Asistido por Computadora , Coronas con Frente Estético , Modelos Dentales , Impresión Tridimensional , Humanos , Diente Molar , Incisivo/anatomía & histología , Dentadura Parcial Fija , Incrustaciones , Preparación Protodóncica del Diente/métodos , Estereolitografía , Diseño de Prótesis Dental , Diente Canino/anatomía & histología , Diente Premolar , Maxilar/anatomía & histología , Corona del Diente/anatomía & histología , Técnica de Impresión Dental/instrumentación , Técnica de Colado Dental , Procesamiento de Imagen Asistido por Computador/métodos , CoronasRESUMEN
STATEMENT OF PROBLEM: Studies on the effect of barium silicate on the material properties of additively manufactured (AM) resins containing 2-methacryloyloxyethyl phosphorylcholine (MPC) for dental applications are lacking. PURPOSE: The purpose of this in vitro study was to evaluate the mechanical properties, transmittance, and protein adsorption of MPC-containing AM resin incorporated with different barium silicate contents and to compare these findings with those of a commercially available unfilled AM resin marketed for definitive restorations. MATERIAL AND METHODS: Resins incorporating 6 wt% MPC and 4 different concentrations of barium silicate (10 wt%, MB10; 20 wt%, MB20; 30 wt%, MB30; and 40 wt%, MB40) were prepared. An MPC-containing resin with no filler was also prepared (0 wt%, MBN). Surface roughness (n=15), Vickers hardness (n=15), flexural strength and modulus (n=15), fracture toughness (n=15), transmittance (n=15), and protein adsorption (n=3) of the filled resin specimens were measured and compared with those of commercially available unfilled resin specimens. All data were analyzed using the Kruskal-Wallis and Dunn tests (α=.05). RESULTS: All experimental resins had higher surface roughness than the unfilled resin (P≤.048). MB40 had higher hardness, flexural strength, flexural modulus, and fracture toughness than most other groups (P≤.047). MB10 had higher transmittance than most other groups (P≤.012). All experimental resins had lower protein adsorption than the unfilled resin, regardless of the barium silicate content (P≤.023). CONCLUSIONS: The experimental resin containing 6 wt% MPC and 40 wt% barium silicate showed better mechanical properties and lower protein adsorption than the resin with no MPC or ceramic fillers. Transmittance decreased with the increase of barium silicate in the resins.
Asunto(s)
Ensayo de Materiales , Silicatos , Propiedades de Superficie , Silicatos/química , Adsorción , Polímeros/química , Compuestos de Bario/química , Metacrilatos/química , Fosforilcolina/química , Fosforilcolina/análogos & derivados , Proteínas/química , Técnicas In Vitro , Resistencia Flexional , Dureza , Materiales Dentales/químicaRESUMEN
This study aimed to evaluate the dimensional stability of maxillary diagnostic casts fabricated from a biobased model resin, which consists of 50% renewable raw materials for sustainable production, a model resin, and stone, over one month. A master maxillary stone cast was digitized with a laboratory scanner to generate a reference file. This master cast was also scanned with an intraoral scanner to additively manufacture casts with a biobased model resin (BAM) and a model resin (AM). Polyvinylsiloxane impressions of the master cast were also made and poured in type III stone (CV) (n = 8). The same laboratory scanner was used to digitize each model one day (T0), 1 week (T1), 2 weeks (T2), 3 weeks (T3), and 4 weeks (T4) after fabrication. Deviations from the reference file were calculated with an analysis software and analyzed with generalized linear model analysis (α = 0.05). The interaction between the material and the time point affected measured deviations (p < 0.001). Regardless of the time point, CV had the lowest and AM had the highest deviations (p < 0.001). BAM mostly had lower deviations at T0 and mostly had higher deviations at T4 (p ≤ 0.011). AM had the highest deviations at T4 and then at T3, whereas it had the lowest deviations at T0 (p ≤ 0.002). The measured deviations of CV increased after each time point (p < 0.001). BAM casts had deviations within the previously reported clinically acceptable thresholds over one month and had acceptable dimensional stability. Therefore, tested biobased resin may be a viable alternative for the sustainable manufacturing of maxillary diagnostic casts that are to be used clinically.
RESUMEN
OBJECTIVE: To evaluate how restorative material, resin cement, and cyclic loading affect the fracture resistance of resin-based crowns fabricated by using additive or subtractive manufacturing. METHODS: A right first molar crown standard tessellation language (STL) file was used to fabricate 120 crowns from one subtractively manufactured polymer-infiltrated ceramic network (SM) and two additively manufactured resin composites (AM-B and AM-S) (N = 40). These crowns were randomly divided into 4 groups within each material according to the dual-polymerizing resin cement to be used (RX and PN) and the aging condition (n = 10). After cementation, the crowns without cyclic loading were subjected to fracture testing, while the others were first cyclically loaded (1.7 Hz, 1.2 million cycles, and 49-N load) and then subjected to fracture testing. Data were analyzed with generalized linear model analysis (α = .05). RESULTS: Fracture resistance of the crowns was affected by material, resin cement, and cyclic loading (P ≤ .030). However, none of the interactions significantly affected fracture resistance of tested crowns (P ≥ .140). Among tested materials, SM had the highest fracture resistance, whereas AM-B had the lowest (P ≤ .025). RX led to higher fracture resistance, and cyclic loading decreased the fracture resistance (P ≤ .026). SIGNIFICANCE: Tested materials can be considered reliable in terms of fracture resistance in short- or mid-term (5 years of intraoral simulation) when used for single molar crowns with 2 mm occlusal thickness. In the long term, polymer-infiltrated ceramic network crowns cemented with RelyX Universal may provide promising results and be less prone to complications considering higher fracture resistance values obtained.
Asunto(s)
Resinas Compuestas , Coronas , Fracaso de la Restauración Dental , Análisis del Estrés Dental , Ensayo de Materiales , Cementos de Resina , Cementos de Resina/química , Resinas Compuestas/química , Diseño de Prótesis Dental , Cerámica/química , Diente Molar , Materiales Dentales/químicaRESUMEN
Effect of model resin and shaft taper angle on the trueness and fit of additively manufactured removable dies in narrow ridge casts Purpose. To evaluate how model resin and shaft taper affect the trueness and fit of additively manufactured removable dies in narrow ridge casts. MATERIAL AND METHODS: A typodont model with a prepared mandibular molar was scanned to design virtual dies with different shaft tapers (0-degree (straight), 5-degree, and 10-degree tapered). Fifteen dies and one hollowed cast per taper were additively manufactured from two resins (G-PRINT 3D Model, GP and DentaMODEL, DM). Dies and casts were digitized to evaluate their trueness (root mean square (RMS)). The fit of the dies was evaluated with crown portion's RMS when seated in the cast and with distance deviations. Kruskal-Wallis and Mann-Whitney U tests were used to analyze data (α =.05). RESULTS: GP dies had lower overall, root, and base RMS, while DM dies had lower crown RMS (P≤.016). Straight dies had the highest overall, root, and base RMS within GP (P≤.030). Ten-degree dies had the lowest overall and base RMS, lower crown RMS than straight, and lower root RMS than 5-degree dies within DM (P≤.047). When the dies were seated, GP had lower crown portion RMS within 5- and 10-degree dies, and 5-degree dies had the highest RMS within DM (P≤.003). GP had lower distance deviations within 5- and 10-degree dies. Five-degree dies had the highest deviations within DM (P≤.049). CONCLUSIONS: GP dies mostly had higher trueness and better fit. Straight dies mostly had lower trueness within GP. Ten-degree taper mostly led to higher trueness within DM. The shaft taper affected DM dies' fit.
RESUMEN
This study aimed to evaluate the effect of ceramic type, firing tray, and firing substrate on the density, shrinkage, biaxial flexural strength, Martens' hardness, and elastic indentation modulus of zirconia veneering ceramics. Disk-shaped specimens were fabricated from a high-fusing (HFZ) and a low-fusing (STR) zirconia veneering ceramic. These specimens were then divided into 10 groups according to firing trays (round, small honeycomb-shaped, cordierite [RSC]; round, large honeycomb-shaped, aluminum oxide [RLA]; rectangular, plane, silicon nitride [RCPS]; round, plane, silicon nitride [RPS]; and rectangular, plane, calcium silicate [RCPC]) and firing substrates (firing cotton and platinum foil) used (n = 12). The density, shrinkage, biaxial flexural strength, Martens' hardness, and indentation modulus were measured, and analyzed with generalized linear model analysis (α = 0.05). The interaction between the ceramic type and firing substrate affected density (p < 0.001), and the other outcomes were affected by the interaction among all main factors (p ≤ 0.045). Higher density was observed with HFZ or platinum foil (p ≤ 0.007). RSC and RLA led to a higher density than RCPS within HFZ and led to the lowest density within STR (p ≤ 0.046). STR had a higher shrinkage (p < 0.001). RSC mostly led to a lower shrinkage of HFZ (p ≤ 0.045). The effect of ceramic type and firing substrates on the biaxial flexural strength, Martens' hardness, and indentation modulus was minimal while there was no clear trend on the effect of firing tray on these properties. Ceramic type, firing tray, and firing substrate affected the mechanical properties of the tested zirconia veneering ceramics. Firing the tested zirconia veneering ceramics over a round and small honeycomb-shaped cordierite firing tray with firing cotton mostly led to improved mechanical properties.
RESUMEN
OBJECTIVES: To evaluate the positional accuracy of implant analogs in biobased model resin by comparing them to that of implant analogs in model resin casts and conventional analogs in dental stone casts. METHODS: Polyvinylsiloxane impressions of a partially edentulous mandibular model with a single implant were made and poured in type IV dental stone. The same model was also digitized with an intraoral scanner and additively manufactured implant casts were fabricated in biobased model resin (FotoDent biobased model) and model resin (FotoDent model 2 beige-opaque) (n = 8). All casts and the model were digitized with a laboratory scanner, and the scan files were imported into a 3-dimensional analysis software (Geomagic Control X). The linear deviations of 2 standardized points on the scan body used during digitization were automatically calculated on x-, y-, and z-axes. Average deviations were used to define precision, and 1-way analysis of variance and Tukey HSD tests were used for statistical analyses (α = 0.05). RESULTS: Biobased model resin led to higher deviations than dental stone (all axes, P ≤ 0.031) and model resin (y-axis, P = 0.015). Biobased model resin resulted in the lowest precision of implant analog position (P ≤ 0.049). The difference in the positional accuracy of implant analogs of model resin and stone casts was nonsignificant (P ≥ 0.196). CONCLUSIONS: Implant analogs in biobased model resin casts mostly had lower positional accuracy, whereas those in model resin and stone casts had similar positional accuracy. Regardless of the material, analogs deviated more towards mesial, while buccal deviations in additively manufactured casts and lingual deviations in stone casts were more prominent.
Asunto(s)
Diseño Asistido por Computadora , Materiales de Impresión Dental , Técnica de Impresión Dental , Modelos Dentales , Polivinilos , Siloxanos , Humanos , Polivinilos/química , Siloxanos/química , Materiales de Impresión Dental/química , Diseño de Prótesis Dental , Imagenología Tridimensional/métodos , Sulfato de Calcio/química , Resinas Sintéticas/química , Implantes Dentales , Mandíbula , Técnica de Colado Dental , Ensayo de MaterialesRESUMEN
STATEMENT OF PROBLEM: Cantilevered complete arch implant-supported prostheses are commonly fabricated from zirconia and more recently from strength gradient zirconia. Different polymer-based materials indicated for definitive fixed prostheses that could be used with additive or subtractive manufacturing have also been marketed recently. However, knowledge on the long-term fatigue behavior of cantilevered implant-supported prostheses made from these polymer-based materials and strength gradient zirconia is lacking. PURPOSE: The purpose of this in vitro study was to evaluate the fatigue behavior of implant-supported cantilevered prostheses of recently introduced computer-aided design and computer-aided manufacturing polymers and zirconia. MATERIAL AND METHODS: A master standard tessellation language file of a 9×11×20-mm specimen with a titanium base (Ti-base) space that represented an implant-supported cantilevered prosthesis was used to fabricate specimens from additively manufactured interim resin (AM), polymethyl methacrylate (SM-PM), nanographene-reinforced polymethyl methacrylate (SM-GR), high-impact polymer composite resin (SM-CR), and strength gradient zirconia (SM-ZR) (n=10). Each specimen was prepared by following the respective manufacturer's recommendations, and Ti-base abutments were cemented with an autopolymerizing luting composite resin. After cementation, the specimens were mounted in a mastication simulator and subjected to 1.2 million loading cycles under 100 N at 1.5 Hz; surviving specimens were subjected to another 1.2 million loading cycles under 200 N at 1.5 Hz. The load was applied to the cantilever extension, 12-mm from the clamp of the mastication simulator. The Kaplan-Meier survival analysis and Cox proportional hazards model were used to evaluate the data (α=.05). RESULTS: Significant differences in survival rate and hazard ratio were observed among materials (P<.001). Among tested materials, SM-ZR had the highest and AM had the lowest survival rate (P≤.031). All materials had a significantly higher hazard ratio than SM-ZR (P≤.011) in the increasing order of SM-GR, SM-PM, SM-CR, and AM. CONCLUSIONS: SM-ZR had the highest survival rate with no failed specimens. Even though most of the tested polymer-based materials failed during cyclic loading, these failures were commonly observed during the second 1.2 million loading cycles with 200 N. All materials had a higher hazard ratio than SM-ZR.
RESUMEN
To investigate how patterns generated by femtosecond (fs) laser and femtosecond laser power affect the surface roughness (Ra) and biaxial flexural strength (BFS) of monolithic zirconia. Eighty disk-shaped zirconia specimens were divided into eight subgroups (n = 10): Control (C), airborne-particle abrasion (APA), 400 mW fs laser (spiral [SP(400)], square [SQ(400)], circular [CI(400)]), and 700 mW fs laser ([SP(700)], [SQ(700)], [CI(700)]). Ra values were calculated by using a surface profilometer. One additional specimen per group was analyzed with scanning electron microscopy and x-ray diffractometry. BFS values were obtained by using the piston-on-3-ball test. One-way ANOVA and either Tukey's HSD (BFS) or Tamhane's T2 (Ra) tests were used to evaluate data (α = 0.05). Regardless of the pattern and power, fs laser groups had higher Ra than C and APA, while SP groups had lower Ra than CI and SQ groups (p ≤ 0.004). For each pattern, Ra increased with higher laser power (p < 0.001), while the laser power did not affect the BFS (p ≥ 0.793). CI and SQ groups had lower BFS than the other groups (p ≤ 0.040), whereas SP groups had similar BFS to C and APA (p ≥ 0.430). Fs laser microstructuring with spiral surface pattern increased the Ra without jeopardizing the BFS of zirconia. Thus, this treatment might be an option to roughen tested zirconia.
Asunto(s)
Rayos Láser , Ensayo de Materiales , Propiedades de Superficie , Circonio , Circonio/química , Resistencia Flexional , Microscopía Electrónica de RastreoRESUMEN
STATEMENT OF PROBLEM: Additive (AM) and subtractive (SM) manufacturing have become popular for fabricating occlusal devices with materials of different chemical compositions. However, knowledge on the effect of material and antagonist type on the wear characteristics of occlusal devices fabricated by using different methods is limited. PURPOSE: The purpose of this in vitro study was to evaluate the effect of material and antagonist type on the wear of occlusal devices fabricated by using conventional manufacturing, AM, and SM. MATERIAL AND METHODS: Two-hundred and forty Ø10×2-mm disk-shaped specimens were fabricated by using heat-polymerized polymethylmethacrylate (control, CM), AM clear device resin fabricated in 3 different orientations (horizontal [AMH], diagonal [AMD], and vertical [AMV]), SM polymethylmethacrylate (SMP), and SM ceramic-reinforced polyetheretherketone (SMB) (n=40). Specimens were then divided into 4 groups based on the antagonists: steatite ceramic (SC); multilayered zirconia (ZR); lithium disilicate (EX); and zirconia-reinforced lithium silicate (ZLS) used for thermomechanical aging (n=10). After aging, the volume loss (mm3) and maximum wear depth (µm) were digitally evaluated. Data were analyzed with 2-way analysis of variance and Tukey honestly significant difference tests (α=.05). RESULTS: The interaction between the device material and the antagonist affected volume loss and maximum depth of wear (P<.001). AMH had volume loss and depth of wear that was either similar to or higher than those of other materials (P≤.044). When SC was used, CM had higher volume loss and depth of wear than AMV, and, when EX was used, AMD had higher volume loss and depth of wear than SMP (P≤.013). SC and ZR led to higher volume loss of CM and AMH than EX and led to the highest depth of wear for these materials, while ZR also led to the highest volume loss and depth of wear of AMD and AMV (P≤.019). EX led to the lowest volume loss and depth of wear of AMV and SMP and to the lowest depth of wear of AMH (P≤.021). Regardless of the antagonist, SMB had the lowest volume loss and depth of wear (P≤.005). CONCLUSIONS: AMH mostly had higher volume loss and depth of wear, while SMB had the lowest volume loss, and its depth of wear was not affected by the tested antagonists. ZR mostly led to higher volume loss and maximum depth of wear, while EX mostly led to lower volume loss and maximum depth of wear of the tested occlusal device materials.
Asunto(s)
Materiales Dentales , Ensayo de Materiales , Polimetil Metacrilato , Circonio , Materiales Dentales/química , Polimetil Metacrilato/química , Circonio/química , Cerámica/química , Humanos , Técnicas In Vitro , Ferulas Oclusales , Alisadura de la Restauración Dental , Diseño de Prótesis Dental , Benzofenonas , Porcelana Dental/química , Polímeros/química , Propiedades de Superficie , Polietilenglicoles/química , Cetonas/químicaRESUMEN
OBJECTIVES: To evaluate whether post-milling firing and material type affect the fabrication trueness and internal fit of lithium disilicate crowns. METHODS: A prefabricated cobalt chromium abutment was digitized to design a mandibular right first molar crown. This design file was used to fabricate crowns from different lithium disilicate ceramics (nano-lithium disilicate (AM), fully crystallized lithium disilicate (IN), advanced lithium disilicate (TS), and lithium disilicate (EX)) (n = 10). Crowns, the abutment, and the crowns when seated on the abutment were digitized by using an intraoral scanner. Fabrication trueness was assessed by using the root mean square method, while the internal fit was evaluated according to the triple scan method. These processes were repeated after the post-milling firing of AM, TS, and EX. Paired samples t-tests were used to analyze the effect of post-milling firing within AM, TS, and EX, while all materials were compared with 1-way analysis of variance and Tukey HSD tests (α = 0.05). RESULTS: Post-milling firing reduced the surface deviations and internal gap of AM and EX (P ≤ 0.014). AM mostly had higher deviations and internal gaps than other materials (P ≤ 0.030). CONCLUSIONS: Post-milling firing increased the trueness and internal fit of tested nano-lithium disilicate and lithium disilicate ceramics. Nano-lithium disilicate mostly had lower trueness and higher internal gap; however, the maximum meaningful differences among tested materials were small. Therefore, the adjustment duration and clinical fit of tested crowns may be similar. CLINICAL SIGNIFICANCE: Tested lithium disilicate ceramics may be suitable alternatives to one another in terms of fabrication trueness and internal fit, considering the small differences in measured deviations and internal gaps.
Asunto(s)
Diseño Asistido por Computadora , Coronas , Porcelana Dental , Diseño de Prótesis Dental , Ensayo de Materiales , Porcelana Dental/química , Humanos , Pilares Dentales , Cerámica/química , Propiedades de Superficie , Materiales Dentales/química , Adaptación Marginal Dental , Aleaciones de Cromo/químicaRESUMEN
OBJECTIVES: To evaluate how restoration thickness (0.5 mm and 0.7 mm) affects the fabrication trueness of additively manufactured definitive resin-based laminate veneers, and to analyze the effect of restoration thickness and margin location on margin quality. METHODS: Two maxillary central incisors were prepared either for a 0.5 mm- or 0.7 mm-thick laminate veneer. After acquiring the partial-arch scans of each preparation, laminate veneers were designed and stored as reference data. By using these reference data, a total of 30 resin-based laminate veneers were additively manufactured (n = 15 per thickness). All veneers were digitized and stored as test data. The reference and test data were superimposed to calculate the root mean square values at overall, external, intaglio, and marginal surfaces. The margin quality at labial, incisal, mesial, and distal surfaces was evaluated. Fabrication trueness at each surface was analyzed with independent t-tests, while 2-way analysis of variance was used to analyze the effect of thickness and margin location on margin quality (α = 0.05). RESULTS: Regardless of the evaluated surface, 0.7 mm-thick veneers had lower deviations (P < 0.001). Only the margin location (P < 0.001) affected the margin quality as labial margins had the lowest quality (P < 0.001). CONCLUSION: Restoration thickness affected the fabrication trueness of resin-based laminate veneers as 0.7 mm-thick veneers had significantly higher trueness. However, restoration thickness did not affect the margin quality and labial margins had the lowest quality. CLINICAL SIGNIFICANCE: Laminate veneers fabricated by using tested urethane-based acrylic resin may require less adjustment when fabricated in 0.7 mm thickness. However, marginal integrity issues may be encountered at the labial surface.
Asunto(s)
Resinas Compuestas , Adaptación Marginal Dental , Materiales Dentales , Coronas con Frente Estético , Incisivo , Propiedades de Superficie , Humanos , Materiales Dentales/química , Resinas Compuestas/química , Ensayo de Materiales , Diseño de Prótesis Dental , Porcelana Dental/química , Diseño Asistido por Computadora , Cerámica/química , Poliuretanos/química , Metacrilatos/químicaRESUMEN
PURPOSE: To evaluate the effect of model resin type and time interval on the dimensional stability of additively manufactured diagnostic casts. MATERIALS AND METHODS: Ten irreversible hydrocolloid impressions and 10 impressions from an intraoral scanner were made from a reference maxillary stone cast, which was also digitized with a laboratory scanner. Conventional impressions were poured in type III stone (SC), while digital impressions were used to additively manufacture casts with a nanographene-reinforced model resin (GP) or a model resin (DM). All casts were digitized with the same laboratory scanner 1 day (T0), 1 week (T1), 2 weeks (T2), 3 weeks (T3), and 4 weeks (T4) after fabrication. Cast scans were superimposed over the reference cast scan to evaluate dimensional stability. Data were analyzed with Bonferroni-corrected repeated measures ANOVA (α = .05). RESULTS: The interaction between the main factors (material type and time interval) affected anterior teeth deviations, while the individual main factors affected anterior teeth and entire-cast deviations (P ≤ .008). Within anterior teeth, DM had the lowest deviations at T3, and GP mostly had lower values at T2 and lower deviations at T3 than at T0 (P ≤ .041). SC had the highest pooled anterior teeth deviations, and GP had the highest pooled entire cast deviations (P < .001). T3 had lower pooled anterior teeth deviations than at T0, T1, and T4, and higher pooled entire cast deviations than T1 were demonstrated (P ≤ .027). CONCLUSIONS: The trueness of nanographene-reinforced casts was either similar to or higher than that of other casts. Dimensional changes were acceptable during the course of 1 month.
Asunto(s)
Diseño Asistido por Computadora , Técnica de Impresión Dental , Maxilar , Imagenología TridimensionalRESUMEN
Computer-aided design and computer-aided manufacturing systems enable digital designing and 3-dimensional (3D) printing of definitive casts with removable dies. However, the fit of the removable dies should be without interferences for their accurate positioning in the cast. Given that the accuracy of additive manufacturing depends on design- and manufacturing-related factors, verifying the accuracy of the position of 3D-printed removable dies in their cast is essential to fabricate positionally accurate definitive prostheses, which would enable minimal or no laboratory and clinical adjustments. This dental technique article presents a straightforward approach to verify the seating of a 3D-printed removable die by using verification matrices made of a polyvinylsiloxane interocclusal registration material.
RESUMEN
PURPOSE: To evaluate the effect of polymerization unit, polishing, and coffee thermocycling on the color and translucency of additively manufactured polyurethane-based resins with different viscosities. In addition, their color behavior was compared with the color of the shade tab throughout the fabrication steps and aging. MATERIALS AND METHODS: Disk-shaped specimens (Ø10 × 2 mm) were fabricated from polyurethane-based resins with different viscosities (Tera Harz TC-80DP and C&B permanent; n = 30 per material). Baseline color coordinates were measured after cleaning. The specimens in each resin group were divided into three subgroups (n = 10 per subgroup) to be polymerized with different polymerization units (Otoflash G171 [FLN], Wash and Cure 2.0 [CLED1], and P Cure [CLED2]), polished, and subjected to coffee thermocycling. Color coordinates were remeasured after each process. Color differences (ΔE00) and relative translucency parameter (RTP) values were calculated. Data were statistically analyzed (α = .05). RESULTS: Time points and polymerization units affected the ΔE00 for each material (P ≤ .049). ΔE00 of each polymerization unit pair had significant differences within and among different time points within each material (P ≤ .024). ΔE00 (when compared with the shade tab) and RTP were mostly affected by polymerization units and time points within both materials (P ≤ .042). CONCLUSIONS: Tested polymerization units, polishing, and coffee thermocycling affected the color difference and translucency of tested resins. Color differences ranged from moderately unacceptable to extremely unacceptable, and the differences in translucency values mostly ranged from perceptible to unacceptable, according to previous thresholds. In addition, tested resin-polymerization unit pairs had unacceptable color differences when compared to the shade tab. CLED1 may enable higher color stability for tested resins.
Asunto(s)
Café , Implantes Dentales , Polimerizacion , Poliuretanos , Color , Ensayo de Materiales , Propiedades de Superficie , Resinas CompuestasRESUMEN
Passive fit is essential for multiple-unit implant-supported prostheses. Conventional methods to assess the passivity of complete-arch implant-supported prostheses do not allow 3-dimensional (3D) visualization and quantification of misfit. This report describes the marginal and internal fit evaluation of a complete-arch implant-supported prosthesis by using the triple-scan protocol involving a scanner and a 3D analysis freeware. This technique allows researchers, clinicians, or dental technicians to detect and quantify 3D prosthetic misfit, which may facilitate the preparation for dental appointments and objective measurement of misfit for research studies.