Inflammatory and degenerative effects of induced osteoarthritis/rheumatoid arthritis models on temporomandibular joint of rats.

OBJECTIVE: The present study compared three models of induction of osteoarthritis (OA) and rheumatoid arthritis (RA) in the temporomandibular joint (TMJ) of rats. DESIGN: The induction method was by injection of complete Freund's adjuvant (CFA) + type II bovine collagen (CII). Twenty-four adult male rats were divided into four groups (n = 6): G1: Sham, 50 µL of 0.9% sodium chloride at the base of the tail and in each TMJ; G2: OA, 50 µL CFA+CII in each TMJ; G3: RA+OA, 100 µL of CFA+CII at the base of the tail and 50 µL CFA+CII in each TMJ; G4: RA, 100 µL of CFA+CII at the base of the tail. All injections were repeated 5 days later. Twenty-three days after the first injection, the animals were sacrificed and the TMJs were submitted to histomorphometric analysis and measurement of cytokines. The Kruskal-Wallis and Dunn tests were used (alpha=0.05). RESULTS: The total thickness of the condylar cartilage increased in G2 in relation to the other groups, G3 and G4 reduced in relation to G1; and G2 and G4 reduced in relation to G2 and G3. The levels of IL-1ß, IL-6 and TNF-α increased in the three induction models compared to G1. The level of IL-10 increased in G2 compared to the other groups and reduced in G3 and G4 compared to G1. CONCLUSION: CFA+CII induced inflammation and degeneration compatible with RA (advanced chronic stage) when injected in the tail, and compatible with OA (acute stage or early disease) when injected only in the TMJ.

Biocompatibility analysis in subcutaneous tissue and physico-chemical analysis of pre-mixed calcium silicate-based sealers.

OBJECTIVES: To evaluate the biocompatibility, physical and chemical properties of three pre-mixed calcium silicate-based sealers and an epoxy resin-based material were assessed. Pre-mixed sealers supposedly obtain water from the root canal moist to hydrate and set. MATERIALS AND METHODS: Polyethylene tubes were filled with the materials Bio-C Sealer Ion+, Bio-C Sealer, EndoSequence BC Sealer and AH Plus Jet, or left empty and surgically implanted in the subcutaneous tissue of Wistar rats. The animals were euthanised and the tubes and tissue were removed for histological analysis and scanning electron microscopy (SEM) coupled with energy-dispersive spectrometry (EDS). Materials' surface chemical characterisation was assessed using Raman spectroscopy and SEM/EDS. Flow, setting time (in two conditions), solubility, radiopacity and pH were also analysed. ANOVA and Bonferroni correction were performed for comparisons (P < 0.05). RESULTS: Inflammatory response observed in the tissues subsided from 7 to 30 days. Tungsten migration could be detected in the surrounding tissue following AH Plus Jet implantation. All calcium silicate-based sealers exhibited zirconium oxide (radiopacifier) and tricalcium silicate peaks before and after implantation. All materials exhibited flow values above 17 mm. An approximately tenfold difference was observed between the plaster- and metal-mould setting times of the calcium silicate cements indicating its sensitivity to moist variations and solubility above 8% was also observed for these materials. CONCLUSIONS: Pre-mixed materials exhibited variable setting time and solubility with a decreasing inflammatory response. CLINICAL RELEVANCE: The variable moist-dependant setting time with high solubility poses a concern for the clinical use of these pre-mixed sealers.