RESUMEN
For the first time, activated carbon from a durian shell (ACDS) activated by H2SO4 was successfully synthesized in the present study. The fabricated ACDS has a porous surface with a specific surface area of 348.0017 m2·g-1, average capillary volume of 0.153518 cm3·g-1, the average pore diameter of 4.3800 nm; ash level of 55.63%; humidity of 4.74%; density of 0.83 g·cm-3; an iodine index of 634 mg·g-1; and an isoelectric point of 6.03. Several factors affecting Methylene Blue (MB) adsorption capacity of ACDS activated carbon was investigated by the static adsorption method, revealing that the adsorption equilibrium was achieved after 90 min. The best adsorbent pH for MB is 7 and the mass/volume ratio is equal to 2.5 g·L-1. The MB adsorption process of ACDS activated carbon follows the Langmuir, Freundlich, Tempkin, and Elovich isotherm adsorption model, which has determined the maximum adsorption capacity for MB of ACDS as qmax = 57.47 mg·g-1. The MB adsorption process of ACDS follows the of pseudo-second-order adsorption kinetic equation. The Weber and Morris Internal Diffusion Model, the Hameed and Daud External Diffusion Model of liquids have been studied to see if the surface phase plays any role in the adsorption process. The results of thermodynamic calculation of the adsorption process show that the adsorption process is dominated by chemical adsorption and endothermic. The obtained results provide an insight for potential applications of ACDS in the treatment of water contaminated by dyes.
RESUMEN
In recent years, photocatalysis has been used as an environmentally friendly method for the degradation of organic pigments in water. In this study, Ce3+/Ce4+-doped ZrO2/CuO as a mixed semiconductor oxide was successfully prepared by a one-step hydrothermal method. The Ce3+/Ce4+-doped ZrO2/CuO has shown high degradation efficiency of methylene blue (MB), and the maximum degradation percentage was observed to be 94.5% at 180 min under irradiation visible light. The photocatalytic activity increases significantly by doping Ce3+/Ce4+ in ZrO2/CuO for MB degradation. Ce3+/Ce4+ doping is shown to reduce the (e-/h+) recombination rate and improve the charge transfer, leading to enhanced photocatalytic activity of materials. The materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), FTIR, EDS, BET and diffuse reflectance spectroscopy (DRS).
RESUMEN
This work investigated the removal of antibiotic tetracycline (TC) from wastewater using nanocomposite material based on laterite modified with polyanion, polystyrene sulfonate (PSS). The effective factors influenced on the TC removal using nanocomposite PSS-modified laterite (NCPML) were optimized and found to be pH 4, solid-liquid ratio 5 mg/mL, and contact time 180 min. The highest removal of TC reached about 88% under the optimum adsorption conditions. The adsorption isotherm and kinetics of TC adsorption onto NCPML were in good agreement with the Langmuir and pseudo-second-order models, respectively. The characteristics of the NCPML material before and after TC adsorption were examined by zeta (ζ) potential measurements, Brunauer-Emmett-Teller (BET) method, and Fourier transform infrared spectroscopy (FT-IR). The TC adsorption onto NCPML was induced by electrostatic interaction, hydrogen bonding, and diffusion interaction. The TC removal from wastewater was approximately 94% while efficiency still reached 66% after five regenerations. Our research reveals that NCPML is a high-performance adsorbent for TC removal from wastewater.