RESUMEN
PURPOSE: To evaluate the effect of different printing orientations and post-polymerization time with thermal cycling on the translucency of 3D-printed denture base resins. METHODS: Heat-polymerized (HP) acrylic resin specimens were fabricated and 3D-printed denture base materials (NextDent, ASIGA, FormLabs) were printed with different printing orientations (0, 45, 90 degrees) and subjected to different post-polymerization times (15-, 30-, 60-, and 90-min). All specimens were polished and immersed in distilled water for 1 day at 37°C. CIEDE2000 was used to measure the translucency parameters (TP00) before and after thermal cycling (5000 cycles) recording the color parameters (L*, a*, b*) against a black and white background using a spectrophotometer. k-factors ANOVA followed by post hoc Tukey's test (α = .05) was performed for statistical analysis. RESULTS: The k-factors ANOVA test showed a significant effect of resin material, post-polymerization time, and printing orientation on translucency (p < 0.001). In comparison to HP, all 3D-printed resins showed lower translucency with all post-polymerization times and printing orientation (p < 0.001) except FormLabs resin (p > 0.05). For all 3D-printed resins, the translucency increased, with increasing the post-polymerization time (p < 0.001) and 60- and 90-min showed the highest translucency. For printing orientation, 90 and 45 degrees significantly showed high translucency in comparison to 0 degrees (p < 0.001). FormLabs showed significantly higher translucency when compared with NextDent and ASIGA per respective printing orientation and post-polymerization time. The translucency significantly decreased after thermal cycling for all tested resins (p < 0.001). CONCLUSION: The findings of this study demonstrated that the translucency of 3D-printed resins is influenced by the printing orientation, post-polymerization time, and resin type. As a result, choosing a resin type, and printing orientation, with a longer post-polymerization time should be considered since it may improve the esthetic appearance of the 3D-printed resins.