Abiotic, Hybrid, and Biological Electrocatalytic Materials Applied in Microfluidic Fuel Cells: A Comprehensive Review.

This article provides an overview of the work reported in the past decade in the field of microfluidic fuel cells. To develop appropriate research, the most commonly used electrocatalytic materials were considered and a new classification was proposed based on their nature: abiotic, hybrid, or biological. This classification allowed the authors to discern the information collected. In this sense, the types of electrocatalysts used for the oxidation of the most common fuels in different environments, such as glucose, ethanol, methanol, glycerol, and lactate, were presented. There are several phenomena presented in this article. This information gives an overview of where research is heading in the field of materials for electrocatalysis, regardless of the fuel used in the microfluidic fuel cell: the synthesis of abiotic and biological materials to obtain hybrid materials that allow the use of the best properties of each material.

Comparative Colorimetric Sensor Based on Bi-Phase γ-/α-Fe2O3 and γ-/α-Fe2O3/ZnO Nanoparticles for Lactate Detection.

This work reports on Fe2O3 and ZnO materials for lactate quantification. In the synthesis, the bi-phase γ-/α-Fe2O3 and γ-/α-Fe2O3/ZnO nanoparticles (NPs) were obtained for their application in a lactate colorimetric sensor. The crystalline phases of the NPs were analyzed by XRD and XPS techniques. S/TEM images showed spheres with an 18 nm average and a needle length from 125 to 330 nm and 18 nm in diameter. The γ-/α-Fe2O3 and γ-/α-Fe2O3/ZnO were used to evaluate the catalytic activity of peroxidase with the substrate 3,3,5,5-tetramethylbenzidine (TMB), obtaining a linear range of 50 to 1000 µM for both NPs, and a 4.3 µM and 9.4 µM limit of detection (LOD), respectively. Moreover, γ-/α-Fe2O3 and γ-/α-Fe2O3/ZnO/lactate oxidase with TMB assays in the presence of lactate showed a linear range of 50 to 1000 µM, and both NPs proved to be highly selective in the presence of interferents. Finally, a sample of human serum was also tested, and the results were compared with a commercial lactometer. The use of ZnO with Fe2O3 achieved a greater response toward lactate oxidation reaction, and has implementation in a lactate colorimetric sensor using materials that are economically accessible and easy to synthesize.

Poly-L-lysine-modified with ferrocene to obtain a redox polymer for mediated glucose biosensor application.

Ferrocene-based polymers as redox mediators are considered versatile and important in the study of glucose biosensors. Poly-L-lysine (PLL), as a cationic polymer, possesses good properties including biocompatibility, biodegradation and water solubility. In this work, PLL was modified with ferrocene carboxylate in a very simple way by activating the carboxyl group of Fc, which reacted with the amino groups of the polymer. The resulting product was analysed by FTIR. Performance as a redox mediator (Fc-PLL) with the enzyme glucose oxidase was tested by cyclic voltammetry and showed an increase in the oxidation current in the presence of glucose in PBS pH 7.4. Additionally, performance as a biosensor was evaluated by amperometry and gave a linear range of 0-10 mM, a limit of detection of 23 µM, a sensitivity of 6.55 µA/cm2 mM and high selectivity. To evaluate the charged regions of Fc-PLL/GOx on the electrode surface, analysis by scanning electrochemical microscopy showed remarkable activity. The Fc-PLL redox polymer as a glucose biosensor has been well accepted as this kind of material, and the results showed remarkable activity as an electron transfer mediator between the redox polymer and the GOx enzyme.