Influence of the type of reciprocating motion on the cyclic fatigue resistance of reciprocating files in a dynamic model.

BACKGROUND: The aim of this study was to compare the influence of two novel reciprocating movements on the cyclic fatigue resistance of endodontic reciprocating files. METHODS: 30 Procodile® (Komet Medical, Lemgo, Germany) files were selected in this study and distributed according to the following study groups depending on the movements to be performed: ReFlex Dynamic (n = 10), ReFlex Smart (n = 10) and Reciproc (n = 10) reciprocating movement. These files were fixed to a specific dynamic cyclic fatigue device designed and manufactured by 3D impression to simulate the pecking motion performed by the operator. The time to failure and the number of cycles of in-and-out of the endodontic files was registered. The results were analyzed by ANOVA and Weibull statistics. RESULTS: Statistically significant differences were found when the number of cycles of in-and-out movement and the time to failure of ReFlex Dynamic and Reciproc reciprocating movement (p < 0.001) and between ReFlex Smart and Reciproc reciprocating movement (p < 0.001) were compared in pairs. However, no statistically significant differences were observed between time to failure and number of cycles of in-and-out movement of ReFlex Dynamic and ReFlex Smart reciprocating movement (p = 0.253). CONCLUSIONS: The ReFlex Smart reciprocating movement increased the cyclic fatigue resistance of endodontic reciprocating files compared with traditional reciprocating movement.

Influence of the CAD-CAM Systems on the Marginal Accuracy and Mechanical Properties of Dental Restorations.

The aim of this study was to compare the quality of different computer-assisted-design and computer assisted manufacturing systems (CAD-CAM) generated by only one scanner, focusing on vertical fit discrepancies and the mechanical properties. A master model was obtained from a real clinical situation: the replacement of an absent (pontic) tooth, with the construction of a fixed partial denture on natural abutments with three elements. Nine scans were performed by each tested and 36 copies were designed using a dental CAD-CAM software (Exocad). The frameworks were manufactured using three-axis and five-axis, with the same batch of the chrome-cobalt (CrCo) alloy. The frameworks were not cemented. A focus ion beam-high resolution scanning electron microscope (FIB-HRSEM) allowed us to obtain the vertical gap measurements in five points for each specimen. Roughness parameters were measured using white light interferometry (WLI). The samples were mechanically characterized by means of flexural tests. A servo-hydraulic testing machine was used with a cross-head rate of 1 mm/min. One-way ANOVA statistical analysis was performed to determine whether the vertical discrepancies and mechanical properties were significantly different between each group (significance level p < 0.05). The overall mean marginal gap values ranged: from 92.38 ± 19.24 µm to 19.46 ± 10.20 µm, for the samples produced by three-axis and five-axis machines, respectively. Roughness was lower in the five-axis machine than the three-axis one, and as a consequence, the surface quality was better when the five-axis machine was used. These results revealed a statistically significant difference (p < 0.005) in the mean marginal gap between the CAD-CAM systems studied. The flexural strength for these restorations range from 6500 to 7000 N, and does not present any statistical differences' significance between two CAD-CAM systems studied. This contribution suggests that the number of axes improves vertical fit and surface quality due to the lower roughness. These claims show some discrepancies with other studies.