RESUMEN
Elementary tellurium is currently of great interest as an element with potential promise in nano-technology applications because of the recent discovery regarding its three two-dimensional phases and the existence of Weyl nodes around its Femi level. Here, we report on the unique nano-photonic properties of elemental tellurium particles [Te(0)], as harvest from a culture of a tellurium-oxyanion respiring bacteria. The bacterially-formed nano-crystals prove effective in the photonic applications tested compared to the chemically-formed nano-materials, suggesting a unique and environmentally friendly route of synthesis. Nonlinear optical measurements of this material reveal the strong saturable absorption and nonlinear optical extinctions induced by Mie scattering over broad temporal and wavelength ranges. In both cases, Te-nanoparticles exhibit superior optical nonlinearity compared to graphene. We demonstrate that biological tellurium can be used for a variety of photonic applications which include their proof-of-concept for employment as ultrafast mode-lockers and all-optical switches.
RESUMEN
In the present study, a tough tetragonal zirconia polycrystalline (Y-TZP) material was developed for use in high-speed infrared windows and domes. The influence of the preparation procedure and the microstructure on the material's optical properties was evaluated by SEM and FT-IR spectroscopy. It was revealed that a high transmittance up to 77% in the three- to five-micrometer IR region could be obtained when the sample was pre-sintered at 1225 °C and subjected to hot isostatic pressing (HIP) at 1275 °C for two hours. The infrared transmittance and emittance at elevated temperature were also examined. The in-line transmittance remained stable as the temperature increased to 427 °C, with degradation being observed only near the infrared cutoff edge. Additionally, the emittance property of 3Y-TZP ceramic at high temperature was found to be superior to those of sapphire and spinel. Overall, the results indicate that Y-TZP ceramic is a potential candidate for high-speed infrared windows and domes.
RESUMEN
Er(3+)-doped transparent glass ceramics containing micron-sized SrF2 crystals were obtained by direct liquid-phase sintering of a mixture of SrF2 powders and precursor glass powders at 820 °C for 15 min. The appearance and microstructural evolution of the SrF2 crystals in the resulting glass ceramics were investigated using X-ray diffraction, field-emission scanning electron microscopy and transmission microscopy. The SrF2 crystals are ~15 µm in size and are uniformly distributed throughout the fluorophosphate glass matrix. The glass ceramics achieve an average transmittance of 75% in the visible region and more than 85% in the near-IR region. The high transmittance of the glass ceramics results from matching the refractive index of the SrF2 with that of the precursor glass. Energy dispersive spectroscopy, photoluminescence spectra, and photoluminescence lifetimes verified the incorporation of Er(3+) into the micron-sized SrF2 crystals. Intense 2.7 µm emissions due to the (4)I11/2 â (4)I13/2 transition were observed upon excitation at 980 nm using a laser diode. The maximum value of the emission cross section of Er(3+) around 2.7 µm is more than 1.2 × 10(-20) cm(2), which indicates the potential of using transparent glass ceramics containing micron-sized SrF2 crystals for efficient 2.7 µm lasers and amplifiers.
RESUMEN
Hierarchical MoS2 thin films nanostructured with orthogonally oriented vertically and horizontally aligned layers were designed and excellent passive Q-switching behavior in a fiber laser was demonstrated. A special solvothermal system containing a small amount of water was applied to synthesize such hierarchical MoS2 nanofilms, in which the reaction rate is carefully controlled by the diffusion rate of the sulfur precursor. Wafer-scale MoS2 thin films with hierarchical structures are formed on various substrates. Moreover, the hierarchical MoS2 thin films consisting of both vertical and horizontal layers can be tuned to possess only horizontally aligned layers by controlling the solvothermal time. To show the potential application proof-of-concept, the nonlinear optical performance of the hierarchical MoS2 was investigated. Superior passive Q-switching behavior in a fiber laser with a minimum pulse width of 2.2 µs was observed.
RESUMEN
Correction for 'Direct synthesis of large-scale hierarchical MoS2 films nanostructured with orthogonally oriented vertically and horizontally aligned layers' by Xiaoyan Zhang et al., Nanoscale, 2016, DOI: 10.1039/c5nr05938k.
RESUMEN
Nonlinear optical property of transition metal dichalcogenide (TMDC) nanosheet dispersions, including MoS2, MoSe2, WS2, and WSe2, was performed by using Z-scan technique with ns pulsed laser at 1064 nm and 532 nm. The results demonstrate that the TMDC dispersions exhibit significant optical limiting response at 1064 nm due to nonlinear scattering, in contrast to the combined effect of both saturable absorption and nonlinear scattering at 532 nm. Selenium compounds show better optical limiting performance than that of the sulfides in the near infrared. A liquid dispersion system based theoretical modelling is proposed to estimate the number density of the nanosheet dispersions, the relationship between incident laser fluence and the size of the laser generated micro-bubbles, and hence the Mie scattering-induced broadband optical limiting behavior in the TMDC dispersions.
RESUMEN
The synthesis of pure and well dispersed lutetium aluminum garnet (LuAG) powder is crucial and important for the preparation of LuAG transparent ceramics. In this paper, high purity and well dispersed LuAG powders have been synthesized via co-precipitation method with lutetium nitrate and aluminum nitrate as raw materials. Ammonium hydrogen carbonate (AHC) was used as the precipitant. The influence of aging time, pH value, and dripping speed on the prepared LuAG powders were investigated. It showed that long aging duration (>15 h) with high terminal pH value (>7.80) resulted in segregation of rhombus Lu precipitate and Al precipitate. By decreasing the initial pH value or accelerating the dripping speed, rhombus Lu precipitate was eliminated and pure LuAG nano powders were synthesized. High quality LuAG transparent ceramics with transmission >75% at 1064 nm were fabricated using these well dispersed nano LuAG powders.
RESUMEN
Employing high-yield production of layered materials by liquid-phase exfoliation, molybdenum disulfide (MoS2) dispersions with large populations of single and few layers were prepared. Electron microscopy verified the high quality of the two-dimensional MoS2 nanostructures. Atomic force microscopy analysis revealed that ~39% of the MoS2 flakes had thicknesses of less than 5 nm. Linewidth and frequency difference of the E(1)2g and A1g Raman modes confirmed the effective reduction of flake thicknesses from the bulk MoS2 to the dispersions. Ultrafast nonlinear optical (NLO) properties were investigated using an open-aperture Z-scan technique. All experiments were performed using 100 fs pulses at 800 nm from a mode-locked Ti:sapphire laser. The MoS2 nanosheets exhibited significant saturable absorption (SA) for the femtosecond pulses, resulting in the third-order NLO susceptibility Imχ((3)) ~ 10(-15) esu, figure of merit ~10(-15) esu cm, and free-carrier absorption cross section ~10(-17) cm(2). Induced free carrier density and the relaxation time were estimated to be ~10(16) cm(-3) and ~30 fs, respectively. At the same excitation condition, the MoS2 dispersions show better SA response than the graphene dispersions.
RESUMEN
Er3+ doped CaF2-fluorophosphate (FP) glass microcomposites were produced by heat-treating the mixture of Er3+:CaF2 precipitate and FP glass powder above the melting temperature of the FP glass. The appearance of CaF2 crystallites in the resulting composites was confirmed by x ray diffraction. Despite the fact that the average diameter of the crystallites was around 10 µm as revealed by the micromorphology study, a transparent composite was obtained by matching the refractive index of FP glass to that of CaF2. Intense IR fluorescence at around 2.7 µm was observed in the composite, implying the composite would be a promising candidate for IR lasers and amplifiers.
RESUMEN
Near-infrared distributed feedback (DFB) laser actions of Oxazine 725 dye in zirconia thin films and in silica bulks were investigated. Intensity modulation and polarization modulation were used to generate the DFB lasing. Wideband tuning of the output wavelength was achieved by varying the period of the modulation generated by a nanosecond Nd:YAG laser at 532 nm. Tuning ranges were 716-778 nm and 724-813 nm for the thin film lasers and the bulk lasers, respectively. The laser output showed different polarization characteristics and threshold energy variation when the feedback mechanism was changed from intensity modulation to polarization modulation.