RESUMEN
A broadband and narrowband switchable terahertz (THz) absorber based on a bulk Dirac semimetal (BDS) and strontium titanate (STO) is proposed. Narrowband and broadband absorption can be switched by adjusting the Fermi level of the BDS. When the Fermi level of the BDS is 100 meV, the device is an absorber with three narrowband absorption peaks. The frequencies are 0.44, 0.86, and 1.96 THz, respectively, when the temperature of STO is 250 K. By adjusting the temperature of STO from 250 to 500 K, the blue shifts of the frequencies are approximately 0.14, 0.32, and 0.60 THz, respectively. The sensitivities of the three absorption peaks are 0.56, 1.27, and 2.38 GHz/K, respectively. When the Fermi level of the BDS is adjusted from 100 to 30 meV, the device can be switched to a broadband absorber with a bandwidth of 0.70 THz. By adjusting the temperature of STO from 250 to 500 K, the central frequency shifts from 1.40 to 1.79 THz, and the bandwidth broadens from 0.70 to 0.96 THz. The sensitivity of the central frequency is 1.57 GHz/K. The absorber also has a wide range of potential applications in multifunctional tunable devices, such as temperature sensors, stealth equipment, and filters.
RESUMEN
In this study, a perfect metamaterial absorber based on strontium titanate and bulk Dirac semimetals is proposed. When the temperature of strontium titanate was 300K, the dual-band absorptions were 99.74% and 99.99% at 1.227 and 1.552 THz, respectively. The sensitivities based on a transverse magnetic (TM) wave were 0.95 and 1.22 GHz/K; the sensitivity based on a transverse electric (TE) wave was 0.76 GHz/K. The TE and TM waves were modulated by inserting a bulk Dirac semimetal between the concave and convex devices. The modulation depth of the TE wave was 97.9% at 1.1 THz; the extinction ratio was 16.9 dB. The modulation depth of the TE wave at 1.435 THz was 95.9%; the extinction ratio was 13.89 dB. The TM wave modulation depth at 1.552 THz was 95.9%; the extinction ratio was 13.98 dB. Irrespective of a TE or TM wave, the terahertz absorber has good switching and temperature-sensing performance based on strontium titanate and bulk Dirac semimetals as well as broad application prospects in temperature sensing and switching devices.