RESUMEN
The reaction of ß-diketophosphazene with the europium (III) salt synthesized the corresponding metal complex which was structured with (3-aminopropyl)triethoxysilane and treated with dibenzoylmethane for additional coordination of europium atoms. The polymer thus obtained exhibits luminescence with a maximum of 615 nm, which is characteristic of europium. The polymer is thermally stable up to 300 °C, the coating based on it has a contact angle of 101°, and the adhesive strength of the coating to non-finished glass (according to ISO 2409: 2013) is 1 point.
RESUMEN
A new method for purification of 2-methyl-2-oxazoline using citric acid was developed and living cationic ring-opening polymerization of 2-methyl-2-oxazoline was carried out. Polymerization was conducted in acetonitrile using benzyl chloride-boron trifluoride etherate initiating system. According to DSC data, the temperature range of melting of the crystalline phase of the resulting polymer was 95-180 °C. According to small-angle X-ray scattering and wide-angle X-ray diffraction data, the degree of crystallinity of the polymer was 12%. Upon cooling of the polymer melt, the polymer became amorphous. Using thermogravimetric analysis, it was found that the thermal destruction of poly(2-methyl-2-oxazoline) started above 209 °C.
RESUMEN
Phosphazene-containing epoxy oligomers (PEO) were synthesized by the interaction of hexachlorocyclotriphosphazene (HCP), phenol, and bisphenol A in a medium of excess of epichlorohydrin using potassium carbonate and hydroxide as HCl acceptors with the aim of obtaining a product with lower viscosity and higher phosphazene content. PEOs are mixtures of epoxycyclophosphazene (ECP) and a conventional organic epoxy resin based on bisphenol A in an amount controlled by the ratio of the initial mono- and diphenol. According to 31P NMR spectroscopy, pentasubstituted aryloxycyclotrophosphazene compounds predominate in the ECP composition. The relative content in the ECP radicals of mono- and diphenol was determined by the MALDI-TOF mass spectrometry method. The organic epoxy fraction, according to gas chromatograpy-mass spectrometry (GC-MS), contains 50-70 wt % diglycidyl ether of bisphenol A. PEO resins obtained in the present work have reduced viscosity when compared to other known phosphazene-containging epoxy resins while phosphazene content is still about 50 wt %. Resins with an epoxy number within 12-17 wt %, are cured by conventional curing agents to form compositions with flame-retardant properties, while other characteristics of these compositions are at the level of conventional epoxy materials.
RESUMEN
The method of optical wedge revealed that the optimum temperature for compatibility of hexakis(4-acetamidophenoxy)cyclotriphosphazene (ACP) and DER-331 epoxy resin is in the range of 220-260 °C. The interdiffusion time of components at these temperatures is about 30 min. The TGA and differential scanning calorimetry (DSC) methods revealed the curing temperature of 280 °Ð¡ for this composition. IR spectroscopy confirmed that the reaction between the resin and ACP is completed within 10 min. According to the DSC data, a glass transition temperature of 130 °Ð¡ was estimated for the cured resin. Combustion test UL-94 demonstrated that the obtained material can be assigned to the fireproof category of V-0. Burning droplets were not formed during the burning. The coke formed during the combustion of samples possessed a dense and porous structure. The shape of pores is closed, while their size is in the range of 0.2-200 µm.
RESUMEN
Phosphazene-containing epoxy-resorcinol oligomers (PERO) are synthesized in one stage with the direct interaction of hexachlorocyclotriphosphazene (HCP), resorcinol, and epichlorohydrin in the presence of solid NaOH. Depending on the initial ratio of HCP:resorcinol, PERO contains from 20 to 50 wt.% phosphazene component (2.0â»4.8% of phosphorus) and have an epoxy group content up to 30 %. Products are characterized using ¹H and 31P NMR spectroscopy, MALDI-TOF mass spectrometry, and elemental analysis. According to mass spectrometry, the phosphazene fractions of PERO include up to 30 individual compounds with a predominance of cyclotriphosphazenes with one unsubstituted chlorine atom and four or five glycidyl groups. PERO has a lower viscosity in comparison with similar resins based on bisphenol A, which can simplify their use as a binder for polymer composites, adhesives, and paints.