Tuning Chemical and Morphological Properties of Ceria Nanopowders by Mechanochemistry.

Cerium oxide powders are widely used and are of fundamental importance in catalytic pollution control and energy production due to the unique chemical properties of CeO2. Processing steps involved in catalyst preparation, such as high-temperature calcination or mechanical milling processes, can alter the morphological and chemical properties of ceria, heavily affecting its final properties. Here, we focus on the tuning of CeO2 nanopowder properties by mild- and high-energy milling processes, as the mechanochemical synthesis is gaining increasing attention as a green synthesis method for catalyst production. The textural and redox properties were analyzed by an array of techniques to follow the aggregation and comminution mechanisms induced by mechanical stresses, which are more prominent under high-energy conditions but strongly depend on the starting properties of the ceria powders. Simultaneously, the evolution of surface defects and chemical properties was followed by Raman spectroscopy and H2 reduction tests, ultimately revealing a trade-off effect between structural and redox properties induced by the mechanochemical action. The mild-energy process appears to induce the largest enhancement in surface properties while maintaining bulk properties of the starting materials, hence confirming its effectiveness for its exploitation in catalysis.

Sintering Behaviour of Waste Olivine and Olivine/Alumina Blends.

The sintering behaviour of several green compacts made with olivine or olivine/alumina powder blends has been examined. To this goal, powders were attrition milled, uniaxially pressed into specimens and air sintered at temperatures ranging from 1100 to 1300 °C. The resulting samples were characterized by water absorption, shrinkage, phase composition and density. Compositions containing 5%, 10% and 20% Al2O3 have a sintering behaviour similar to that of olivine alone, reaching low residual porosity when fired at 1300 °C. Conversely, the composition containing 40% Al2O3 displays an almost flat shrinkage profile and maintains high residual porosity in the examined temperature range.

Fly and bottom ashes from biomass combustion as cement replacing components in mortars production: rheological behaviour of the pastes and materials compression strength.

In the present research mortar pastes obtained by replacing a commercial cement with the equivalent mass of 5, 10, 20 and 30 wt.% of fly ash or bottom ash from fir chips combustion, were prepared and rheologically characterized. It was observed that the presence of ash modifies their rheological behaviour with respect to the reference blend due to the presence, in the ashes, of KCl and K2SO4 which cause precipitation of gypsum and portlandite during the first hydration stages of the pastes. Hydrated materials containing 5 wt.% of ash display compression strength and absorption at 28 d of same magnitude as the reference composition; conversely, progressive increase of ash cause a continuous decline of materials performances. Conversely, samples tested after 180 d display a marked decline of compression strength, as a consequence of potassium elution and consequent alkali-silica reaction against materials under curing.

Steelmaking slag as aggregate for mortars: effects of particle dimension on compression strength.

The present paper reports on the results of some experiments obtained from the production, hydration and subsequent measurement of the mechanical properties of several mortars prepared using a commercial CII/B-LL Portland cement, steelmaking slag, superplasticizer and water. Relevant parameters for the mortar preparation are the weight ratios of cement/water, the weight ratio superplasticizer/cement and between fine and granulated coarse particles. It has been demonstrated that optimisation of such parameters leads to the production of materials with mechanical properties suitable for civil engineering applications. Moreover, materials with improved compressive strength can be prepared by the use of slag containing extensive amounts of large particles.