Roughness and wettability of titanium implant surfaces modify the salivary pellicle composition.

This study reports the differences in the protein composition of salivary pellicles formed under in situ conditions on two Titanium (Ti) surfaces, with different roughness and wettability. Smooth pretreatment Ti surfaces (Ti-PT) with an average roughness (Ra) of 0.45 µm and a water contact angle (WCA) of 92.4°, as well as a more rough sandblasted, large grit, acid-etched treatment Ti surfaces (Ti-SLA) with a Ra of 3.3 µm and WCA of 131.8°, were tested. The salivary pellicles were quantitatively analyzed by bicinchoninic acid assays, and the protein identification was performed by Nano-LC-MS/MS (nano mass spectrometry). Protein levels of 2.5, and 9.1 µg/ml were quantified from the detached salivary pellicle formed on the Ti-PT and Ti-SLA surfaces, respectively. Using Nano-LC-MS/MS, a total of 597 proteins were identified on all the substrates tested; 43 proteins were identified only on the Ti-PT, and 226 proteins were adsorbed solely on the Ti-SLA substrates. The physicochemical characteristics of the Ti implant surfaces modified the amount and the identity of the salivary proteome of the pellicles formed, confirming the high selectivity of the protein pellicle formed on a surface once is exposed in the oral cavity.

Antibacterial composite membranes of polycaprolactone/gelatin loaded with zinc oxide nanoparticles for guided tissue regeneration.

The bacterial colonization of absorbable membranes used for guided tissue regeneration (GTR), as well as their rapid degradation that can cause their rupture, are considered the major reasons for clinical failure. To address this, composite membranes of polycaprolactone (PCL) and gelatin (Gel) loaded with zinc oxide nanoparticles (ZnO-NPs; 1, 3 and 6 wt% relative to PCL content) were fabricated by electrospinning. To fabricate homogeneous fibrillar membranes, acetic acid was used as a sole common solvent to enhance the miscibility of PCL and Gel in the electrospinning solutions. The effects of ZnO-NPs in the physico-chemical, mechanical and in vitro biological properties of composite membranes were studied. The composite membranes showed adequate mechanical properties to offer a satisfactory clinical manipulation and an excellent conformability to the defect site while their degradation rate seemed to be appropriate to allow successful regeneration of periodontal defects. The presence of ZnO-NPs in the composite membranes significantly decreased the planktonic and the biofilm growth of the Staphylococcus aureus over time. Finally, the viability of human osteoblasts and human gingival fibroblasts exposed to the composite membranes with 1 and 3 wt% of ZnO-NPs indicated that those membranes are not expected to negatively influence the ability of periodontal cells to repopulate the defect site during GTR treatments. The results here obtained suggest that composite membranes of PCL and Gel loaded with ZnO-NPs have the potential to be used as structurally stable GTR membranes with local antibacterial properties intended for enhancing clinical treatments.

Adhesion of Streptococcus mutans and Streptococcus sanguinis on Er:YAG Laser-Irradiated Dental Enamel: Effect of Surface Roughness.

Objective: To determine surface roughness caused by Er:YAG laser irradiation and its effect on the increase in bacterial adhesion. Background: Er:YAG laser was proposed as a strategic device to reduce caries by its ability to generate chemical and structural changes in tooth enamel; in turn, it produces undesirable effects on the tooth surface that could increase its roughness and allow a greater accumulation of microorganisms. Methods: Eighty-four samples of human enamel were divided into seven groups (n = 12): G1_control (no laser irradiation); G2_100/H2O, G3_200/H2O, and G4_300/H2O were irradiated with Er:YAG laser (12.7, 25.5, and 38.2 J/cm2, respectively) under water irrigation. In addition, G5_100, G6_200, and G7_300 were irradiated with the energy densities described above and no water irrigation. Surface roughness measurements were recorded before and after treatment using a profilometer. Afterward, three samples per group were incubated in a microorganism suspension for the tetrazolium salt (XTT) assay. Biofilm morphology was observed using scanning electron microscopy and confocal laser scanning microscope. One-way analysis of variance and t-tests were performed for statistical analysis (p < 0.05). Results: There were no statistically significant differences in roughness values in the G5_100 group before and after treatment, but there were statistically significant differences observed in the other groups evaluated (p < 0.05). No significant differences in adhesion of both strains were detected in irradiated groups compared with G1_control. Conclusions: The increase in roughness on dental enamel surfaces was proportional to the irradiation conditions. However, the increase in surface roughness caused by Er:YAG laser irradiation did not affect Streptococcus mutans and S. sanguinis adhesion.