Efficacy of removing Candida albicans from orthodontic acrylic bases: an in vitro study.

BACKGROUND: This study evaluated the efficacy of four methods in removing Candida albicans from the acrylic base material used to fabricate removable orthodontic appliances. METHODS: Heat-processed bars of orthodontic acrylic were incubated in a suspension of C. albicans for 2 h at 37 °C. Samples were allocated into five groups (five bars per group) according to the cleaning method: (1) manual brushing using a toothbrush; (2) soaking in a commercial denture cleaning solution; (3) soaking in a commercial mouthwash solution; (4) using an ultrasonic cleaner; and (5) soaking in distilled water as a negative control. Yeast remaining attached to the bars after cleaning were removed by vortexing in growth medium and plated on Sabouraud dextrose agar. The reduction in yeast colony count after cleaning was calculated and expressed as the number of colony forming units per acrylic bar (CFU/bar). The experiment was carried out three times. RESULTS: All four cleaning methods resulted in a significant decrease in viable yeast cells associated with the acrylic bars compared to the control group. The mean percentage reduction in viable yeast cells affected by the cleaning methods was: brushing 89.9%; chlorhexidine 95.8%; ultrasonic cleaning 99.9%; and denture tablet 100%. CONCLUSIONS: All four methods evaluated in this study were effective, to some extent, in removing C. albicans from orthodontic acrylic samples. The most effective, and readily available, cleaning method was the use of commercial denture sterilizing tablets.

An evaluation of two types of nickel-titanium wires in terms of micromorphology and nickel ions' release following oral environment exposure.

BACKGROUND: This study aimed to compare superelastic and heat-activated nickel-titanium orthodontic wires' surface morphology and potential release of nickel ions following exposure to oral environment conditions. METHODS: Twenty-four 20-mm-length distal cuts of superelastic (NiTi Force I®) and 24 20-mm-length distal cuts of heat-activated (Therma-Ti Lite®) nickel-titanium wires (American Orthodontics, Sheboygan, WI, USA) were divided into two equal groups: 12 wire segments left unused and 12 segments passively exposed to oral environment for 1 month. Scanning electron microscopy and atomic force microscopy were used to analyze surface morphology of the wires which were then immersed in artificial saliva for 1 month to determine potential nickel ions' release by means of atomic absorption spectrophotometer. RESULTS: Heat-activated nickel-titanium (NiTi) wires were rougher than superelastic wires, and both types of wires released almost the same amount of Ni ions. After clinical exposure, more surface roughness was recorded for superelastic NiTi wires and heat-activated NiTi wires. However, retrieved superelastic NiTi wires released less Ni ions in artificial saliva after clinical exposure, and the same result was recorded regarding heat-activated wires. CONCLUSIONS: Both types of NiTi wires were obviously affected by oral environment conditions; their surface roughness significantly increased while the amount of the released Ni ions significantly declined.