Investigation of the structure and dielectric properties of doped barium titanates.

This work examined the influence of zirconium concentration on barium titanate (BZT) BaZrxTi1-xO3, with (x = 0, 0.15, 0.50, 0.75, and 1), produced by the tartrate precursor technique. The Fourier transform infrared (FTIR) spectra support the X-ray diffraction (XRD) results regarding formation of the perovskite structure. Grain size grows with Zr concentration, suggesting that the presence of Zr ions enlarges the grains. The transmission electron microscopy (TEM) images demonstrated that, due to their nano size, nanocrystallites are agglomerated in most images with irregular morphologies and average particle sizes from 20.75 nm to 63.75 nm. Increasing Zr content diminished the piezoelectric coefficient (d33) and the grain size. The value of d33 decreases by increasing Zr content, and there is an inverse relationship between grain size and d33. The remnant polarization of BZT increases with increasing Zr4+ content, which may be suitable for permanent memory device applications.

Structure, Morphology and Electrical/Magnetic Properties of Ni-Mg Nano-Ferrites from a New Perspective.

Using the auto combustion flash method, Ni1-x+2Mgx+2Fe2+3O4 (x = 0, 0.2, 0.6, 0.8 and 1) nano-ferrites were synthesized. All samples were thermally treated at 973 K for 3 h. The structural analysis for the synthesized samples was performed using XRD, high-resolution transmission electron microscopy (HRTEM), and FTIR. Scanning electron microscopy (SEM) was undertaken to explore the surface morphology of all the samples. The thermal stability of these samples was investigated using thermogravimetric analysis (TGA). XRD data show the presence of a single spinel phase for all the prepared samples. The intensity of the principal peak of the spinel phase decreases as Mg content increases, showing that Mg delays crystallinity. The Mg content raised the average grain size (D) from 0.084 µm to 0.1365 µm. TGA shows two stages of weight loss variation. The vibrating sample magnetometer (VSM) measurement shows that magnetic parameters, such as initial permeability (µi) and saturation magnetization (Ms), decay with rising Mg content. The permeability and magnetic anisotropy at different frequencies and temperatures were studied to show the samples' magnetic behavior and determine the Curie temperature (TC), which depends on the internal structure. The electrical resistivity behavior shows the semi-conductivity trend of the samples. Finally, the dielectric constant increases sharply at high temperatures, explained by the increased mobility of charge carriers, and decreases with increasing frequency.