RESUMEN
Recently, the manufacturing of porous polydimethylsiloxane (PDMS) with engineered porosity has gained considerable interest due to its tunable material properties and diverse applications. An innovative approach to control the porosity of PDMS is to use transient liquid phase water to improve its mechanical properties, which has been explored in this work. Adjusting the ratios of deionized water to the PDMS precursor during blending and subsequent curing processes allows for controlled porosity, yielding water emulsion foam with tailored properties. The PDMS-to-water weight ratios were engineered ranging from 100:0 to 10:90, with the 65:35 specimen exhibiting the best mechanical properties with a Young's Modulus of 1.17 MPa, energy absorption of 0.33 MPa, and compressive strength of 3.50 MPa. This led to a porous sample exhibiting a 31.46% increase in the modulus of elasticity over a bulk PDMS sample. Dowsil SE 1700 was then added, improving the storage capabilities of the precursor. The optimal storage temperature was probed, with -60 °C resulting in great pore stability throughout a three-week duration. The possibility of using these water emulsion foams for paste extrusion additive manufacturing (AM) was also analyzed by implementing a rheological modifier, fumed silica. Fumed silica's impact on viscosity was examined, revealing that 9 wt% of silica demonstrates optimal rheological behaviors for AM, bearing a viscosity of 10,290 Pa·s while demonstrating shear-thinning and thixotropic behavior. This study suggests that water can be used as pore-formers for PDMS in conjunction with AM to produce engineered materials and structures for aerospace, medical, and defense industries as sensors, microfluidic devices, and lightweight structures.
RESUMEN
The integration of 3D printed sensors into hosting structures has become a growing area of research due to simplified assembly procedures, reduced system complexity, and lower fabrication cost. Embedding 3D printed sensors into structures or bonding the sensors on surfaces are the two techniques for the integration of sensors. This review extensively discusses the fabrication of sensors through different additive manufacturing techniques. Various additive manufacturing techniques dedicated to manufacture sensors as well as their integration techniques during the manufacturing process will be discussed. This review will also discuss the basic sensing mechanisms of integrated sensors and their applications. It has been proven that integrating 3D printed sensors into infrastructures can open new possibilities for research and development in additive manufacturing and sensor materials for smart goods and the Internet of Things.
RESUMEN
This research presents a simple method to additively manufacture Cone 5 porcelain clay ceramics by using the direct ink-write (DIW) printing technique. DIW has allowed the application of extruding highly viscous ceramic materials with relatively high-quality and good mechanical properties, which additionally allows a freedom of design and the capability of manufacturing complex geometrical shapes. Clay particles were mixed with deionized (DI) water at different ratios, where the most suitable composition for 3D printing was observed at a 1:5 w/c ratio (16.2 wt.%. of DI water). Differential geometrical designs were printed to demonstrate the printing capabilities of the paste. In addition, a clay structure was fabricated with an embedded wireless temperature and relative humidity (RH) sensor during the 3D printing process. The embedded sensor read up to 65% RH and temperatures of up to 85 °F from a maximum distance of 141.7 m. The structural integrity of the selected 3D printed geometries was confirmed through the compressive strength of fired and non-fired clay samples, with strengths of 70 MPa and 90 MPa, respectively. This research demonstrates the feasibility of using the DIW printing of porcelain clay with embedded sensors, with fully functional temperature- and humidity-sensing capabilities.