RESUMEN
The chemoresistive properties of multilayer titanium-containing Ti2CTx and Ti3C2Tx MXenes, synthesized by etching the corresponding MAX phases with NaF solution in hydrochloric acid, and the composites based on them, obtained by partial oxidation directly in a sensor cell in an air flow at 150 °C, were studied. Significant differences were observed for the initial MXenes, both in microstructure and in the composition of surface functional groups, as well as in gas sensitivity. For single Ti2CTx and Ti3C2Tx MXenes, significant responses to oxygen and ammonia were observed. For their partial oxidation at a moderate temperature of 150 °C, a high humidity sensitivity (T, RH = 55%) is observed for Ti2CTx and a high and selective response to oxygen for Ti3C2Tx at 125 °C (RH = 0%). Overall, these titanium-containing MXenes and composites based on them are considered promising as receptor materials for low temperature oxygen sensors.
RESUMEN
At present, a new class of 2D nanomaterials, MXenes, is of great scientific and applied interest, and their application prospects are very broad, including as effective doping components for receptor materials of MOS sensors. In this work we have studied the influence on the gas-sensitive properties of nanocrystalline zinc oxide synthesized by atmospheric pressure solvothermal synthesis, with the addition of 1-5% of multilayer two-dimensional titanium carbide Ti2CTx, obtained by etching Ti2AlC with NaF solution in hydrochloric acid. It was found that all the obtained materials have high sensitivity and selectivity with respect to 4-20 ppm NO2 at a detection temperature of 200 °C. It is shown that the selectivity towards this compound is best for the sample containing the highest amount of Ti2CTx dopant. It has been found that as the MXene content increases, there is an increase in nitrogen dioxide (4 ppm) from 1.6 (ZnO) to 20.5 (ZnO-5 mol% Ti2CTx). reactions which the responses to nitrogen dioxide increase. This may be due to the increase in the specific surface area of the receptor layers, the presence of MXene surface functional groups, as well as the formation of the Schottky barrier at the interface between the phases of the components.
RESUMEN
ZnO/Fe2O3 nanocomposites with different concentration and thickness of the Fe2O3 layer were obtained by two-stage aerosol vapor deposition (AACVD). It was shown that the ZnO particles have a wurtzite structure with an average size of 51-66 nm, and the iron oxide particles on the ZnO surface have a hematite structure and an average size of 23-28 nm. According to EDX data, the iron content in the films was found to be 1.3-5.8 at.%. The optical properties of the obtained films were studied, and the optical band gap was found to be 3.16-3.26 eV. Gas-sensitive properties at 150-300 °C were studied using a wide group of analyte gases: CO, NH3, H2, CH4, C6H6, ethanol, acetone, and NO2. A high response to 100 ppm acetone and ethanol at 225-300 °C and a high and selective response to 300-2000 ppb NO2 at 175 °C were established. The effect of humidity on the magnitude and shape of the signal obtained upon NO2 detection was studied.