RESUMEN
Current research into the production of sustainable construction materials for retrofitting and strengthening historic structures has been rising, with geopolymer technology being seen as an advantageous alternative to traditional concrete. Fiber reinforcement using this novel cementitious material involves a low embodied carbon footprint while ensuring cohesiveness with local materials. This study aims to develop fly ash-based geopolymers reinforced with six different types of fibers: polyvinyl alcohol, polypropylene, chopped basalt, carbon fiber, and copper-coated stainless steel. The samples are produced by mixing the geopolymer mortar in random distribution and content. Twenty-eight geopolymer mixes are evaluated through compressive strength, split-tensile strength, and modulus of elasticity to determine the fiber mix with the best performance compared with pure geopolymer mortar as a control. Polyvinyl alcohol and copper-coated stainless-steel fiber samples had considerably high mechanical properties and fracture toughness under applied tensile loads. However, the polypropylene fiber source did not perform well and had lower mechanical properties. One-way ANOVA verifies these results. Based on these findings, polyvinyl alcohol and stainless-steel fibers are viable options for fiber reinforcement in historical structures, and further optimization and testing are recommended before application as a reinforcement material in historic structures.
RESUMEN
Approximately 2.78 Mt of coal fly ash is produced in the Philippines, with a low utilization rate. Using fly ash-based geopolymer for construction will lessen the load sent to landfills and will result in lower GHG emissions compared to OPC. It is necessary to characterize the fly ash and optimize the geopolymer components to determine if it can replace OPC for in situ applications. The activator-to-precursor ratio, the water-to-solids ratio, and the sodium hydroxide-to-sodium silicate ratio were optimized using a randomized I-optimal design from the experimental results of 21 runs with five replicates, for a total of 105 specimens of 50 mm × 50 mm × 50 mm paste cubes. The engineering properties chosen as the optimization responses were the unconfined compressive strength (UCS), the initial setting time, and the final setting time. The samples were also ambient-cured with the outdoor temperature ranging from 30 °C to 35 °C and relative humidity of 50% ± 10% to simulate the on-site environment. Runs with high unconfined compressive strength (UCS) and short setting times were observed to have a low water-to-solids (W/S) ratio. All runs with a UCS greater than 20 MPa had a W/S ratio of 0.2, and the runs with the lowest UCS had a W/S of 0.4. The initial setting time for design mixes with a W/S ratio of 0.2 ranged from 8 to 105 min. Meanwhile, five out of seven design mixes with a W/S ratio of 0.4 took longer than 1440 min to set. Specimens with an alkali activator ratio (NaOH/WG) of 0.5 (1:2) and 0.4 (1:2.5) also had significantly lower setting times than those with an alkali activator ratio of 1. The RSM model was verified through confirmatory tests. The results of the confirmatory tests are agreeable, with deviations from the expected UCS ranging from 0 to 38.12%. The generated model is a reliable reference to estimate the UCS and setting time of low-calcium FA geopolymer paste for in situ applications.
