Comparative physical and mechanical properties of a 3D printed temporary crown and bridge restorative material.

Background: The objective was to compare physic-mechanical properties of different materials used for temporary restorations. Material and Methods: Protemp 4/bisacrylic resin, Jet/acrylic resin, and Nexdent C&B/3D-printed resin samples (10mm diameter x 2mm thickness) were analyzed for surface roughness and color stability tests (baseline, after 5 thousand brushing cycles; and after artificial aging in water at 60oC for 24 hours) and Knoop microhardness. All data were checked for normality using Shapiro-Wilk test. Surface roughness and color stability were analyzed using two-way repeated measurements ANOVA, microhardness data was subjected to one-way ANOVA. All tests were followed by Tukey test and were performed with α=0.05. Results: For roughness, material (p=.002), time points (p=.002) and interaction between both (p<.001) were significant. All groups presented similar roughness for measurements of baseline and after brushing. After artificial aging, 3D printed resin showed decreased roughness when compared with other resins, and with its baseline reading. Acrylic resin showed an increase in surface roughness (when compared with measurement after brushing cycles). Considering color stability, only the material (p=.039) and the time (p<0.001) were significant. All groups showed similar color variation before and after artificial aging. There was an increase in color alteration after artificial aging for all groups. Considering microhardness test (p<.001), the 3D printed resin showed the highest values and acrylic resin the lowest. Bysacylic resin was similar to both 3D printed and acrylic resins. Conclusions: The tested 3D printed resins present similar or better properties than other tested temporary materials while being integrated with the digital workflow. Key words:Disinfection methods, hydroxyl radical, environment, surfaces, dentistry.

The stamp technique for direct restoration in a ICDAS 4 carious lesion: A 4-year follow-up.

OBJECTIVE: This case report described the use of a stamping technique associated with a bulk fill composite to restore an ICDAS 4 carious lesion on a posterior tooth. The 4-year follow-up is also presented. CLINICAL CONSIDERATIONS: A 32-year-old patient presented a carious lesion on tooth 36 with an underlying dark shadow at the dentin seen from the noncavitated enamel occlusal surface, which was compatible with an ICDAS 4 carious lesion. The lesion was radiographically detected and the caries disease was treated with dietary and hygiene habits orientations. Before accessing the lesion and selectively removing the carious tissue, an occlusal stamp was made by applying a flowable resin composite to copy the anatomy of the noncavitated enamel surface. The cavity was restored using a bulk fill resin composite (Opus Bulk Fill, FGM) with 4-mm-thick increments. Before curing the last increment, a Teflon band was adapted at the uncured bulk fill composite surface and the occlusal stamp made with the flowable composite was pressed against it to reproduce the natural characteristics and initial occlusal anatomy. The top surface was light-activated for 40 s. After 4 years, small wear could be seen in the restoration, but still within clinically acceptable levels. CONCLUSION: The occlusal stamp technique allows reproduction of the natural anatomy of teeth affected by ICDAS 4 carious lesions with good clinical longevity over 4 years. CLINICAL SIGNIFICANCE: This case report presents the use of the stamp technique to restore a tooth affected by an ICDAS 4 lesion, in which a carious process reached the dentin and the enamel anatomy was still preserved. The bulk fill resin composite associated with the occlusal stamp was chosen to quickly restore the cavity with clinical predictability. Bulk fill composites allow the insertion of up to 4-mm-thick increments and offer lower shrinkage stress, good clinical longevity and a less time-consuming procedure in cases of posterior teeth, especially if associated with the stamp technique.

Dentin bond strength evaluation between a conventional and universal adhesive using etch-and-rinse strategy

Aim: The aim of this study was to compare the microtensile bond strength (µTBS) and the characteristics of the adhesive interface of Scotchbond Universal - SU ­ etch-and-rise mode (3M ESPE) and Adper Scotchbond Multi-Purpose - MP (3M ESPE) to dentin over time. Methods: Class I cavity preparations were performed in 60 human molars that were randomly divided according to the dentin bonding system (DBS) used (n=30): (1) Acid conditioning + SU and (2) Acid conditioning + MP. For bonding strength (BS) analysis, 30 teeth (n = 15) were sectioned into sticks and submitted to the microtensile test in a universal testing machine after 24 hours and 12 months. The adhesive interface of the others 30 teeth was analyzed in a confocal microscope after 24 hours and 12 months. The data of µTBS were analyzed by two-way repeated measures ANOVA and Tukey's HSD (α = 0.05). Results: SU presented the lowest DBS compared to MP (p=0.000). Time did not influenced DBS for both adhesive systems (p=0.177). Confocal microscopy analysis showed no cracks between both adhesive systems tested. Conclusion: The results indicate that MP - µTBS showed a better performance compared to SU in total-etch mode

Effect of the addition of functionalized TiO2 nanotubes and nanoparticles on properties of experimental resin composites.

OBJECTIVE: To evaluate the influence of the addition of functionalized and non-functionalized TiO2 nanostructures on properties of a resin composite. METHODS: TiO2 nanostructures were synthesized and functionalized, using 3-(aminopropyl)triethoxysilane (APTMS) and 3-(trimethoxysilyl)propyl methacrylate (TSMPM). Characterizations were performed with XRD, EDS, TEM, and TGA. Resin composites containing Bis-GMA/TEGDMA, CQ, DABE, and barium-aluminum silicate glass were produced according to TiO2 nanostructure (nanotube or nanoparticle), concentration (0.3 or 0.9 wt%), and functionalization (APTMS or TSMPM). The resin composite without nanostructures was used as control. The amount of fillers was kept constant at 78.3 wt% for all materials. The degree of conversion (DC - at 0 h and 24 h), maximum polymerization rate (Rpmax), and Knoop microhardness (KHN before and after ethanol softening) were evaluated. Data were analyzed with two-way ANOVA with repeated measures and Tukey's HSD (α = 0.05). RESULTS: TGA results demonstrated that functionalizations were effective for both nanostructures. For DC, resin composites, time and interaction effect were significant (p < 0.001). Higher DC was found for 0.3-wt%-functionalized-nanotubes at 24 h. For nanoparticles, only 0.9-wt%-non-functionalized and 0.3-wt%-APTMS-functionalized showed DC similar to the control and all other groups showed higher DC (p < 0.05). Rpmax was higher for 0.3-wt%-APTMS-nanotubes, which corresponded to higher DC after 24 h. The lowest Rpmax occurred for 0.9-wt%-TSMPM-nanotubes, which showed smaller DC at 0 h. For KHN, resin composites, ethanol softening and interaction effect were significant (p < 0.001). KHN decreased after ethanol softening all groups, except for 0.3-wt%-TSMPM-nanotubes, 0.9-wt%-TSMPM-nanotubes, and 0.3-wt%-non-functionalized-nanoparticles. CONCLUSION: The resin with 0.3-wt%-TSMPM-nanotubes showed higher DC after 24 h, while being the most stable material after the ethanol softening. SIGNIFICANCE: The addition of functionalized TiO2 nanostructures in resin-based materials may improve the properties of the material.

Color evaluation of white spot lesions treated with resin infiltration after water or grape juice storage

Aim: To evaluate the color stability of bovine enamel with artificial white spot lesions treated with resin infiltration (ICON) or remineralization with fluoride using two storage methods. Methods: Sixty incisors were submitted to artificial white spot lesion induced by demineralization-remineralization (DE-RE) cycling. Initial color was evaluated with CIE-Lab to measure ΔEab. Demineralized teeth were divided according to the treatment of the white spot lesion (n = 20): 1) Remineralization with 2% neutral fluoride gel for 4min (control); 2) ICON application following manufacturer's recommendations; and 3) ICON with decreased drying time after the application of ethanol. After 24h, color was evaluated and samples were subdivided (n = 10) according to storage: 1) distilled water for 1 month; 2) grape juice for 10min daily. After storage, color was evaluated. L*, a* and b* data were analyzed by one-way ANOVA and ∆Eab data by two-way ANOVA followed by Tukey's HSD (α = 0.05). Results: L* was affected by juice storage, and decreased when ICON was applied with decreased drying time after the ethanol application. The same behavior occurred with a* (increase with reduced drying time), while b* was not affected. For ∆Eab significant differences were observed between groups (p = 0.0219) and storage methods (p = 0.0007). There was no interaction effect (p = 0.1118). Remineralization with fluoride presented the lowest color changes after storage in water. Conclusion: Treatment of artificial carious lesions with resin infiltration presented greater color changes than fluoride remineralization after storage in both solutions in vitro