We have examined the crystal structures and structural phase transitions of the deuterated, partially deuterated and hydrogenous organic-inorganic hybrid perovskite methyl ammonium lead iodide (MAPbI3) using time-of-flight neutron and synchrotron X-ray powder diffraction. Near 330 K the high temperature cubic phases transformed to a body-centered tetragonal phase. The variation of the order parameter Q for this transition scaled with temperature T as Q â¼ (Tc-T)ß, where Tc is the critical temperature and the exponent ß was close to », as predicted for a tricritical phase transition. However, we also observed coexistence of the cubic and tetragonal phases over a range of temperature in all cases, demonstrating that the phase transition was in fact first-order, although still very close to tricritical. Upon cooling further, all the tetragonal phases transformed into a low temperature orthorhombic phase around 160 K, again via a first-order phase transition. Based upon these results, we discuss the impact of the structural phase transitions upon photovoltaic performance of MAPbI3 based solar cells.
RESUMEN
The effect of nanoparticles (NP) on chain dimensions in polymer melts has been the source of considerable theoretical and experimental controversy. We exploit our ability to ensure a spatially uniform dispersion of 13 nm silica NPs miscible in polystyrene melts, together with neutron scattering, x-ray scattering, and transmission electron microscopy, to show that there is no measurable change in the polymer size in miscible mixtures, regardless of the relative sizes of the chains and the nanoparticles, and for NP loadings as high as 32.7 vol%. Our results provide a firm basis from which to understand the properties of polymer nanocomposites.