RESUMEN
In this study, the thermoluminescence (TL) properties of natural NaCl from Lluta, Arequipa-Peru was investigated. The number of peaks and the kinetic parameters associated with the TL glow peaks of NaCl sample after gamma-irradiation were analyzed by initial rise and deconvolution method. Defect centers induced in pure salt by gamma irradiation have been studied by electron spin resonance (ESR) with a view to identify the centers associated with the TL process in the salt. Thermal annealing experiments indicate the presence of three defect centers. Center I characterized by the g-value 2.011 is identified as an O- ion and relates with the dominant TL peak at 220 °C. Center II with a g-value of 2.0058 is attributed to a F center and is found to correlate with the 128 °C TL peak. Center III has of g-value 2.014 and is also assigned to an O- ion.
RESUMEN
This study shows that there are some ionic crystals which after irradiation with high gamma dose Dm and subsequent irradiation with low doses ranging up to 500Gy present a decreasing TL intensity as dose increases. This interesting feature can be used as a calibration curve in radiation dosimetry. Such behavior can be found in green quartz, three varieties of beryl and pink tourmaline. In all these silicate crystals it can be shown that irradiation with increasing γ-dose there is a dose Dm for which the TL intensity is maximum. Of course, Dm varies depending on the crystal and irradiated crystal with the dose Dm is stable. If one of these crystals is taken and irradiated with doses from low values up to 400-500Gy, a curve of decreasing TL intensity is obtained; such a curve can be used as a calibration curve.
RESUMEN
L3PO4:Mg,Cu, a low effective atomic number and high sensitivity TSL phosphor, has been prepared. Its TSL glow curve shows a major peak around 360 degrees C with minor peaks around 110 degrees C and 230 degrees C. The optimum concentrations of the dopants are found to be 200 ppm each. Its gamma sensitivity is 1.2 times as compared to CaSO4:Dy (0.1 mol%). The optimum preirradiation annealing treatment is found to be 650 degrees C, 15 min. Its PL emission shows a band at 370 nm with excitation band at 250 nm. Dose to TSL response shows that its response is linear up to the gamma dose of 100 Gy for irradiations carried out at RT. An irradiated sample shows a distinct new ESR signal, which is tentatively assigned to an electron/hole localised on one of the oxygen(s) of the phosphate group. Step annealing experiments show decay of the defect centre around 340 degrees C. This correlates well with the TSL peak around 360 degrees C.