Fabrication of 3D Printed poly(lactic acid) strut and wet-electrospun cellulose nano fiber reinforced chitosan-collagen hydrogel composite scaffolds for meniscus tissue engineering.

The main goal of the study was to produce chitosan-collagen hydrogel composite scaffolds consisting of 3D printed poly(lactic acid) (PLA) strut and nanofibrous cellulose for meniscus cartilage tissue engineering. For this purpose, first PLA strut containing microchannels was incorporated into cellulose nanofibers and then they were embedded into chitosan-collagen matrix to obtain micro- and nano-sized topographical features for better cellular activities as well as mechanical properties. All the hydrogel composite scaffolds produced by using three different concentrations of genipin (0.1, 0.3, and 0.5%) had an interconnected microporous structure with a swelling ratio of about 400% and water content values between 77 and 83% which is similar to native cartilage extracellular matrix. The compressive strength of all the hydrogel composite scaffolds was found to be similar (∼32 kPa) and suitable for cartilage tissue engineering applications. Besides, the hydrogel composite scaffold comprising 0.3% (w/v) genipin had the highest tan δ value (0.044) at a frequency of 1 Hz which is around the walking frequency of a person. According to the in vitro analysis, this hydrogel composite scaffold did not show any cytotoxic effect on the rabbit mesenchymal stem cells and enabled cells to attach, proliferate and also migrate through the inner area of the scaffold. In conclusion, the produced hydrogel composite scaffold holds great promise for meniscus tissue engineering.

Wet-electrospun PHBV nanofiber reinforced carboxymethyl chitosan-silk hydrogel composite scaffolds for articular cartilage repair.

The objective of the study was to produce three-dimensional and porous nanofiber reinforced hydrogel scaffolds that can mimic the hydrated composite structure of the cartilage extracellular matrix. In this regard, wet-electrospun poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) nanofiber reinforced carboxymethyl chitosan-silk fibroin (PNFs/CMCht-SF) hydrogel composite scaffolds that were chemically cross-linked by poly(ethylene glycol) diglycidyl ether (PEGDE) were produced. To the best of our knowledge, this is the first study in cartilage regeneration where a three dimensional porous spongy composite scaffold was obtained by the dispersion of wet-electrospun nanofibers within a polymer matrix. All of the produced hydrogel composite scaffolds had an interconnected microporous structure with well-integrated PHBV nanofibers on the pore walls. The scaffold comprising an equal amount of PEGDE and polymer (PNFs/CMCht-SF1:PEGDE1) demonstrated comparable water content (91.4 ± 0.7%), tan δ (0.183 at 1 Hz) and compressive strength (457 ± 85 kPa) values to that of articular cartilage. Besides, based on the histological analysis, this hydrogel composite scaffold supported the chondrogenic differentiation of bone marrow mesenchymal stem cells. Consequently, this hydrogel composite scaffold presented a great promise for cartilage tissue regeneration.