Development of microfiltration membranes based on polysulfone and polyetherimide blends.

In this study, membranes blended with polysulfone (PSU) and polyetherimide (PEI) polymers in different ratios were fabricated. Their potential to remove pollutants from rivers, which are a potential drinking water source, was investigated. Scanning electron microscopy analysis revealed that the PSU membranes had a dense and homogeneous layer, whereas the addition of PEI formed a spongy substrate. The water content of the fabricated membranes varied between 5.37 and 22.42%, porosities 28.73-89.36%, contact angles 69.18-85.81%, and average pure water fluxes 257.25-375.32 L/m2 h. The blended membranes removed turbidity, chloride, alkalinity, conductivity, sulfate, iron, manganese, and total organic carbon up to 98.32, 92.28, 96.87, 90.67, 99.58, 94.63, 97.48, and 79.11%, respectively. These results show that when PEI was added to the PSU polymer, the filtration efficiency increased owing to an increase in the hydrophilicity of the membranes. Blending these two polymers enabled the optimization of membrane properties such as permeability, selectivity, and mechanical strength. In addition, membrane fabrication processes are simple and incur low costs.

Halloysite Nanotube-Enhanced Polyacrylonitrile Ultrafiltration Membranes: Fabrication, Characterization, and Performance Evaluation.

This research focuses on the production and characterization of pristine polyacrylonitrile (PAN) as well as halloysite nanotube (HNT)-doped PAN ultrafiltration (UF) membranes via the phase inversion technique. Membranes containing 0.1, 0.5, and 1% wt HNT in 16% wt PAN are fabricated, and their chemical compositions are examined using Fourier transform infrared (FTIR) spectroscopy. Scanning electron microscopy (SEM) is utilized to characterize the membranes' surface and cross-sectional morphologies. Atomic force microscopy (AFM) is employed to assess the roughness of the PAN/HNT membrane. Thermal characterization is conducted using thermal gravimetric analysis (TGA) and differential thermal analysis (DTA), while contact angle and water content measurements reveal the hydrophilic/hydrophobic properties. The pure water flux (PWF) performance of the porous UF water filtration membranes is evaluated at 3 bar, with porosity and mean pore size calculations. The iron (Fe), manganese (Mn), and total organic carbon (TOC) removal efficiencies of PAN/HNT membranes from dam water are examined, and the surfaces of fouled membranes are investigated by using SEM post-treatment. Mechanical characterization encompasses tensile testing, the Mori-Tanaka homogenization approach, and finite element analysis. The findings offer valuable insights into the impact of HNT doping on PAN membrane characteristics and performance, which will inform future membrane development initiatives.

Characterisation and modelling the mechanics of cellulose nanofibril added polyethersulfone ultrafiltration membranes.

The performance of the membranes can be improved by adding the appropriate amount of nanomaterials to the polymeric membranes that can be used for water/wastewater treatment. In this study, the effects of polyvinylpyrrolidone (PVP), the impact of different amounts (0.5% and 1% wt.) of cellulose nanofibril (CNF), and the combined effects of PVP-CNF on the properties/performance of the polyethersulfone-based (PES-based) membrane are investigated. All PES-based ultrafiltration (UF) membranes are manufactured employing the phase inversion method and characterised via Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), and the relevant techniques to determine the properties, including porosity, mean pore size, contact angle, water content, and pure water flux tests. Furthermore, the thermal properties of the prepared membranes are investigated using thermal gravimetric analysis (TGA) and differential thermal analysis (DTA) techniques. Experimental and numerical methods are applied for the mechanical characterisation of prepared membranes. For the experimental process, tensile tests under dry and wet conditions are conducted. The finite element (FE) method and Mori-Tanaka mean-field homogenisation are used as numerical methods to provide more detailed knowledge of membrane mechanics.

Effects of Fe(OH)3 and MnO2 Flocs on Iron/Manganese Removal and Fouling in Aerated Submerged Membrane Systems.

Many treatment methods are used to remove iron and manganese from water. Aeration and membrane filtration are two of these methods. In this study, Fe2+ and Mn2+ removal by aeration with different catalysts and instead of simple membrane filtration applied in other studies, the aerated-submerged membrane systems were evaluated separately. When Fe(OH)3 was applied in the aeration step and complete oxidation of Fe2+ was obtained after 27 min, while complete Mn2+ oxidation was obtained in 76 min. However, when MnO2 was applied in the aeration step, complete oxidation of Fe2+ and Mn2+ was relatively slow (36 and 110 min, respectively). According to the results obtained from the aerated membrane system, Fe2+ and Mn2+ removal were extended by Fe(OH)3 via adsorption/surface oxidation. It is clearly shown from the flux, resistance results, scanning electron microscope (SEM) and Fourier transform infrared (FT/IR) spectroscopy observation that manganese oxides were deposited mainly in membrane pores forming membrane fouling by small flocs, while iron oxide particles were deposited on the membrane surface. Although the flux performance of PT PES membrane was higher than HF PP membrane, fouling resistance of HF PP membrane was higher than PT PES.

Effect of PVP content and polymer concentration on polyetherimide (PEI) and polyacrylonitrile (PAN) based ultrafiltration membrane fabrication and characterization.

In this study, four different membranes were fabricated by using polyetherimide and polyacrylonitrile polymers, N-methyl-2-pyrrolidone and polyvinylpyrrolidone (PVP) via phase inversion method to improve the membrane performance in fruit juice wastewater (FJWW) treatment. The addition of PVP to the casting solution increased membrane hydrophilicity, water content, contact angle, porosity, Fourier transform infrared spectroscopy peaks, membrane thickness, average roughness and viscosity of cast solutions compared to the bare membrane. It can be said that the addition of a lower polymer concentration and PVP intensively increases the pure water flux of the membrane. However, as the flux increased, a small decrease in FJWW rejection was observed.