Exploration of multifunctional wood coating based on an interpenetrating network system of rosin-CO2-based polyurethane and mussel bionic rosin-based benzoxazine.

Polyurethane (PU) prepared by blending rosin base and CO2-polyol already has good mechanical properties and hydrophobic effect and has powerful benefits in acid and alkali resistance and salt resistance. In this study, mussel bionic rosin-based benzoxazine (BZ) was synthesized using dehydroabietylamine, catechol, and paraformaldehyde. Mixing BZ into PU can endow the resulting PU/BZ with special effects such as zero curing shrinkage, excellent mechanical behavior, and flame retardancy through a 3D interpenetrating network system. From the results, the modulus of rupture (MOR) and modulus of elasticity (MOE) of PU wood coatings are 97.04 and 2601.97 MPa, respectively; in contrast, the PU/BZ wood coatings exhibited higher values of MOR and MOE of 110.87 and 2738.11 MPa. PU/BZ wood coatings show higher flexural strength and elastic modulus. They are also stronger than PU coatings in terms of acid/alkali and aging resistance. At the same time, the coating is endowed with flame retardant properties, and the LOI is 30.2 due to the presence of BZ. Thus, PU/BZ can be a versatile and practical wood coating. The interpenetrating network system of PU/BZ has an innovative impact on the preparation of wood coatings.

Novel dopamine-modified cellulose acetate ultrafiltration membranes with improved separation and antifouling performances.

Cellulose acetate (CA) is widely used in the preparation of ultrafiltration membranes due to its many excellent characteristics, especially chemical activity and biodegradability. To improve the inherent hydrophobic and antifouling properties of CA membrane, in this work, CA was successfully modified with dopamine (CA-2,3-DA) through selective oxidation and Schiff base reactions, which was confirmed by FTIR and 1H NMR measurements. Then, CA-2,3-DA membrane with high water permeability and excellent antifouling property was prepared by the phase inversion method. Compared with the original CA membrane, the CA-2,3-DA membrane maintained a higher rejection ratio for BSA (92.5%) with a greatly increased pure water flux (167.3 L m-2 h-1), which could overcome the trade-off between permeability and selectivity of the traditional CA membrane to a certain extent. According to static protein adsorption and three-cycle dynamic ultrafiltration experiments, the CA-2,3-DA membrane showed good antifouling performance and superior long-term performance stability, as supported by the experimental results, including flux recovery ratio, flux decline ratio, and filtration resistance. It is expected that this approach can greatly expand the high-value utilization of modified natural organic polysaccharides in separation engineering.

Development and investigation of novel antifouling cellulose acetate ultrafiltration membrane based on dopamine modification.

In this contribution, a novel cellulose acetate modified with dopamine (CA-DA) membrane material was designed and prepared by a two-step route consist of chlorination and further substitution reactions. The chemical structure of the prepared CA-DA material was determined by FTIR and 1H NMR, respectively. The CA-DA ultrafiltration membrane was subsequently fabricated by the scalable phase inversion process. Compared with cellulose acetate membrane as the control sample, the introduction of dopamine improved the porosity, pore size and hydrophilicity of the CA-DA membrane, which was helpful to the water permeability (181.2 L/m2h) without obviously affecting the protein rejection (93.5%). According to the static protein adsorption and dynamic cycle ultrafiltration experiments, the CA-DA membrane displayed persistent antifouling performance, which was verified by flux recovery ratio, flux decline ratio and filtration resistance. Moreover, the water flux recovery ratio of the CA-DA membrane was retained at 97.3% after three-cycles of BSA solution filtration, which was much higher than that of the reference CA membrane. This new approach provided a long life and excellent ultrafiltration performance for polymer-based membranes, which has potential application prospects in the field of separation process.