Organic-inorganic hybrid nanoparticles controlled delivery system for anticancer drugs.

The use of organic-inorganic hybrid nanocarriers for controlled release of anticancer drugs has been gained a great interest, in particular, to improve the selectivity and efficacy of the drugs. In this study, iron oxide nanoparticles were prepared then surface modified via diazonium chemistry and coated with chitosan, and its derivative chitosan-grafted polylactic acid. The purpose was to increase the stability of the nanoparticles in physiological solution, heighten drug-loading capacity, prolong the release, reduce the initial burst effect and improve in vitro cytotoxicity of the model drug doxorubicin. The materials were characterized by DLS, ζ-potential, SEM, TGA, magnetization curves and release kinetics studies. Results confirmed the spherical shape, the presence of the coat and the advantages of using chitosan, particularly its amphiphilic derivative, as a coating agent, thereby surpassing the qualities of simple iron oxide nanoparticles. The coated nanoparticles exhibited great stability and high encapsulation efficiency for doxorubicin, at over 500µg per mg of carrier. Moreover, the intensity of the initial burst was clearly diminished after coating, hence represents an advantage of using the hybrid system over simple iron oxide nanoparticles. Cytotoxicity studies demonstrate the increase in cytotoxicity of doxorubicin when loaded in nanoparticles, indirectly proving the role played by the carrier and its surface properties in cell uptake.

Synthesis, Characterization, and Antimicrobial Activity of Near-IR Photoactive Functionalized Gold Multibranched Nanoparticles.

Surface-modified gold multibranched nanoparticles (AuMs) were prepared by simple chemical reduction of gold chloride aqueous solution followed by in situ modification by using water-soluble arenediazonium tosylates with different functional organic groups. Chemical and morphological structures of the prepared nanoparticles were examined by using transmission electron and scanning electron microscopies. The covalent grafting of organic compounds was confirmed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDX) and Raman spectroscopy techniques. Covalent functionalization of nanoparticles significantly expands the range of their potential uses under physiological conditions, compared with traditional non-covalent or thiol-based approaches. The antibacterial effect of the surface-modified AuMs was evaluated by using Escherichia coli and Staphylococcus epidermidis bacteria under IR light illumination and without external triggering. Strong plasmon resonance on the AuMs cups leads to significant reduction of the light power needed kill bacteria under the mild conditions of continuous illumination. The effect of the surface-modified AuMs on the light-induced antibacterial activities was founded to be dependent on the grafted organic functional groups.

The convenient preparation of stable aryl-coated zerovalent iron nanoparticles.

A novel approach for the in situ synthesis of zerovalent aryl-coated iron nanoparticles (NPs) based on diazonium salt chemistry is proposed. Surface-modified zerovalent iron NPs (ZVI NPs) were prepared by simple chemical reduction of iron(III) chloride aqueous solution followed by in situ modification using water soluble arenediazonium tosylate. The resulting NPs, with average iron core diameter of 21 nm, were coated with a 10 nm thick organic layer to provide long-term protection in air for the highly reactive zerovalent iron core up to 180 °C. The surface-modified iron NPs possess a high grafting density of the aryl group on the NPs surface of 1.23 mmol/g. FTIR spectroscopy, XRD, HRTEM, TGA/DTA, and elemental analysis were performed in order to characterize the resulting material.

Preparation and X-ray Structural Study of Dibenziodolium Derivatives.

New experimental procedures for the preparation of dibenziodolium salts by oxidative cyclization of 2-iodobiphenyl in the presence of appropriate strong acids are described. Particularly useful is a convenient one-pot synthesis of dibenziodolium hydrogen sulfate from 2-iodobiphenyl using Oxone as an inexpensive and environmentally safe oxidant. Dibenziodolium hydrogen sulfate, bis(triflyl)imidate, or triflate can be readily converted to various other dibenziodolium derivatives (chloride, bromide, thiocyanate, azide, cyanide, phenylsulfinate) by anion exchange. Structures of key products have been established by single-crystal X-ray diffraction analysis. Particularly interesting is the X-ray structure of dibenziodolium thiocyanate, which represents the first example of a structurally characterized hypervalent iodine compound with a relatively short iodine-sulfur secondary bond distance.