A family of pyridine-oxazoline-ligated cobalt complexes L2CoCl23a-h were synthesized and characterized. Determined via single-crystal X-ray diffraction, complexes 3a and 3d, ligated by two ligands, displayed a distorted tetrahedral coordination of a cobalt center. The X-ray structure indicated the pyridine-oxazoline ligands acted as unusual mono-dentate ligands by coordinating only to Noxazoline. Upon activation with AlEt2Cl (diethylaluminum chloride), these cobalt complexes all exhibited high catalytic activity (up to 2.5 × 106 g·molCo-1·h-1), affording cis-1,4-co-3,4-polyisoprene with molecular weights of 4.4-176 kg mol-1 and a narrow Ð of 1.79-3.42, suggesting a single-site nature of the active sites. The structure of cobalt catalysts and reaction parameters, especially co-catalysts and the reaction temperature, all have significant influence on the polymerization activity but not on the microstructure of polyisoprene.
RESUMEN
Polyurethane (PU) is a widely used polymer material that will age under prolonged exposure to ultraviolet (UV) light, shortening the service life. Several methods have been used to prepare the anti-UV PU, including adding nonreactive anti-UV additives, functional fillers, and biological antioxidant molecules. However, the nonreactive anti-UV additives may migrate during long-term use, the functional fillers may damage the mechanical properties and seriously reduce the light transmittance of the sample, and the biological antioxidant molecules will inevitably color the sample. To solve these problems, in this work, a benzotriazole UV absorber (Chiguard R-455) was introduced into the PU molecular chains by in situ polymerization to prepare the nonmigrating intrinsic anti-UV PU sample with high performance and colorless transparency. The anti-UV PU samples exhibit light transmittance of over 88% in the visible range and superior mechanical properties with tensile strength higher than 65 MPa and elongation at break higher than 900%. After 24 h UV irradiation (200 W, 365 nm), the tensile strength and elongation at break of pure PU sample are significantly reduced to only 8.9 and 15.8% of the original one, respectively. On the contrary, the addition of Chiguard R-455 will endow the PU sample with excellent anti-UV performance. After 24 h UV irradiation, the tensile strength (67.2 ± 1.6 MPa) and elongation at break (917.4 ± 30.0%) of PU-0.5% (the content of Chiguard R-455 is only 0.5 wt %) have changed little compared with the sample without irradiation (67.4 ± 3.5 MPa and 919.4 ± 26.5%). Additionally, the anti-UV mechanism of the PU sample is systematically studied. This work provides a feasible method for preparing colorless, transparent, high-performance, nonmigrating intrinsic UV-shielding PU samples, which can be used as a UV light-shielding material in various fields with visible and aesthetic requirements, such as protection fields and wearable products.