RESUMEN
The corrosion of metals is still a huge challenge for various industries, and the pursuit of effective treatments ensures environmental sustainability. In this study, we utilized Chiquita banana sap-water extract (BSWE) to prevent mild steel from electrochemical corrosion in a 0.1 M HCl at room temperature. Corrosion resistance was assessed using various electrochemical methodologies, combining with surface characterization techniques. The results showed a high level of effectiveness when the corrosion current density decreased from 3292.67 µA cm-2 (for the sample immerged in the blank solution) to 187.33 µA cm-2 after 24 hours of immersion in the solution containing BSWE at a 2000 ppm concentration, equivalent to corrosion efficiency of 94.32%. Surface characterization revealed diminished corrosion on the inhibited steel surface due to the formation of a protective layer. X-ray photoelectron spectroscopy results demonstrated the presence of BSWE ingredients combining with iron oxides and hydroxides to form a smooth protective layer. Furthermore, theoretical calculations also indicated that the addition of BSWE can reduce steel surface damage when exposing to corrosive environment. The inhibitor based on banana sap extract can be referred to as a sustainable protective coating since it is biodegradable, abundantly available in banana plants and free of other harmful substances.
RESUMEN
A porous and low-density protective film on a steel surface in the corrosive environment can undergo deterioration even in the presence of organic inhibitors due to infiltration of aggressive ions into the pinholes and/or pores. This phenomenon is related to the localized corrosion that takes place even in the presence of an optimal concentration of organic corrosion inhibitors in the given medium. To overcome this issue, we have designed an organic protective film on a steel surface with the help of titania nanoparticles (TNPs) combined with an organic corrosion inhibitor derived from Aganonerion polymorphum leaf extract (APLE), all to be studied in a simulated ethanol fuel blend (SEFB). The TNPs with varied diameters and concentrations have been studied for examining their effect on the inhibition capacity of 1000 ppm APLE on the steel surface in SEFB medium using electrochemical and surface analysis techniques. Enhanced corrosion inhibition of the surficial film was observed in the presence of both the APLE inhibitor and small amounts of TNPs. A direct agreement was observed between the experimental and molecular dynamics theoretical investigations showcasing high binding energy between inhibitor molecules and steel substrates, resulting in a much higher adhesion of the protective film, good thermal stability of the adsorbent film, and electron abundance for the supply of steel substrate of inhibitor species.