A Universal Electronic Structure Modulation Strategy: Is Strong Adsorption Always Correlated with High Catalysis?

Unveiling the inherent link between polysulfide adsorption and catalytic activity is key to achieving optimal performance in Lithium-sulfur (Li-S) batteries. Current research on the sulfur reaction process mainly relies on the strong adsorption of catalysts to confine lithium polysulfides (LiPSs) to the cathode side, effectively suppressing the shuttle effect of polysulfides. However, is strong adsorption always correlated with high catalysis? The inherent relationship between adsorption and catalytic activity remains unclear, limiting the in-depth exploration and rational design of catalysts. Herein, the correlation between "d-band center-adsorption strength-catalytic activity" in porous carbon nanofiber catalysts embedded with different transition metals (M-PCNF-3, M = Fe, Co, Ni, Cu) is systematically investigated, combining the d-band center theory and the Sabatier principle. Theoretical calculations and experimental analysis results indicate that Co-PCNF-3 electrocatalyst with appropriate d-band center positions exhibits moderate adsorption capability and the highest catalytic conversion activity for LiPSs, validating the Sabatier relationship in Li-S battery electrocatalysts. These findings provide indispensable guidelines for the rational design of more durable cathode catalysts for Li-S batteries.

In Situ 1D Carbon Chain-Mail Catalyst Assembly for Stable Lithium-Sulfur Full Batteries.

The main obstacles for the commercial application of Lithium-Sulfur (Li-S) full batteries are the large volume change during charging/discharging process, the shuttle effect of lithium polysulfide (LiPS), sluggish redox kinetics, and the indisciplinable dendritic Li growth. Especially the overused of metal Li leads to the low utilization of active Li, which seriously drags down the actual energy density of Li-S batteries. Herein, an efficient design of dual-functional CoSe electrocatalyst encapsulated in carbon chain-mail (CoSe@CCM) is employed as the host both for the cathode and anode regulation simultaneously. The carbon chain-mail constituted by carbon encapsulated layer cross-linking with carbon nanofibers protects CoSe from the corrosion of chemical reaction environment, ensuring the high activity of CoSe during the long-term cycles. The Li-S full battery using this carbon chain-mail catalyst with a lower negative/positive electrode capacity ratio (N/P < 2) displays a high areal capacity of 9.68 mAh cm-2 over 150 cycles at a higher sulfur loading of 10.67 mg cm-2 . Additionally, a pouch cell is stable for 80 cycles at a sulfur loading of 77.6 mg, showing the practicality feasibility of this design.