RESUMEN
The polyol synthesis of CoO nanoparticles (NPs) is typically conducted by dissolving and heating cobalt acetate tetrahydrate and water in diethylene glycol (DEG). This process yields aggregates of approximately 100 nm made of partially aligned primary crystals. However, the synthesis demands careful temperature control to allow the nucleation of CoO while simultaneously preventing reduction, caused by the activity of DEG. This restriction hinders the flexibility to freely adjust synthesis conditions, impeding the ability to obtain particles with varied morpho-structural properties, which, in turn, directly impact chemical and physical attributes. In this context, the growth of CoO NPs in polyol was studied focusing on the effect of the polyol chain length and the synthesis temperature at two different water/cations ratios. During this investigation, we found that longer polyol chains remove the previous limits of the method, allowing the tuning of aggregate size (20-150 nm), shape (spherical-octahedral), and crystalline length (8-35 nm). Regarding the characterization, our focus revolved around investigating the magnetic properties inherent in the synthesized products. From this point of view, two pivotal findings emerged. Firstly, we identified small quantities of a layered hydroxide ferromagnetic intermediate, which acted as interference in our measurements. This intermediate exhibited magnetic properties consistent with features observed in other publications on CoO produced in systems compatible with the intermediate formation. Optimal synthetic conditions that prevent the impurity from forming were found. This resolution clarifies several ambiguities existing in literature about CoO low-temperature magnetic behavior. Secondly, a regular relationship of the NPs' TN with their crystallite size was found, allowing us to regulate TN over ~ 80 K. For the first time, a branching was found in this structure-dependent magnetic feature, with samples of spheroidal morphology consistently having lower magnetic temperatures, when compared to samples with faceted/octahedral shape, providing compelling evidence for a novel physical parameter influencing the TN of a material. These two findings contribute to the understanding of the fundamental properties of CoO and antiferromagnetic materials.
RESUMEN
A charge detector has been constructed and mounted inside the vacuum housing of a commercial mass spectrometer (Micromass-Waters Quattro I, Waters Corp., Manchester, UK). The in-house built single-pass charge detector is composed of a designed, complete electronics system that includes a low-noise charge amplifier. Communication to the data acquisition system was enabled, and analog and digital filters were devised, followed by their tuning and programming. Data treatment scripts for data analysis and plotting were automated, and the assembled system was calibrated and tested. The instrument has an acquisition speed of â¼200 detection events/s, and it permits detection down to â¼510 charges (= three times RMS noise) for a single measured particle. The charge detector was employed to determine the oligomer distribution of a megadalton polymer, polyethylene glycol (PEG). The PEG size distribution exhibits a maximum at â¼ m/z 5910 with the oligomeric population mass distribution peaking near 4.45 MDa. In studies of methanol droplet dynamics, "charge vs time-of-flight" plots enabled clear visualization of the zone near the Rayleigh limit to droplet charging. The highest population of methanol droplets near the Rayleigh limit carried 5000-7000 charges. This corresponds to droplet weights of 10-20 GDa, with the high-end tail extending above 70 GDa. This visualization of the most highly charged droplets (that bear numbers of charges near those defined by the Rayleigh equation) was exploited as a calibration aid for our charge detector, which lacks a means of precisely defining ion energy. A maximum m/z error of -12.3% was calculated for the method, i.e., less than the potential error in assigning the true level of charging of the most highly charged droplets relative to the Rayleigh limit. With these limitations in mind, the introduced method will provide a new means for aiding the calibration of m/z values in charge detectors.
RESUMEN
Nanoscale heterostructures of covalent intermetallics should give birth to a wide range of interface-driven physical and chemical properties. Such a level of design however remains unattainable for most of these compounds, due to the difficulty to reach a crystalline order of covalent bonds at the moderate temperatures required for colloidal chemistry. Herein, we design heterostructured cobalt silicide nanoparticles to trigger magnetic and catalytic properties in silicon-based materials. Our strategy consists in controlling the diffusion of cobalt atoms into silicon nanoparticles, by reacting these particles in molten salts. By adjusting the temperature, we tune the conversion of the initial silicon particles toward homogeneous CoSi nanoparticles and core-shell nanoparticles made of a CoSi shell and a silicon-rich core. The increased interface-to-volume ratio of the CoSi component in the core-shell particles yields distinct properties compared to the bulk and homogeneous nanoparticles. First, the core-shell particles exhibit increased ferromagnetism, despite the bulk diamagnetic properties of cobalt monosilicide. Second, the core-shell nanoparticles act as efficient precatalysts for alkaline water oxidation, where the nanostructure is converted in situ into a layered cobalt silicon oxide/(oxy)hydroxide with high and stable oxygen evolution reaction (OER) electrocatalytic activity. This work demonstrates a route to design heterostructured nanocrystals of covalent intermetallic compounds and shows that these new structures exhibit very rich, yet poorly explored, interface-based physical properties and reactivity.