To obtain high-quality joints of Al/steel dissimilar materials, a new extrinsic-riveting friction stir lap welding (ERFSLW) method was proposed combining the synthesis advantages of mechanical riveting and metallurgical bonding. SiC-reinforced Al matrix composite bars were placed in the prefabricated holes in Al sheets and steel sheets, arranged in a zigzag array. The bars were stirred and mixed with Al sheets under severe plastic deformation (SPD), forming composite rivets to strengthen the mechanical joining. SiC particles were uniformly dispersed in the lower part of the welding nugget zone (WNZ). The smooth transition between the SiC mixed zone and extrinsic-riveting zone (ERZ) ensured the metallurgical bonding. The maximum tensile shear load of the joints reached 7.8 kN and the maximum load of the weld per unit length was 497 N/mm. The fracture occurred at the interface between the rivets and steel sheets rather than the conventional Al/steel joining interface. Moreover, ERFSLW can prolong the service life of joints due to three fracture stages. This method can be further extended to the welding of other dissimilar materials that conform to the model of "soft/hard".
RESUMEN
The medium-thick Al/Mg dissimilar friction stir welding (FSW) joint has serious groove and cavity defects due to uneven thermal distribution in the thickness direction. The submerged friction stir welding (SFSW) was employed to decrease the peak temperature of the joint and control the thermal gradient of the thickness direction, which were beneficial in suppressing the coarsening of the intermetallic compounds (IMCs) layer and improving the weld formation. According to the SEM results, the thickness value of the IMC layer in the nugget zone and shoulder affect zone decreased from 0.78 µm and 1.31 µm in FSW process to 0.59 µm and 1.21 µm in SFSW process at the same parameter, respectively. Compared with the FSW process, SFSW improves the thermal accumulation during the process, which inhibits the formation of the IMCs and facilitates the material flow to form a mechanical interlocking structure. This firm interface formation elevates the effective contact area of the whole joint interface and provides a strong connection between the dissimilar metals. Thus, the ultimate strength of the 6 mm thick Al/Mg dissimilar SFSW joints was enhanced to 171 MPa, equivalent to 71.3% of AZ31B Mg alloys strength.