Stability of Polymeric Membranes to UV Exposure before and after Coating with TiO2 Nanoparticles.

The combination of photocatalysis and membrane filtration in a single reactor has been proposed, since the photocatalytic treatment may degrade the pollutants retained by the membrane and reduce fouling. However, polymeric membranes can be susceptible to degradation by UV radiation and free radicals. In the present study, five commercial polymeric membranes were exposed to ultraviolet (UV) radiation before and after applying a sol-gel coating with TiO2 nanoparticles. Membrane stability was characterized by changes in hydrophilicity as well as analysis of soluble substances and nanoparticles detached into the aqueous medium, and by Fourier transform infrared spectroscopy (FTIR), scanning electron microscope (SEM), and energy-dispersive X-ray spectrometry (EDS) for structural, morphological, and elemental distribution analysis, respectively. The TiO2 coating conferred photocatalytic properties to the membranes and protected them during 6 h of UV radiation exposures, reducing or eliminating chemical and morphological changes, and in some cases, improving their mechanical resistance. A selected commercial nanofiltration membrane was coated with TiO2 and used in a hybrid reactor with a low-pressure UV lamp, promoting photocatalysis coupled with cross-flow filtration in order to remove 17α-ethinylestradiol spiked into an aqueous matrix, achieving an efficiency close to 100% after 180 min of combined filtration and photocatalysis, and almost 80% after 90 min.

Solvent-Free Process for the Development of Photocatalytic Membranes.

This work described a new sustainable method for the fabrication of ceramic membranes with high photocatalytic activity, through a simple sol-gel route. The photocatalytic surfaces, prepared at low temperature and under solvent-free conditions, exhibited a narrow pore size distribution and homogeneity without cracks. These surfaces have shown a highly efficient and reproducible behavior for the degradation of methylene blue. Given their characterization results, the microfiltration photocatalytic membranes produced in this study using solvent-free conditions are expected to effectively retain microorganisms, such as bacteria and fungi that could then be inactivated by photocatalysis.

Development and characterisation of hybrid polysaccharide membranes for dehydration processes.

The purpose of this work is the development and characterisation of new hybrid polysaccharide (FucoPol) membranes. These membranes were prepared by incorporation of a SiO2 network homogeneously dispersed by using a sol-gel method with GPTMS as a crosslinker silica precursor. They were further crosslinked with CaCl2 for reinforcement of mechanical properties and improvement of their permeation performance. They were characterised in terms of their structural, mechanical and thermal properties. They presented a dense and homogeneous structure, resistant to deformation, with a Tg of 43 °C and a thermal decomposition between 240 and 251 °C. The hybrid FucoPol membranes were tested for ethanol dehydration by pervaporation and also for nitrogen dehydration. They exhibited high water selectivity values, similar to PERVAP® 4101, however they lost their stability when exposed to solutions of 10.0 wt.% water in ethanol. In contrast, these membranes were stable when applied in N2 dehydration, leading to reproducible performance and very high water selectivities.