Effects of sepiolite addition to acrylic-latex paint on pull-off adhesion strength in nanosilver-impregnated and thermally-modified beech (Fagus orientalis L.) wood.

Sepiolite is a silicate mineral that improves the fire properties in solid wood when mixed with a water-based coating. The present study was carried out to investigate and evaluate the effects of sepiolite addition to acrylic-latex paint on the pull-off adhesion strength, as an important characteristic of paints and finishes used in the modern furniture industry and historical furniture as well for preservation and restoration of heritage objects. Sepiolite was added at the rate of 10%, and brushed onto plain-sawn beech (Fagus orientalis L.) wood specimens, unimpregnated and impregnated with a 400 ppm silver nano-suspension, which were further thermally modified at 185 °C for 4 h. The results showed that thermal modification had a decreasing effect on the pull-off adhesion strength, primarily as a result of the thermal degradation of cell-wall polymers (mostly hemicelluloses). Still, a decreased wettability as a result of condensation and plasticization of lignin was also partially influential. Based on the obtained results,thermal modification was found to have a significant influence on pull-off adhesion strength. Sepiolite addition had a decreasing effectin all treatments, though the effect was not statistically significant in all treatments. The maximum and minimum decreases due to sepiolite addition were observed in the unimpregnated control (21%) and the thermally-modified NS-impregnated (4%) specimens. Other aspects of the sepiolite addition, and further studies that cover different types of paints and coatings, should be evaluated before coming to a final firm conclusion in this regard.

Analysis of the Interior Microclimate in Art Nouveau Heritage Buildings for the Protection of Exhibits and Human Health.

Poor air quality inside museums can have a double effect; on the one hand, influencing the integrity of the exhibits and on the other hand, endangering the health of employees and visitors. Both components can be very sensitive to the influence of the internal microclimate, therefore careful monitoring of the physical parameters and pollutants is required in order to maintain them within strict limits and thus to reduce the hazards that can be induced. The current study considers the determination and analysis of 15 indicators of the internal microclimate in an Art Nouveau museum built at the beginning of the 20th century in the Municipality of Oradea, Romania. The monitoring spanned a period of seven months, between September 2021 and March 2022, targeting three rooms of the museum with different characteristics and containing exhibits with a high degree of fragility. The results show that, although there are numerous indicators that have exceeded the thresholds induced by international standards, the possible negative impact on the exhibits and/or on human health remains moderate. This is due to the fact that, most of the time, exceeding the permitted limits are small or only sporadic, the values quickly returning to the permitted limits. Thus, only 22 of the 212 days of monitoring recorded marginal conditions regarding the quality of the indoor air, the rest having acceptable and good conditions. To improve the indoor conditions, a more careful management is needed, especially regarding the values of temperature, humidity, particulate matters, natural and artificial light, volatile organic compounds (VOC) and formaldehyde (HCHO), which during the measurements recorded high values that fluctuated in a wide spectrum. The obtained results can represent the basis for the development and implementation of long-term strategies for stabilizing the microclimatic conditions in the museum in order to preserve the exhibits preventively and to ensure a clean and safe environment for people.

Effects of Nanosilver and Heat Treatment on the Pull-Off Strength of Sealer-Clear Finish in Solid Wood Species.

Pull-off strength is an important property of solid wood, influencing the quality of paints and finishes in the modern furniture industry, as well as in historical furniture and for preservation and restoration of heritage objects. The thermal modification and heat treatment of solid wood have been the most used commercial wood modification techniques over the past decades globally. The effects of heat treatment at two mild temperatures (145 and 185 °C) on the pull-off strength of three common solid wood species, i.e., common beech (Fagus sylvatica L.), black poplar (Populus nigra L.), and silver fir (Abies alba Mill.), were studied in the present research work. The specimens were coated with an unpigmented sealer-clear finish based on an organic solvent. The results demonstrated a positive correlation between the density and pull-off strength in the solid wood species. Heat treatment at 145 °C resulted in an increase in the pull-off strength in all three species, due to the formation of new bonds in the cell-wall polymers. Thermal degradation of the polymers at 185 °C weakened the positive effect of the formation of new bonds, resulting in a largely unchanged pull-off strength in comparison with the control specimens. Impregnation with a silver nano-suspension decreased the pull-off strength in beech specimens. It was concluded that density is the decisive factor in determining the pull-off strength, having a significant positive correlation (R-squared value of 0.89). Heat treatment at lower temperatures is recommended, to increase pull-off strength. Higher temperatures can have a decreasing effect on pull-off strength, due to the thermal degradation of cell-wall polymers.

Interdisciplinary Research to Advance Digital Imagery and Natural Compounds for Eco-Cleaning and for Preserving Textile Cultural Heritage.

The old fibers that make up heritage textiles displayed in museums are degraded by the aging process, environmental conditions (microclimates, particulate matter, pollutants, sunlight) and the action of microorganisms. In order to counteract these processes and keep the textile exhibits in good condition for as long as possible, both reactive and preventive interventions on them are necessary. Based on these ideas, the present study aims to test a natural and non-invasive method of cleaning historic textiles, which includes the use of a natural substance with a known antifungal effect (being traditionally used in various rural communities)-lye. The design of the study was aimed at examining a traditional women's shirt that is aged between 80-100 years, using artificial intelligence techniques for Scanning Electron Microscopy (SEM) imagery analysis and X-ray powder diffraction technique in order to achieve a complex and accurate investigation and monitoring of the object's realities. The determinations were performed both before and after washing the material with lye. SEM microscopy investigations of the ecologically washed textile specimens showed that the number of microorganism colonies, as well as the amount of dust, decreased. It was also observed that the surface cellulose fibers lost their integrity, eventually being loosened on cellulose fibers of cotton threads. This could better visualize the presence of microfibrils that connect the cellulose fibers in cotton textiles. The results obtained could be of real value both for the restorers, the textile collections of the different museums, and for the researchers in the field of cultural heritage. By applying such a methodology, cotton tests can be effectively cleaned without compromising the integrity of the material.