Controlling the surface silanol density in capillary columns and planar silicon via the self-limiting, gas-phase deposition of tris(dimethylamino)methylsilane, and quantification of surface silanols after silanization by low energy ion scattering.

Surface silanols (Si-OH) play a vital role on fused silica surfaces in chromatography. Here, we used an atmospheric-pressure, gas-phase reactor to modify the inner surface of a gas chromatography, fused silica capillary column (0.53 mm ID) with a small, reactive silane (tris(dimethylamino)methylsilane, TDMAMS). The deposition of TDMAMS on planar witness samples around the capillary was confirmed with X-ray photoelectron spectroscopy (XPS), ex situ spectroscopic ellipsometry (SE), and wetting. The number of surface silanols on unmodified and TDMAMS-modified native oxide-terminated silicon were quantified by tagging with dimethylzinc (DMZ) via atomic layer deposition (ALD) and counting the resulting zinc atoms with high sensitivity-low energy ion scattering (HS-LEIS). A bare, clean native oxide - terminated silicon wafer has 3.66 OH/nm2, which agrees with density functional theory (DFT) calculations from the literature. After TDMAMS modification of native oxide-terminated silicon, the number of surface silanols decreases by a factor of ca. 10 (to 0.31 OH/nm2). Intermediate surface testing (IST) was used to characterize the surface activities of functionalized capillaries. It suggested a significant deactivation/passivation of the capillary with some surface silanols remaining; the modified capillary shows significant deactivation compared to the native/unmodified fused silica tubing. We believe that this methodology for determining the number of residual silanols on silanized fused silica will be enabling for chromatography.

Flow-Through Atmospheric Pressure-Atomic Layer Deposition Reactor for Thin-Film Deposition in Capillary Columns.

We demonstrate the development of a new atmospheric pressure-atomic layer deposition(AP-ALD) system to coat the inner walls of capillary columns for gas chromatography (GC). Unlike traditional ALD, this reactor operates at near-atmospheric pressure and addresses the challenges of depositing thin films inside capillaries, which include long pump down times, deposition in high-aspect-ratio materials, and temperature control. We show ALD of alumina in 5 and 12 m capillaries (0.53 mm ID) via sequential half reactions of trimethylaluminum and water. Our system yields pinhole-free, uniform thin films. It includes small witness chambers for witness silicon shards before and after the capillary. An engineering flow/transport analysis of the device is provided. Our ALD alumina thin films are characterized by spectroscopic ellipsometry (SE), X-ray photoelectron spectroscopy, transmission electron microscopy (TEM), and energy-dispersive X-ray spectroscopy. Alumina film growth achieved is 1.4-1.5 Å/cycle, which is consistent with previously reported results. Film thickness measurements by SE on witness shards of silicon and by TEM at both ends of the capillary are in good agreement. A capillary column coated with alumina is used to separate different gases by GC, although the retention times of gases are essentially the same as with an untreated fused silica capillary. This successful deposition of ALD alumina in long capillaries opens the door for other possible ALD coatings, including hybrid organic-inorganic coatings, using the 450+ ALD precursors available today.

6-Phenylhexyl silane derivatized, sputtered silicon solid phase microextraction fiber for the parts-per-trillion detection of polyaromatic hydrocarbons in water and baby formula.

We report the fabrication of 6-phenylhexylsilane derivatized, sputtered silicon, solid phase microextraction fibers that show parts per trillion detection limits for polyaromatic hydrocarbons, and negligible carry over and phase bleed. Their fabrication involves sputtering silicon on silica fibers under various conditions. Six different fibers were evaluated by generating three different thicknesses of sputtered silicon at two different throw distances, which altered the morphologies of the silicon surfaces. All of the fibers were coated with similar thicknesses of 6-phenylhexylsilane (ca. 2 nm). These fibers were characterized with multiple analytical techniques. The optimum fiber configuration was then used to analyze polyaromatic hydrocarbons via direct immersion, gas chromatography mass spectrometry. Our best fiber for the extraction of low molecular weight polyaromatic hydrocarbons in water had similar performance to that of a commercial fiber. However, our fiber demonstrated ca. 3 times the extraction efficiency for higher molecular weight polyaromatic hydrocarbons. In addition, it outperformed the commercial fiber by showing better linearity, repeatability, and detection limits. A method for analyzing polyaromatic hydrocarbons in baby formula was developed, which showed very good linearity (0.5-125 ppb), repeatability (2-26%), detection limits (0.12-0.81 ppb), and recoveries (103-135%). In addition, our fiber showed much less (negligible) carry over and phase bleed than the commercially available fibers.