Poly(butylene succinate) (PBS) forms small and imperfect crystals of low melting temperature at high supercooling of the melt. Slow heating allows reorganization of the obtained semicrystalline structure with the changes of the crystallinity and of the size and perfection of crystals analyzed by differential scanning calorimetry (DSC) and temperature-resolved X-ray scattering techniques. Crystals generated at 20 °C begin to melt and reorganize at a few K higher temperature with their initial imperfection and thickness unchanged upon heating to 70-80 °C. Slow heating to temperatures higher than 70-80 °C yields a distinct exothermic peak in the DSC scan, paralleled by detection of crystals of larger size/higher perfection, beginning to melt at ≈100 °C. These observations suggest that below 70-80 °C, reorganization of the semicrystalline morphology is constrained such that only minor and local improvement of the structure of crystals are possible. The formation of both perfect and thicker crystal lamellae at higher temperature proceeds via melting of imperfect crystals followed by melt-recrystallization as for PBS solid-state thickening is impossible. The study shows the limit of low-temperature reorganization processes when not involving both complete melting of crystals and rearrangement of the lamellar-stack structure.
RESUMEN
Young's modulus of α'- and α-crystals of poly (l-lactic acid) (PLLA), more precisely, of aggregates of isotropically arranged lamellae, has been estimated based on dynamic-mechanical analysis of sets of isotropic film samples containing largely different though well-defined amounts of crystals. Evaluation of the modulus of elasticity of these film samples yielded the dependence of Young's modulus as a function of the enthalpy-based crystallinity, increasing with the crystal fraction in the assessed range, from zero to about 75% crystallinity. Extrapolation towards 100% crystallinity suggests values of Young's modulus of around 3.7 and 4.6 GPa for isotropic aggregates of α'- and α-crystals, respectively, being only slightly higher than the modulus of the unaged glassy amorphous phase of 3.0 GPa. Noting the inherent anisotropy of the crystal modulus, suggested in the literature, the average modulus determined in this work seems to be controlled by weaker interchain secondary bonding but not the modulus in chain direction. Great effort has been undertaken to minimize errors by keeping the lamellar thickness in samples of different crystallinity constant, and by providing evidence for independence of the moduli on the spherulitic superstructure.
Asunto(s)
Ácido Láctico , Módulo de Elasticidad , Elasticidad , Anisotropía , Termodinámica , Ácido Láctico/químicaRESUMEN
The polymer/solvent system poly(l-lactic acid)/ethyl butylacetylaminopropionate (PLLA/IR3535) is regarded as an insect-repellent-delivery system, serving, e.g., for fighting mosquito-borne tropical diseases. In such systems the solid polymer hosts the liquid repellent, with the latter slowly released to the environment, expelling mosquitoes. As a new approach, exceeding prior work about application of different technologies to obtain such devices, in this work, samples of the polymer/repellent system PLLA/IR3535 were prepared by 3D-printing. The experiments showed that it is possible to print 3D-parts containing up to 25 m% repellent, with an only minor loss of repellent during the printing process. For samples containing low amount of repellent, crystallization of PLLA was suppressed due to the rather fast cooling step and the low bed temperature of around 25 °C, being lower than the glass transition temperature of the homogeneous polymer/repellent strands. At higher repellent concentration, due to the lowering of the glass transition temperature to near or even below ambient temperature, the crystallinity slowly increased during storage after printing. For all samples, regardless of the initial repellent concentration, the repellent-release rate increases with temperature, and at ambient temperature the release-time constant is in the order of 10 days. The study successfully proved the applicability of the technology of extrusion-based 3D-printing for the preparation of polymer parts with a specific shape/design containing mosquito-repellent at a concentration which raises the expectation to be used as a repellent delivery-device.
Asunto(s)
Repelentes de Insectos/administración & dosificación , Repelentes de Insectos/química , Impresión Tridimensional , Enfermedades Transmitidas por Vectores/prevención & control , Animales , Insectos , Poliésteres , Polímeros/química , Propionatos/química , Clima TropicalRESUMEN
Bio-sourced and biodegradable poly(butylene succinate) (PBS) strands containing up to 40 m% mosquito-repellent N,N-diethyl-3-methylbenzamide (DEET) were obtained by extrusion, for an initial evaluation of the DEET evaporation characteristics and the possible application of such strands as biodegradable slow-release repellent-delivery devices. For DEET concentrations up to 20 m%, DEET is entrapped in the semicrystalline spherulitic superstructure of PBS. In contrast, at higher DEET concentrations, the liquid repellent, at least partially, is not fully incorporated in the PBS spherulites rather than segregates to form an own macrophase. Quantification of the release of DEET to the environment by thermogravimetric analysis at different temperatures between 60 and 100 °C allowed estimation of the evaporation rate at lower service temperatures, suggesting an extremely low release rate with a time constant of the order of magnitude of 1-2 years at 25 °C, independent of the initial concentration.
RESUMEN
The bulk enthalpy of melting of α-crystals of poly (L-lactic acid) (PLLA) is evaluated by fast scanning calorimetry (FSC), by correlating the melting enthalpy of samples of different crystallinity with the corresponding heat capacity at 90 °C, that is at a temperature higher than the glass transition temperature of the bulk amorphous phase and lower than the melting temperature. Extrapolation of this relationship for crystals formed at 140 °C towards the heat capacity of fully solid PLLA yields a value of 104.5±6 J g-1 when melting occurs at 180-200 °C. The analysis relies on a two-phase structure, that is, absence of a vitrified rigid amorphous fraction (RAF) at the temperature of analysis the solid fraction (90 °C). Formation and vitrification of an RAF are suppressed by avoiding continuation of primary crystallization and secondary crystallization during cooling the system from the crystallization temperature of 140 °C to 90 °C, making use of the high cooling capacity of FSC. Small-angle X-ray scattering (SAXS) confirmed thickening of initially grown lamellae which only is possible if these lamellae are not surrounded by a glassy RAF. Linear crystallinity values obtained by SAXS and calorimetrically determined enthalpy-based crystallinities agree close to each other.
Asunto(s)
Ácido Láctico , Calorimetría , Rastreo Diferencial de Calorimetría , Ácido Láctico/química , Dispersión del Ángulo Pequeño , Difracción de Rayos XRESUMEN
Decomposition by microorganisms of plastics in soils is almost unexplored despite the fact that the majority of plastics released into the environment end up in soils. Here, we investigate the decomposition process and microbiome of one of the most promising biobased and biodegradable plastics, poly(butylene succinate-co-adipate) (PBSA), under field soil conditions under both ambient and future predicted climates (for the time between 2070 and 2100). We show that the gravimetric and molar mass of PBSA is already largely reduced (28-33%) after 328 days under both climates. We provide novel information on the PBSA microbiome encompassing the three domains of life: Archaea, Bacteria, and Eukarya (fungi). We show that PBSA begins to decompose after the increase in relative abundances of aquatic fungi (Tetracladium spp.) and nitrogen-fixing bacteria. The PBSA microbiome is distinct from that of surrounding soils, suggesting that PBSA serves as a new ecological habitat. We conclude that the microbial decomposition process of PBSA in soil is more complex than previously thought by involving interkingdom relationships, especially between bacteria and fungi.
Asunto(s)
Ascomicetos , Plásticos Biodegradables , Microbiota , Biodegradación Ambiental , Suelo , Microbiología del SueloRESUMEN
Propylene-based random copolymers with either ethylene or 1-hexene as comonomer, produced using a metallocene catalyst, were studied regarding their crystallization behaviors, with a focus on rapid cooling. To get an impression of processing effects, fast scanning chip calorimetry (FSC) was used in addition to the characterization of the mechanical performance. When comparing the comonomer type and the relation to commercial grades based on Ziegler-Natta-type catalysts, both an interaction with the catalyst-related regio-defects and a significant difference between ethylene and 1-hexene was observed. A soluble-type nucleating agent was found to modify the behavior, but to an increasingly lesser degree at high cooling rates.
RESUMEN
The concept of specific work of flow has been applied for the analysis of critical shearing conditions for the formation of crystal nuclei in poly (l-lactic acid) (PLLA). Systematic variation in both time and rate of shearing the melt in a parallel-plate rheometer revealed that these parameters are interconvertible regarding the shear-induced formation of crystal nuclei; that is, low shear rate can be compensated for by increasing the shear time and vice versa. This result supports the view that critical shearing conditions can be expressed by a single quantity, providing additional options for tailoring polymer processing routes when enhanced nuclei formation is desired/unwanted. Analysis of PLLA of different mass-average molar masses of 70, 90, 120, and 576 kDa confirmed improved shear-induced crystal nucleation for materials of higher molar mass, with critical specific works of flow, above which shear-induced nuclei formation occurs, of 550, 60, 25, and 5 kPa, respectively.
RESUMEN
The different thermal stabilities of shear-induced pointlike and shishlike crystallization precursors of polyamide 11, generated in a parallel-plate rheometer and coexisting in the same sample, were quantified by hot-stage microscopy, by performing self-seed crystallization experiments. Crystals formed at low supercooling of the melt from these different types of precursors melt at about the same temperature. Annealing of the melt at different temperatures for a predefined time revealed dissolution/disordering of these precursors at 10-15 K higher temperature, near the equilibrium melting point. Despite their similar thermal stabilities, pointlike and shishlike crystallization precursors exhibit distinctly different nucleation efficacies. Under identical crystallization conditions, shishlike precursors cause faster crystallization than pointlike crystal nuclei. The faster crystallization of the shishlike nuclei can be explained, for example, by (a) the larger size of the shishlike precursors, providing numerous nucleation sites; (b) the more perfect chain conformation at the shish surface, which serves as a substrate for crystallization; or perhaps (c) the higher local orientation of the surrounding melt compared with molecular segments near pointlike nuclei, reducing the activation energy for crystallization.
RESUMEN
The crystallization kinetics of metallocene-catalyzed heterophasic isotactic polypropylene composed of a matrix of isotactic polypropylene (iPP) and rubbery particles made of random ethylene-propylene copolymers (EPC), often denoted as heterophasic iPP copolymers, was analyzed as a function of the cooling rate and supercooling in nonisothermal and isothermal crystallization experiments, respectively. Fast scanning chip calorimetry (FSC) allowed assessing crystallization at processing-relevant conditions, and variation of the content (0-39 wt %) and composition (0-35 wt % propylene counits) of the EPC particles revealed qualitatively new insight about mechanisms of heterogeneous crystal nucleation. For neat iPP homopolymer, the characteristic bimodal temperature dependence of the crystallization rate due to predominance of heterogeneous and homogeneous crystal nucleation at high and low temperatures, respectively, is reconfirmed. At high temperatures, in heterophasic iPP, the here studied ethylene-(C2)-rich EPC particles accelerate crystallization of the iPP-matrix, with the acceleration or nucleation efficacy correlating with the EPC-particle content. The crystallization time reduces by more than half in presence of 39 wt % EPC particles. An additional nucleating effect of the EPC particles on iPP-matrix crystallization is detected after their crystallization, suggesting that liquid/rubbery particles are less effective than solid/semicrystalline particles in affecting crystallization of the surrounding iPP-matrix. At low temperature, homogeneous crystal nucleation in the iPP-matrix outpaces all heterogeneous nucleation effects, and the matrix-crystallization rate is independent of the sample composition. The obtained results lead to the conclusion that the crystallization kinetics of iPP can be affected significantly by the content and composition of EPC particles, even towards superfast crystallizing iPP grades.
RESUMEN
Despite the important role of wood-inhabiting fungi (WIF) in deadwood decomposition, our knowledge of the factors shaping the dynamics of their species richness and community composition is scarce. This is due to limitations regarding the resolution of classical methods used for characterizing WIF communities and to a lack of well-replicated long-term experiments with sufficient numbers of tree species. Here, we used a large scale experiment with logs of 11 tree species at an early stage of decomposition, distributed across three regions of Germany, to identify the factors shaping WIF community composition and Operational Taxonomic Unit (OTU) richness using next generation sequencing. We found that tree species identity was the most significant factor, corresponding to (P < 0.001) and explaining 10% (representing 48% of the explainable variance) of the overall WIF community composition. The next important group of variables were wood-physicochemical properties, of which wood pH was the only factor that consistently corresponded to WIF community composition. For overall WIF richness patterns, we found that approximately 20% of the total variance was explained by wood N content, location, tree species identity and wood density. It is noteworthy that the importance of determinants of WIF community composition and richness appeared to depend greatly on tree species group (broadleaved vs. coniferous) and it differed between the fungal phyla Ascomycota and Basidiomycota.
RESUMEN
Forest management practices (FMPs) significantly influence important ecological processes and services in Central European forests, such as leaf litter decomposition and nutrient cycling. Changes in leaf litter diversity, and thus, its quality as well as microbial community structure and function induced by different FMPs were hypothesized to be the main drivers causing shifts in decomposition rates and nutrient release in managed forests. In a litterbag experiment lasting 473 days, we aimed to investigate the effects of FMPs (even-aged timber management, selective logging and unmanaged) on bacterial and fungal communities involved in leaf litter degradation over time. Our results showed that microbial communities in leaf litter were strongly influenced by both FMPs and sampling date. The results from nonmetric multidimensional scaling (NMDS) ordination revealed distinct patterns of bacterial and fungal successions over time in leaf litter. We demonstrated that FMPs and sampling dates can influence a range of factors, including leaf litter quality, microbial macronutrients, and pH, which significantly correlate with microbial community successions.