RESUMEN
A styrene-butadiene-styrene co-polymer matrix nanocomposite filled with graphene nanoplatelets was studied to prepare chemiresistive volatile organic compounds (VOCs) room temperature sensors with considerable response and selectivity. Nanofiller concentration was estimated from the electrical conductivity percolation behaviour of the nanocomposite. Fabricated sensors provided selective relative responses to representative VOCs differing by orders of magnitude. Maximum observed average relative responses upon exposure to saturated vapours of the tested VOCs were ca. 23% for ethanol, 1600% for acetone, and the giant values were 9 × 106% for n-heptane and 10 × 106% for toluene. The insensitivity of the sensor to the direct saturated water vapour exposure was verified. Although high humidity decreases the sensor's response, it paradoxically enhances the resolution between hydrocarbons and polar organics. The non-trivial sensing mechanism is explained using the Hansen solubility parameters (HSP), enabling a rational design of new sensors; thus, the HSP-based class of sensors is outlined.
RESUMEN
Ti-based anode materials are considered to be an alternative to graphite anodes to accomplish high-rate application requirements. Ti2Nb10O29 (TNO15) has attracted much attention due to its high lithium storage capacity through the utilization of multiple redox couples and a suitable operating voltage window of 1.0 to 2.0 V vs Li/Li+. However, poor intrinsic electronic conductivity has limited the futuristic applicability of this material to the battery anode. In this work, we report the modification of TNO15 by introducing oxygen vacancies and using few-layered carbon and copper coatings on the surface to improve its Li+ storage property. With the support of the galvanostatic intermittent titration technique (GITT), we found that the diffusion coefficient of carbon/copper coated TNO15 is 2 orders of magnitude higher than that of the uncoated sample. Here, highly conductive copper metal on the surface of the carbon-coated oxygen-vacancy-incorporated TNO15 increases the overall electronic and ionic conductivity. The prepared TNO15-800-C-Cu-700 half-cell shows a significant rate capability of 92% when there is a 10-fold increase in the current density. In addition, the interconnected TNO15 nanoparticles create a porous microsphere structure, which enables better Li-ion transportation during charge/discharge process, and experiences an enhancement after the carbon and copper coating on the surface of the primary TNO15 nanocrystallites.
RESUMEN
Hybrid organic/inorganic conducting and magnetic composites of core-shell type have been prepared by in-situ coating of nickel microparticles with polypyrrole. Three series of syntheses have been made. In the first, pyrrole was oxidised with ammonium peroxydisulfate in water in the presence of various amounts of nickel and the composites contained up to 83 wt% of this metal. The second series used 0.1 M sulfuric acid as a reaction medium. Finally, the composites with polypyrrole nanotubes were prepared in water in the presence of structure-guiding methyl orange dye. The nanotubes have always been accompanied by the globular morphology. FTIR and Raman spectroscopies confirmed the formation of polypyrrole. The resistivity of composite powders of the order of tens to hundreds Ω cm was monitored as a function of pressure up to 10 MPa. The resistivity of composites slightly increased with increasing content of nickel. This apparent paradox is explained by the coating of nickel particles with polypyrrole, which prevents their contact and subsequent generation of metallic conducting pathways. Electrical properties were practically independent of the way of composite preparation or nickel content and were controlled by the polypyrrole phase. On the contrary, magnetic properties were determined exclusively by nickel content. The composites were used as a solid phase to prepare a magnetorheological fluid. The test showed better performance when compared with a different nickel system reported earlier.
RESUMEN
The development of flexible, lightweight, and thin high-performance electromagnetic interference shielding materials is urgently needed for the protection of humans, the environment, and electronic devices against electromagnetic radiation. To achieve this, the spinel ferrite nanoparticles CoFe2O4 (CZ1), Co0.67Zn0.33Fe2O4 (CZ2), and Co0.33Zn0.67Fe2O4 (CZ3) were prepared by the sonochemical synthesis method. Further, these prepared spinel ferrite nanoparticles and reduced graphene oxide (rGO) were embedded in a thermoplastic polyurethane (TPU) matrix. The maximum electromagnetic interference (EMI) total shielding effectiveness (SET) values in the frequency range 8.2-12.4 GHz of these nanocomposites with a thickness of only 0.8 mm were 48.3, 61.8, and 67.8 dB for CZ1-rGO-TPU, CZ2-rGO-TPU, and CZ3-rGO-TPU, respectively. The high-performance electromagnetic interference shielding characteristics of the CZ3-rGO-TPU nanocomposite stem from dipole and interfacial polarization, conduction loss, multiple scattering, eddy current effect, natural resonance, high attenuation constant, and impedance matching. The optimized CZ3-rGO-TPU nanocomposite can be a potential candidate as a lightweight, flexible, thin, and high-performance electromagnetic interference shielding material.
RESUMEN
In this work, nickel ferrite (NiFe2O4) nanoparticles were synthesized by dextrin from corn-mediated sol-gel combustion method and were annealed at 600, 800, and 1000 °C. The structural and physical characteristics of prepared nanoparticles were studied in detail. The average crystallite size was 20.6, 34.5, and 68.6 nm for NiFe2O4 nanoparticles annealed at 600 °C (NFD@600), 800 °C (NFD@800), and 1000 °C (NFD@1000), respectively. The electromagnetic interference shielding performance of prepared nanocomposites of NiFe2O4 nanoparticles (NFD@600 or NFD@800 or NFD@1000) in polypropylene (PP) matrix engineered with reduced graphene oxide (rGO) have been investigated; the results indicated that the prepared nanocomposites consisted of smaller-sized nickel ferrite nanoparticles exhibited excellent electromagnetic interference (EMI) shielding characteristics. The total EMI shielding effectiveness (SET) for the prepared nanocomposites have been noticed to be 45.56, 36.43, and 35.71 dB for NFD@600-rGO-PP, NFD@800-rGO-PP, and NFD@1000-rGO-PP nanocomposites, respectively, at the thickness of 2 mm in microwave X-band range (8.2-12.4 GHz). The evaluated values of specific EMI shielding effectiveness (SSE) were 38.81, 32.79, and 31.73 dB·cm3/g, and the absolute EMI shielding effectiveness (SSE/t) values were 388.1, 327.9, and 317.3 dB·cm2/g for NFD@600-rGO-PP, NFD@800-rGO-PP, and NFD@1000-rGO-PP, respectively. The prepared lightweight and flexible sheets can be considered useful nanocomposites against electromagnetic radiation pollution.