Towards Acid-Tolerated Ethanol Dehydration: Chitosan-Based Mixed Matrix Membranes Containing Cyano-Bridged Coordination Polymer Nanoparticles.

Prussian blue (PB) nanoparticles, one of many cyano-bridged coordination polymers, are successfully incorporated into chitosan (CS) polymer to prepare PB/CS mixed matrix membranes (MMMs). The PB nanoparticles are uniformly distributed in the MMMs without the collapse of the original PB structure. As-prepared PB/CS MMMs are used for ethanol dehydration at 25 °C in the pervaporation process. The effect of loading PB in CS matrix on pervaporation performance is carefully investigated. The PB/CS membrane with 30 wt% PB loading shows the best performance with a permeate flux of 614 g. m-2 . h-1 and a separation factor of 1472. The pervaporation using our PB/CS membranes exhibits outstanding performance in comparison with the previously reported CS-based membranes and MMMs. Furthermore, the addition of PB allows PB/CS MMMs to be tolerant of acidic environment. The present work demonstrates good pervaporation performance of PB/CS MMMs for the separation of an ethanol/water (90:10 in wt%) solution. Our new system provides an opportunity for dehydration of bioethanol in the future.

Synthesis of hierarchical micro/mesoporous structures via solid-aqueous interface growth: zeolitic imidazolate framework-8 on siliceous mesocellular foams for enhanced pervaporation of water/ethanol mixtures.

A new hierarchical micro/mesoporous composite is synthesized via direct growth of microporous zeolitic imidazolate framework-8 (ZIF-8) on siliceous mesocellular foams (MCF). Depending on different synthetic conditions, ZIF-8 with two different particle sizes, i.e., ZIF-8 microparticles and ZIF-8 nanoparticles, were successfully formed on the external surface of amine-functionalized MCF (denoted as microZIF-8@MCF and nanoZIF-8@MCF, respectively). The synthesized hierarchical micro/mesoporous ZIF-8@MCF structures were characterized with several spectroscopic techniques including X-ray diffraction (XRD), solid-state NMR, and FT-IR and electron microscopic techniques (scanning electron microscope, SEM, and transmission electron microscopy, TEM). In addition, the pervaporation measurements of the liquid water/ethanol mixture show that nanoZIF-8@MCF/PVA (poly(vinyl alcohol) mixed-matrix membrane exhibits enhanced performance both on the permeability and separation factor. Compared to conventional routes for chemical etching, this study demonstrates a promising and simple strategy for synthesizing novel hierarchical porous composites exhibiting both advantages of mesoporous materials and microporous materials, which is expected to be useful for gas adsorption, separation, and catalysis.