High-Performance Washable PM2.5 Filter Fabricated with Laser-Induced Graphene.

This study demonstrates a novel application of laser-induced graphene (LIG) as a reusable conductive particulate matter (PM) filter. Four types of LIG-based filters were fabricated based on the laser-induced pyrolysis of thin polyimide (PI) sheets, each pyrolyzed on either a single side or both sides, with or without densification. The LIG filters exhibited a high removal efficiency while maintaining minimal pressure drop compared to a commercial fiberglass filter. The densified LIG (dLIG) filters displayed a higher PM2.5 removal efficiency (>99.86%) than regular LIG filters. The dLIG filters also exhibited excellent durability when tested for washability by ultrasonication in tap water. After being cleaned and left to dry, the structures of the dLIG filters were well-maintained; their filtration efficiencies were also well-maintained (less than a 7% change in PM2.5 removal efficiency), and their resistances only marginally increased (less than a 7% increase after five uses). These results demonstrate the robustness and reusability of the dLIG filters and the accessibility of their cleaning (not requiring aggressive cleaning agents). These promising features will enable the application of LIG in economical, scalable, and high-performance air cleaning.

Laser Pyrolysis of Imprinted Furan Pattern for the Precise Fabrication of Microsupercapacitor Electrodes.

The design or dimension of micro-supercapacitor electrodes is an important factor that determines their performance. In this study, a microsupercapacitor was precisely fabricated on a silicon substrate by irradiating an imprinted furan micropattern with a CO2 laser beam under ambient conditions. Since furan is a carbon-abundant polymer, electrically conductive and porous carbon structures were produced by laser-induced pyrolysis. While the pyrolysis of a furan film in a general electric furnace resulted in severe cracks and delamination, the laser pyrolysis method proposed herein yielded porous carbon films without cracks or delamination. Moreover, as the imprinting process already designated the furan area for laser pyrolysis, high-precision patterning was achieved in the subsequent laser pyrolysis step. This two-step process exploited the superior resolution of imprinting for the fabrication of a laser-pyrolyzed carbon micropattern. As a result, the technical limitations of conventional laser direct writing could be overcome. The laser-pyrolyzed carbon structure was employed for microsupercapacitor electrodes. The microsupercapacitor showed a specific capacitance of 0.92 mF/cm2 at 1 mA/cm2 with a PVA-H2SO4 gel electrolyte, and retained an up to 88% capacitance after 10,000 charging/discharging cycles.