RESUMEN
A method has been developed for direct non-destructive energy dispersive X-ray fluorescence (EDXRF) determination of sulfur in solid uranium ores and intermediates, obtained from the alkaline recovery process for uranium from its ores. The method involves thorough grinding of a few mg of solid powder samples to fine particle size and mixing the fine powder thus obtained with a few drops of 10% collodion solution in amyl acetate to make a paste. A very small amount of this paste was transferred with the help of the pestle tip, spread uniformly in the form of thin slurry on Mylar films, and dried to make very thin sample specimens on thin Mylar film supports. These specimens were presented for EDXRF measurements. A calibration plot was made by plotting the intensity ratios of S Kα and Rayliegh scattered peak of the excitation source (Ge Kα) against sulphur percent in the certified reference materials (CRMs). It was found that the precision obtained using this methodology was within 5% (±1σ) and the deviation of the EDXRF analytical results from the expected values of CRM was within 7%. The developed method was successfully applied for the determination of sulfur in the samples obtained from the different stages of the uranium ore processing using alkaline based leaching method.
RESUMEN
The development of a direct non-destructive synchrotron-radiation-based total reflection X-ray fluorescence (TXRF) analytical methodology for elemental determinations in zirconium alloy samples is reported for the first time. Discs, of diameter 30â mm and about 1.6â mm thickness, of the zirconium alloys Zr-2.5%Nb and Zircalloy-4 were cut from plates of these alloys and mirror polished. These specimens were presented for TXRF measurements directly after polishing and cleaning. The TXRF measurements were made at the XRF beamline at Elettra synchrotron light source, Trieste, Italy, at two different excitation energies, 1.9â keV and 14â keV, for the determinations of low- and high-Z elements, respectively. The developed analytical methodology involves two complementary quantification schemes, i.e. using either the fundamental parameter method or relative sensitivity based method, allowing quantification of fifteen minor and trace elements with respect to Zr with very good precision and accuracy. In order to countercheck the TXRF analytical results, some samples were analyzed using the DC arc carrier distillation atomic emission spectrometry technique also, which shows an excellent agreement with the results of the TXRF-based methodology developed in this work. The present work resulted in a non-destructive TXRF elemental characterization methodology of metal and alloy samples avoiding the cumbersome dissolution and matrix separation which are normally required in other techniques and traditional methods of TXRF determination. In addition, the production of analytical waste could also be avoided to a large extent. Although the work was carried out for specific applications in the nuclear industry, it is equally suitable for other such samples in different industrial applications.
RESUMEN
MgO particles of few micron size are synthesized through a sol-gel method at different annealing temperatures such as 600 °C (MgO-600), 800 °C (MgO-800) and 1000 °C (MgO-1000). EDX and ICP-AES studies confirmed a near total purity of the sample with respect to paramagnetic metal ion impurities. Magnetic measurements showed a low temperature weak ferromagnetic ordering with a TC (Curie temperature) around 65 K (±5 K). Unexpectedly, the saturation magnetization (Ms) was found to be increased with increasing annealing temperature during synthesis. It was observed that with J = 1 or 3/2 or S = 1 or 3/2, the experimental points are fitted well with the Brillouin function of weak ferromagnetic ordering. A positron annihilation lifetime measurement study indicated the presence of a divacancy (2VMg + 2VO) cluster in the case of the low temperature annealed compound, which underwent dissociations into isolated monovacancies of Mg and O at higher annealing temperatures. An EPR study showed that both singly charged Mg vacancies and oxygen vacancies are responsible for ferromagnetic ordering. It also showed that at lower annealing temperatures the contribution from was very low while at higher annealing temperatures, it increased significantly. A PL study showed that most of the F+ centers were present in their dimer form, i.e. as centers. DFT calculation implied that this dimer form has a higher magnetic moment than the monomer. After a careful consideration of all these observations, which have been reported for the first time, this thermally tunable unusual magnetism phenomenon was attributed to a transformation mechanism of one kind of cluster vacancy to another.
RESUMEN
La doped Bi2UO6 solid solutions of the general formula Bi2-2xLa2xUO6 (x = 0-0.05) were prepared by the solid state reaction of Bi2O3, La(OH)3 and U3O8 in a stoichiometric ratio. These solid solutions were characterized by X-ray diffraction, Extended X-ray Absorption Fine Structure (EXAFS) and X-ray Absorption Near Edge Spectroscopy (XANES) studies. It was found that La goes to the Bi sites of the Bi2UO6 lattice during the formation of these solid solutions. For further confirmation, a photoluminescence (PL) study on an iso-structural Bi1.96Eu0.04UO6 was performed, and this supports the above observation. The solid solutions were also probed by EPR studies. The PL and EPR studies suggest that there are doping induced oxygen vacancies in these solid solutions.