RESUMEN
The fretting wear behaviors of silicone rubber under dry friction and different lubrication conditions are studied experimentally. Water, engine oil, dimethyl silicone oil (DSO), and dimethyl silicone oil doped with graphene oxide (DSO/GO) are selected as lubricants. Under the liquid lubrication conditions, the silicone rubber samples are always immersed in the same volume of lubricant. The contact model of a 440C steel ball and silicone rubber sample is the sphere-on-flat contact. The reciprocating fretting wear experiments are carried out using the reciprocating friction wear tester. A scanning electron microscope and three-dimensional white-light interference profilometer are used to detect the surface wear morphology and obtain the wear volume, respectively. The influences of normal force, lubrication condition, and displacement amplitude on fretting wear behavior are discussed. The fretting wear performances of silicone rubber under different fretting states and lubrication conditions are compared. The results show that for a small normal force, silicone rubber has the best wear resistance under DSO/GO lubrication. While for a large normal force, silicone rubber has the best wear resistance under engine oil lubrication.
RESUMEN
Rubbers are widely used in various fields as the important sealing materials, such as window seal, door seal, valve, pump seal, etc. The fretting wear behavior of rubbers has an important effect on their sealing performance. This paper presents an experimental study on the fretting wear behavior of rubbers against the steel ball under air conditions (room temperature at 20 ± 2 °C and humidity at 40%). Three kinds of rubbers, including EPDM (ethylene propylene diene monomer), FPM (fluororubber), and NBR (nitrile-butadiene rubber), are considered in experiments. The sphere-on-flat contact pattern is used as the contact model. The influences of the displacement amplitude, normal force, frequency, and rubber hardness on the fretting wear behavior are discussed in detail. White light profiler and scanning electron microscope (SEM) are used to analyze the wear mechanism of the rubber surface. The fretting wear performances of three rubbers are compared by considering the effect of the displacement amplitude, normal force, frequency, and rubber hardness. The results show that NBR has the most stable friction coefficient and the best wear resistance among the three rubbers.
RESUMEN
This paper discusses an in-depth experimental study on the fretting wear behavior of PVDF (polyvinylidene fluoride) piezoelectric thin film against a Si3N4 ceramic sphere under air conditions. A fretting wear device with a ball-on-plate contact configuration was applied. The changes of displacement amplitude, normal force, and applied voltage were taken into account. The friction logs were used to determine the contact state of the PVDF thin film during the fretting test. The 3D topography instrument and scanning electron microscope (SEM) were used to measure the details of the surface morphology and wear volume. The test results of PVDF thin films under different normal force, displacement amplitude, and applied voltage are summarized through the collection and analysis of experimental data. It is shown that the creep and plastic deformation lead to obvious winkles at the contact surface, which may decrease the specific wear rate of PVDF thin films.