Metal Organic Frameworks: Current State and Analysis of Their Use as Modifiers of the Vulcanization Process and Properties of Rubber.

The interest in and application of metal organic frameworks (MOF) is increasing every year. These substances are widely used in many places, including the separation and storage of gases and energy, catalysis, electrochemistry, optoelectronics, and medicine. Their use in polymer technology is also increasing, focusing mainly on the synthesis of MOF-polymer hybrid compounds. Due to the presence of metal ions in their structure, they can also serve as a component of the crosslinking system used for curing elastomers. This article presents the possibility of using zeolitic imidazolate framework ZIF-8 or MOF-5 as activators for sulfur vulcanization of styrene-butadiene rubber (SBR), replacing zinc oxide in conventional (CV) or effective (EF) curing systems to different extents. Their participation in the curing process and influence on the crosslinking density and structure, as well as the mechanical and thermal properties of the rubber vulcanizates, were examined.

Evaluation of the Selected Mechanical and Aesthetic Properties of Experimental Resin Dental Composites Containing 1-phenyl-1,2 Propanedione or Phenylbis(2,4,6-trimethylbenzoyl)-phosphine Oxide as a Photoinitiator.

The goal of this study was to compare the mechanical properties of experimental resin dental composites containing a conventional photoinitiating system (camphorquinone CQ and 2-(dimethylami-no)ethyl methacrylate (DMAEMA)) to a photoinitiator system containing 1-phenyl-1,2 propanedione (PPD) with 2-(dimethylami-no)ethyl methacrylate) or acting alone phenylbis(2,4,6-trimethylbenzoyl)-phosphine oxide (BAPO). The manually produced composites consisted of an organic matrix: bis-GMA (60 wt. %), TEGDMA (40 wt. %), and silanized silica filler (45 wt. %). The composites contained 0.4/0.8 wt. %, 0.8/1.6 wt. %, and 1/2 wt. % of PPD/DMAEMA and another group included 0.25, 0.5, or 1 wt. % of BAPO. Vickers hardness, microhardness (in the nanoindentation test), diametral tensile strength, and flexural strength were assessed, and CIE L* a* b* colorimetric analysis was conducted for each composite produced. The highest average Vickers hardness values were obtained for the composite containing 1 wt. % BAPO (43.73 ± 3.52 HV). There was no statistical difference in the results of diametral tensile strength for the experimental composites tested. The results of 3-point bending tests were the highest for composites containing CQ (77.3 ± 8.84 MPa). Despite the higher hardness of experimental composites including PPD or BAPO, compared with composites with CQ, the overall results indicate that the composite with CQ still represents a better solution when used as a photoinitiator system. Moreover, the composites containing PPD and DMAEMA are not promising in terms of color or mechanical properties, especially as they require significantly longer irradiation times.

Fly Ash from Lignite Combustion as a Filler for Rubber Mixes-Part II: Chemical Valorisation of Fly Ash.

Fly ash (FA) fractions with a particle size of 63 µm < FA < 250 µm obtained by sieve fractionation were used as a partial carbon black (CB) replacement in a rubber mixture based on styrene-butadiene rubber (SBR). In order to improve the interactions at the interface between rubber and fractionated ash, at the stage of preparing the rubber mixtures, two different vinyl silanes were added to the system: Vinyltrimethoxysilane (U-611) or Vinyl-tris (2-methoxy-ethoxy) silane (LUVOMAXX VTMOEO DL50), silane with epoxy groups: 3-(glycidoxypropyl)trimethoxysilane (U-50) or sulfur functionalized silanes: containing sulfide bridges: Bis(triethoxysilylpropyl)polysulfide silane (Si-266) or mercapto groups: Mercaptopropyltrimethoxysilane (Dynaslan MTMO). The conducted research confirmed the effectiveness of silanization with selected functional silanes, from the point of view of improving the processing and operational properties of vulcanizates, in which CB is partially replaced with the finest fractions of fly ash. The silanization generally increased the interaction at the rubber−ash interface, while improving the degree of filler dispersion in the rubber mixture. The results of TGA and FTIR analyses confirmed the presence of silanes chemically bonded to the surface of fly ash particles. SEM tests and determination of the bound rubber (BdR) content show that the introduction of the silanes to the mixture increases the degree of ash dispersion (DI) and the Payne effect, which is the greatest when mercaptosilane was used for modification. The highest increase in torque, which was recorded in the case of rubber mixtures containing sulfur silanes and silane with epoxy groups, may be due to their participation in the vulcanization process, which is confirmed by the results of vulcametric studies. The lowest values of mechanical strength, elongation at break, and the highest hardness of vulcanizates obtained in this case may be the result of the over-crosslinking of the rubber. The addition of sulfur-containing silanes significantly slowed down the vulcanization process, which is particularly visible (up to three times extension of the t90 parameter, compared to mixtures without silane) in the case of Si-266. The addition of silanes, except for Si-266 (with a polysulfide fragment), generally improved the abrasion resistance of vulcanizates. The Dynaslan MTMO silane (with mercapto groups) performs best in this respect. Proper selection of silane for the finest fraction of fly ash in the rubber mixtures tested allows for an increase in the mechanical strength of their vulcanizates from 9.1 to 17 MPa, elongation at break from 290 to 500%, hardness from 68 to 74 °ShA, and reduction in abrasion from 171 to 147 mm3.

SBR Vulcanizates Filled with Modified Ground Tire Rubber.

Ground tire rubber (GTR) is used to decrease the cost of vulcanizates. However, insufficient interactions between GTR particles and rubber matrices make mechanical properties of vulcanizates containing GTR deteriorate. This paper compares original methods of GTR modification. The effects of surface activation of GTR by sulfuric acid (A), its modification by (3-mercaptopropyl)trimethoxy silane (M), or the hybrid treatment-combining both approaches (H), were analyzed in terms of surface energy, specific surface area and morphology of GTR particles. Vulcanizates containing virgin GTR were compared to the rubber filled with the modified GTR particles keeping the same amount of CB in the rubber mix, according to their crosslink density, mechanical and tribological properties. Contrary to the virgin GTR, the addition of modified GTR increases the stiffness of the vulcanizates. The highest changes have been observed for the samples filled with ca. 12 phr of the GTR modified with silane and ca. 25 phr of the GTR subjected to the hybrid treatment, representing the highest crosslink density of rubber vulcanizates filled with GTR. Furthermore, the addition of modified GTR, especially in the case of the samples where 10 phr of rubber was replaced, results in the significant lowering of friction but higher abrasive wear.

Influence of n-ZnO Morphology on Sulfur Crosslinking and Properties of Styrene-Butadiene Rubber Vulcanizates.

This paper examines the influence of the morphology of zinc oxide nanoparticles (n-ZnO) on the activation energy, vulcanization parameters, crosslink density, crosslink structure, and mechanical properties in the extension of the sulfur vulcanizates of styrene-butadiene rubber (SBR). Scanning electron microscopy was used to determine the particle size distribution and morphology, whereas the specific surface area (SSA) and squalene wettability of the n-ZnO nanoparticles were adequately evaluated using the Brunauer-Emmet-Teller (BET) equation and tensiometry. The n-ZnO were then added to the SBR in conventional (CV) or efficient (EV) vulcanization systems. The vulcametric curves were plotted, from which the cure rate index (CRI) rate of the vulcanization and the activation energy were calculated. The influence on the mechanical properties of the SBR vulcanizates was stronger in the case of the EV curing system than when the CV curing system was used. Of the vulcanizates produced in the EV curing system, the best performance was detected for n-ZnO particles with a hybrid morphology (flat-ended rod-like particles on a "cauliflower" base) and high SSA. Vulcanizates produced using the CV curing system showed slightly better mechanical properties after the addition of nanoparticles with a "cauliflower" morphology than when the rod-like type were used, irrespective of their SSA. In general, nanoparticles with a rod-like structure reduced the activation energy and increased the speed of vulcanization, whereas the cauliflower type slowed the rate of the process and the vulcanizates required a higher activation energy, especially when using the EV system. The crosslink structures were also more clearly modified, as manifested by a reduction in the polysulfidic crosslink content, especially when n-ZnO activators with a rod-like morphology were applied.