Microporous calcium phosphate ceramics as tissue engineering scaffolds for the repair of osteochondral defects: Histological results.

Treatment of defects in joint cartilage aims to re-establish normal joint function. In vitro experiments have shown that the application of synthetic scaffolds is a promising alternative to existing therapeutic options. A sheep study was conducted to test the suitability of microporous pure ß-tricalcium phosphate (TCP) ceramics as tissue engineering scaffolds for the repair of osteochondral defects. Cylindrical plugs of microporous ß-TCP (diameter: 7mm; length: 25mm; porosity: 43.5±2.4%; pore diameter: ~5µm) with interconnecting pores were used. Scaffolds were seeded with autologous chondrocytes in vitro and cultured for 4weeks. A drill hole (diameter 7mm) was placed in both medial femoral condyles of sheep. For the left knee the defect was filled with a TCP plug and for the right knee the defect was left empty. After 6, 12, 26 and 52weeks, seven animals from each group were killed and studied. The samples were examined employing histological, histomorphometric and immunohistological methods as well as various imaging techniques (X-ray, microcomputer tomography and scanning electron microscopy). After explantation the cartilage defects were first assessed macroscopically. There were no signs of infection or inflammation. Histological grading scales were used for assessment of bony integration and cartilage repair. An increasing degradation (81% after 52weeks) of the ceramic with concomitant bone formation was observed. The original structure of cancellous bone was almost completely restored. After 26 and 52weeks, collagen II-positive hyaline cartilage was detected in several samples. New subchondral bone had formed. The formation of cartilage began at the outer edge and proceeded to the middle. According to the O'Driscoll score, values corresponding to healthy cartilage were not reached after 1year. Integration of the newly formed cartilage tissue into the surrounding native cartilage was found. The formation of biomechanical stable cartilage began at the edge and progressed towards the centre of the defect. After 1year this process was still not completed. Microporous ß-TCP scaffolds seeded with chondrocytes are suitable for the treatment of osteochondral defects.

Microporous calcium phosphate ceramics as tissue engineering scaffolds for the repair of osteochondral defects: biomechanical results.

This work investigated the suitability of microporous ß-tricalcium phosphate (TCP) scaffolds pre-seeded with autologous chondrocytes for treatment of osteochondral defects in a large animal model. Microporous ß-TCP cylinders (Ø 7 mm; length 25 mm) were seeded with autologous chondrocytes and cultured for 4 weeks in vitro. Only the upper end of the cylinder was seeded with chondrocytes. Chondrocytes formed a multilayer on the top. The implants were then implanted in defects (diameter 7 mm) created in the left medial femoral condyle of ovine knees. The implants were covered with synovial membrane from the superior recess of the same joint. For the right knees, an empty defect with the same dimensions served as control. Twenty-eight sheep were split into 6-, 12-, 26- and 52 week groups of seven animals. Indentation tests with a spherical (Ø 3mm) indenter were used to determine the biomechanical properties of regenerated tissue. A software-based limit switch was implemented to ensure a maximal penetration depth of 200 µm and maximal load of 1.5 N. The achieved load, the absorbed energy and the contact stiffness were measured. Newly formed cartilage was assessed with the International Cartilage Repair Society Visual Assessment Scale (ICRS score) and histomorphometric analysis. Results were analysed statistically using the t-test, Mann-Whitney U-test and Wilcoxon test. Statistical significance was set at p<0.05. After 6 weeks of implantation, the transplanted area tolerated an indentation load of 0.05±0.20 N. This value increased to 0.10±0.06 N after 12 weeks, to 0.27±0.18 N after 26 weeks, and 0.27±0.11 N after 52 weeks. The increase in the tolerated load was highly significant (p<0.0001), but the final value was not significantly different from that of intact cartilage (0.30±0.12 N). Similarly, the increase in contact stiffness from 0.87±0.29 N mm-(1) after 6 weeks to 3.14±0.86 N mm(-1) after 52 weeks was highly significant (p<0.0001). The absorbed energy increased significantly (p=0.02) from 0.74×10(-6)±0.38×10(-6) Nm after 6 weeks to 2.83×10(-6)±1.35×10(-6) Nm after 52 weeks. At 52 weeks, the International Cartilage Repair Society (ICRS) scores for the central area of the transplanted area and untreated defects were comparable. In contrast, the score for the area from the edge to the centre of the transplanted area was significantly higher (p=0.001) than the score for the unfilled defects. A biomechanically stable cartilage was built outside the centre of defect. After 52 weeks, all but one empty control defect were covered by bone and a very thin layer of cartilage (ICRS 7 points). The empty hole could still be demonstrated beneath the bone. The histomorphometric evaluation revealed that 81.0±10.6% of TCP was resorbed after 52 weeks. The increase in TCP resorption and replacement by spongy bone during the observation period was highly significant (p<0.0001). In this sheep trial, the mechanical properties of microporous TCP scaffolds seeded with transplanted autologous chondrocytes were similar to those of natural cartilage after 52 weeks of implantation. However, the central area of the implants had a lower ICRS score than healthy cartilage. Microporous TCP was almost fully resorbed at 52 weeks and replaced by bone.