RESUMEN
The electrochemical nitrogen and nitrate reduction reactions (E-NRR and E-NO3RR) promise to provide decentralized and fossil-fuel-free ammonia synthesis, and as a result, E-NRR and E-NO3RR research has surged in recent years. Membrane NH3/NH4+ crossover during E-NRR and E-NO3RR decreases Faradaic efficiency and thus the overall yield. During catalyst evaluation, such unaccounted-for crossover results in measurement error. Herein, several commercially available membranes were screened and evaluated for use in ammonia-generating electrolyzers. NH3/NH4+ crossover of the commonly used cation-exchange membrane (CEM) Nafion 212 was measured in an H-cell architecture and found to be significant. Interestingly, some anion exchange membranes (AEMs) show negligible NH4+ crossover, addressing the problem of measurement error due to NH4+ crossover. Further investigation of select membranes in a zero-gap gas diffusion electrode (GDE)-cell determines that most membranes show significant NH3 crossover when the cell is in an open circuit. However, uptake and crossover of NH3 are mitigated when -1.6 V is applied across the GDE-cell. The results of this study present AEMs as a useful alternative to CEMs for H-cell E-NRR and E-NO3RR electrolyzer studies and present critical insight into membrane crossover in zero-gap GDE-cell E-NRR and E-NO3RR electrolyzers.
RESUMEN
Bipolar membranes (BPMs) are the enabling component of many promising electrochemical devices used for separation and energy conversion. Here, we describe the development of high-performance BPMs, including two-dimensional BPMs (2D BPMs) prepared by hot-pressing two preformed membranes and three-dimensional BPMs (3D BPMs) prepared by electrospinning ionomer solutions and polyethylene oxide. Graphene oxide (GOx) was introduced into the BPM junction as a water-dissociation catalyst. We assessed electrochemical performance of the prepared BPMs by voltage-current (V-I) curves and galvanostatic electrochemical impedance spectroscopy. We found the optimal GOx loading in 2D BPMs to be 100 µg cm-2, which led to complete coverage of GOx at the interface. The integration of GOx beyond this loading moderately improved electrochemical performance but significantly compromised mechanical strength. GOx-catalyzed 2D BPMs showed comparable performance with a commercially available Fumasep BPM at current densities up to 500 mA cm-2. The 3D BPMs exhibited even better performance: lower resistance and higher efficiency for water dissociation and substantially higher stability under repeated cycling up to high current densities. The improved electrochemical performance and mechanical stability of the 3D BPMs make them suitable for incorporation into CO2 electrolysis devices where high current densities are necessary.
RESUMEN
Photoelectrochemical (PEC) water splitting is an elegant method of converting sunlight and water into H2 fuel. To be commercially advantageous, PEC devices must become cheaper, more efficient, and much more durable. This work examines low-cost polycrystalline chalcopyrite films, which are successful as photovoltaic absorbers, for application as PEC absorbers. In particular, Cu-Ga-Se films with wide band gaps can be employed as top cell photocathodes in tandem devices as a realistic route to high efficiencies. In this report, we demonstrate that decreasing Cu/Ga composition from 0.66 to 0.31 in Cu-Ga-Se films increased the band gap from 1.67 to 1.86 eV and decreased saturated photocurrent density from 18 to 8 mA/cm2 as measured by chopped-light current-voltage (CLIV) measurements in a 0.5 M sulfuric acid electrolyte. Buffer and catalyst surface treatments were not applied to the Cu-Ga-Se films, and they exhibited promising stability, evidenced by unchanged CLIV after 9 months of storage in air. Finally, films with Cu/Ga = 0.36 (approximately stoichiometric CuGa3Se5) and 1.86 eV band gaps had exceptional durability and continuously split water for 17 days (â¼12 mA/cm2 at -1 V vs RHE). This is equivalent to â¼17 200 C/cm2, which is a world record for any polycrystalline PEC absorber. These results indicate that CuGa3Se5 films are prime candidates for cheaply achieving efficient and durable PEC water splitting.