RESUMEN
OBJECTIVE: To evaluate the effect of surface finishing and printing layer orientation on the surface roughness and flexural strength of three-dimensionally (3D) printed 3 mol% yttria-stabilized zirconia manufactured by stereolithography (SLA). METHODS: Ninety bar-shaped zirconia specimens (1 mm x 1 mm x 12 mm) were 3D-printed via SLA. After debinding and sintering, they were randomly divided according to the printing layer orientation: parallel (PR) or perpendicular (PD) to the tensile surface for bending test. Each group was submitted to a surface finishing protocol (n=15/group): unpolished (subgroup 0), with polished tensile surface (subgroup 1), and with polished lateral and tensile surfaces (subgroup 3). Roughness of tensile surface was determined using a contact sensor and surface morphology was analyzed under Scanning Electron Microscopy (SEM). Flexural strength, apparent elastic modulus, and Weibull parameters were assessed using a 3-point bending test. Fractured specimens were examined to identify failure origins. Finite element analysis was used to evaluate tensile stress peaks and failure risk. RESULTS: PR orientation exhibited higher strength, higher apparent elastic modulus, higher maximum principal stress peaks, and lower failure risk. For both layer orientations, groups with polished lateral and tensile sides (PR3 and PD3) were the strongest. SEM revealed that polishing led to changes in defect type, location, and size. SIGNIFICANCE: SLA zirconia shows different mechanical properties according to surface roughness and defects. Orienting the printed layers parallel to the tensile side improves its mechanical performance. Polishing can significantly improve its flexural strength. It is necessary to reduce the final product's surface roughness and large pores for its best performance.
Asunto(s)
Materiales Dentales , Circonio , Resistencia Flexional , Ensayo de Materiales , Estereolitografía , Propiedades de Superficie , Circonio/química , Materiales Dentales/químicaRESUMEN
OBJECTIVE: The objective of this study was to investigate the effects of glazing technique and firing on the surface roughness and flexural strength of an advanced lithium disilicate (ALD) and lithium disilicate (LD). METHODS: Eight groups of bar-shaped specimens (1 mm × 1 mm × 12 mm, N=160, 20/group) were manufactured from ALD (CEREC Tessera, Dentsply Sirona) and LD (IPS e.max CAD, Ivoclar). The specimens were then submitted to various posttreatments: crystallization (c), crystallization followed by a second firing (c-r), crystallization with glaze in one step (cg), and crystallization followed by a glaze layer firing (c-g). Surface roughness was measured by means of a profilometer, and flexural strength was determined using a three-point bending test. Surface morphology, fractography, and crack healing analysis were conducted using scanning electron microscopy. RESULTS: Refiring (c-r) did not affect the surface roughness (Ra) while applying glaze at both cg and c-g procedures increased the roughness. ALDc-g (442.3 ± 92.5 MPa) promoted higher strength than ALDcg (282.1 ± 64.4 MPa), whereas LDcg (402.9 ± 78.4 MPa) was stronger than LDc-g (255.5 ± 68.7 MPa). Refiring completely closed the crack in ALD, but it had a limited effect on LD. CONCLUSIONS: Two-step crystallization and glazing improved ALD strength compared to the one-step protocol. Refiring and one-step glazing do not increase LD's strength, while two-step glazing has a negative effect. CLINICAL RELEVANCE: Besides both materials being lithium-disilicate glass ceramics, the glazing technique and firing protocol affected their roughness and flexural strength differently. A two-step crystallization and glazing should be the first choice for ALD, while for LD, glazing is optional and when necessary, should be applied in one-step.
Asunto(s)
Porcelana Dental , Resistencia Flexional , Ensayo de Materiales , Propiedades de Superficie , Porcelana Dental/química , Cerámica/química , Diseño Asistido por ComputadoraRESUMEN
This study investigated the fatigue failure load of simplified monolithic yttria partially stabilized zirconia polycrystal restorations cemented to a dentin-like substrate using different luting systems. Disc-shaped ceramic (Zenostar T, 10 mm Ø × 0.7 mm thick) and dentin-like substrate (10 mm Ø × 2.8 mm thick) were produced and randomly allocated into eight groups, without or with thermocycling (TC=5-55°C/12,000×): "cement" (RelyX Luting 2 - glass ionomer cement [Ion], [Ion/TC]; RelyX U200 - self-adhesive resin cement [Self], [Self/TC]; Single Bond Universal+RelyX Ultimate - MDP-containing adhesive + resin cement [MDPAD + RC], [MDP-AD + RC/TC]; ED Primer II+Panavia F 2.0 - Primer + MDP-containing resin cement [PR + MDP-RC], [PR + MDP-RC/TC])). Each luting system was used as recommended by the manufacturer. Staircase methodology (20 Hz; 250,000 cycles) was applied for obtaining the fatigue failure loads. Fractographic characteristics were also assessed. At baseline, the Ion group presented the lowest fatigue load, although it was statistically similar to the Self group. The resin-based cement systems presented the highest fatigue performance, with the Ion group being only statistically equal to the Self group. Thermocycling influenced the groups differently. After aging, the MDP-AD + RC presented the highest mean, followed by the PR + MDP-RC and Self groups, while the Ion group had the lowest mean. Fractographic analysis depicted all failures as radial cracks starting at the zirconia intaglio surface. The luting system with MDP-containing adhesive applied prior to the resin cement presented the highest fatigue failure load after aging, presenting the best predictability of stable performance. Despite this, monolithic zirconia presents high load-bearing capability regardless of the luting agent.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Cerámica/química , Cementos Dentales/química , Cementos Dentales/uso terapéutico , Materiales Dentales , Análisis del Estrés Dental , Cementos de Ionómero Vítreo , Ensayo de Materiales , Cementos de Resina/química , Cementos de Resina/uso terapéutico , Propiedades de Superficie , Circonio/químicaRESUMEN
Sagittal split ramus osteotomy (SSRO) with large mandibular advancements is a common surgical procedure and could be indicated for patients with sleep apnoea. As a large variety of fixation methods is used for the stabilisation of SSRO, a biomechanical test model was used to analyse which fixation technique was most stable. For this in vitro study, 80 polyurethane hemimandibles with a prefabricated SSRO were used as substrates. Loads in Newtons were recorded at displacements of the mandibular incisive edge at 1mm, 3mm and 5mm. The samples were divided into two groups: mandibular advancements of 10mm and 15mm. In both groups, four fixation techniques were used: (A) one four-hole miniplate; (B) two four-hole miniplates; (C) one four-hole miniplate plus one bicortical screw; and (D) three bicortical screws in an inverted-L arrangement. In group 1, three bicortical screws resulted in the best stability, and in group 2, two miniplates resulted in the best stability. The use of two miniplates did not show significant differences between both groups. Other fixation methods showed more stability with 10mm advancements. This study therefore suggests that in SSRO with advancements exceeding 10mm, the use of two miniplates is the optimal means of providing rigid fixation.
Asunto(s)
Avance Mandibular , Osteotomía Sagital de Rama Mandibular , Fenómenos Biomecánicos , Placas Óseas , Humanos , Mandíbula/cirugía , Modelos AnatómicosRESUMEN
Ideal restoration material for caries would allow attachment of gingival epithelia. The attachment of epithelial cells to specimens of the 4 most commercially used well- or partially-cured resin composites, with and without TEGDMA, was assessed. Effects of resin composite on the Ca9-22 gingival epithelial cell-line were assessed by measuring the cytotoxicity, viability and gene expression for attachment, apoptosis, ROS-production, pro-inflammatory cytokines, and matrix metalloproteinases. As controls, cells on tissue culture plastic or bovine tooth enamel specimens were used. Significantly less cell attachment was measured on freshly made resin-composite specimens. Concomitantly, significantly higher cytotoxicity was measured in the presence of freshly made resin-composite specimens. However, after 8 d of leakage, the cell attachment to and cytotoxicity of the resin composite was comparable to bovine tooth enamel. Significantly higher expressions of IL6, MMP2, BCL6 and ITGA4 were measured in cells attached to resin-composite surfaces than controls. There were no significant differences between the results using different conditions of resin composite, with or without TEGDMA and well or partially cured. Less cell attachment and presence of more inflammatory markers were observed on all freshly-made resin-composite surfaces. However, after a leakage period attachment of cells to the resin composite improved to the level of natural tooth materials such as enamel. This indicated that the negative effects of resin composites on epithelial cells might be transient.
Asunto(s)
Resinas Compuestas/farmacología , Epitelio/fisiología , Encía/fisiología , Animales , Bovinos , Adhesión Celular/efectos de los fármacos , Recuento de Células , Muerte Celular/efectos de los fármacos , Línea Celular , Supervivencia Celular/efectos de los fármacos , Esmalte Dental/efectos de los fármacos , Esmalte Dental/ultraestructura , Células Epiteliales/citología , Células Epiteliales/efectos de los fármacos , Células Epiteliales/ultraestructura , Epitelio/efectos de los fármacos , Regulación de la Expresión Génica/efectos de los fármacos , Encía/efectos de los fármacos , HumanosRESUMEN
Tooth wear in bruxing patients often results in a need for treatment with composite restorations. In some cases, bruxing patients receive an occlusal splint as a protective means as well. However, the wear between these opposing materials has not been investigated yet. The aim of this in vitro study was to assess the wear of different splint materials against resin composite materials. A two-body wear test was conducted using the ACTA wear machine. The materials selected for this study were three composites used for direct restorations (Filtek Z250, CLEARFIL AP-X, and Filtek Supreme XT) and four occlusal splints materials, viz. a polyamide resin (ThermoSens) an conventional (hand-processed), milled and printed polymethylmethacrylate (PMMA). As antagonistic materials, stainless steel, Filtek Supreme XT and CLEARFIL AP-X were used. The wear rate of the seven materials was determined after 200 000 cycles, using a profilometry. The rates were analysed using two-way ANOVA and post hoc Tukey's tests. The wear rates were significantly higher for the conventional and milled PMMA materials than for all other materials (P < .001). The wear rates of printed PMMA and the polyamide resin were comparable to composite wear rates. The antagonist materials have minor or no influence on the amount of wear of the various splint materials (P < .001). In conclusion, different splint materials yielded different wear rates for all antagonist materials tested. Keeping in mind that this study is an experimental in vitro study, this finding enables practitioners to choose the splint material necessary according to their patients' needs.
Asunto(s)
Materiales Dentales/química , Alisadura de la Restauración Dental/estadística & datos numéricos , Ensayo de Materiales , Ferulas Oclusales , Resinas Compuestas , Humanos , Técnicas In Vitro , Metacrilatos , Microscopía Electrónica de Rastreo , Polimetil Metacrilato , Propiedades de SuperficieRESUMEN
BACKGROUND: Nowadays, personalized medical devices are frequently used for patients. Due to the manufacturing procedure sterilization is required. How different sterilization methods affect the mechanical behavior of these devices is largely unknown. MATERIALS AND METHODS: Three poly(methyl methacrylate) (PMMA) based materials (Vertex Self-Curing, Palacos R+G, and NextDent C&B MFH) were sterilized with different sterilization methods: ethylene oxide, hydrogen peroxide gas plasma, autoclavation, and γ-irradiation. Mechanical properties were determined by testing the flexural strength, flexural modulus, fracture toughness, and impact strength. RESULTS: The flexural strength of all materials was significantly higher after γ-irradiation compared to the control and other sterilization methods, as tested in a wet environment. NextDent C&B MFH showed the highest flexural and impact strength, Palacos R+G showed the highest maximum stress intensity factor and total fracture work. CONCLUSION: Autoclave sterilization is not suitable for the sterilization of PMMA-based materials. Ethylene oxide, hydrogen peroxide gas plasma, and γ-irradiation appear to be suitable techniques to sterilize PMMA-based personalized medical devices.
Asunto(s)
Fenómenos Mecánicos , Polimetil Metacrilato , Medicina de Precisión/instrumentación , Esterilización , Rayos gamma , Gases em Plasma/química , Polimetil Metacrilato/químicaRESUMEN
The aim of this study was to evaluate the effect of grinding with diamond burs and low-temperature aging on the material surface characteristics and bacteria adhesion on a yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) surface. Y-TZP specimens were made from presintered blocks, sintered as recommended by the manufacturer, and assigned into six groups according to two factors-grinding (three levels: as sintered, grinding with extra-fine diamond bur [25-µm grit], and grinding with coarse diamond bur [181-µm grit]) and hydrothermal aging-to promote low-temperature degradation (two levels: presence/absence). Phase transformation (X-ray diffractometer), surface roughness, micromorphological patterns (atomic force microscopy), and contact angle (goniometer) were analyzed. Bacterial adhesion (colony-forming units [CFU]/biofilm) was quantified using an in vitro polymicrobial biofilm model. Both the surface treatment and hydrothermal aging promoted an increase in m-phase content. Roughness values increased as a function of increasing bur grit sizes. Grinding with a coarse diamond bur resulted in significantly lower values of contact angle (p<0.05) when compared with the extra-fine and control groups, while there were no differences (p<0.05) after hydrothermal aging simulation. The CFU/biofilm results showed that neither the surface treatment nor hydrothermal aging simulation significantly affected the bacteria adherence (p>0.05). Grinding with diamond burs and hydrothermal aging modified the Y-TZP surface properties; however, these properties had no effect on the amount of bacteria adhesion on the material surface.
Asunto(s)
Adhesión Bacteriana , Cerámica/uso terapéutico , Pulido Dental/métodos , Itrio/uso terapéutico , Circonio/uso terapéutico , Humanos , Técnicas In Vitro , Propiedades de SuperficieRESUMEN
OBJECTIVE: The aim of this study was to investigate the influence of the cementation strategy on the fatigue resistance of zirconia crowns. The null hypothesis was that the cementation strategy would not affect the fatigue resistance of the crowns. METHODS AND MATERIALS: Seventy-five simplified molar tooth crown preparations were machined in glass fiber-filled epoxy resin. Zirconia crowns were designed (thickness=0.7 mm), milled by computer-aided design/computer-aided manufacturing, and sintered, as recommended. Crowns were cemented onto the resin preparations using five cementation strategies (n=15): ZP, luting with zinc phosphate cement; PN, luting with Panavia F resin cement; AL, air particle abrasion with alumina particles (125 µm) as the crown inner surface pretreatment + Panavia F; CJ, tribochemical silica coating as crown inner surface pretreatment + Panavia F; and GL, application of a thin layer of porcelain glaze followed by etching with hydrofluoric acid and silanization as crown inner surface pretreatment + Panavia F. Resin cement was activated for 30 seconds for each surface. Specimens were tested until fracture in a stepwise stress fatigue test (10,000 cycles in each step, 600 to 1400 N, frequency of 1.4 Hz). The mode of failure was analyzed by stereomicroscopy and scanning electron microscopy. Data were analyzed by Kaplan-Meier and Mantel-Cox (log rank) tests and a pairwise comparison (p<0.05) and by Weibull analysis. RESULTS: The CJ group had the highest load mean value for failure (1200 N), followed by the PN (1026 N), AL (1026 N), and GL (1013 N) groups, while the ZP group had the lowest mean value (706 N). Adhesively cemented groups (CJ, AL, PN, and GL) needed a higher number of cycles for failure than the group ZP did. The groups' Weibull moduli (CJ=5.9; AL=4.4; GL=3.9; PN=3.7; ZP=2.1) were different, considering the number of cycles for failure data. The predominant mode of failure was a fracture that initiated in the cement/zirconia layer. Finite element analysis showed the different stress distribution for the two models. CONCLUSION: Adhesive cementation of zirconia crowns improves fatigue resistance.
Asunto(s)
Cementación/métodos , Coronas , Diseño de Prótesis Dental , Fracaso de la Restauración Dental , Abrasión Dental por Aire , Diseño Asistido por Computadora , Porcelana Dental , Análisis del Estrés Dental , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Cementos de Resina , Propiedades de Superficie , Cemento de Fosfato de Zinc , CirconioRESUMEN
This study aimed to evaluate the bond strength between dentin and five different ceramic inlays in permanent maxillary premolars, with and without mechanical cycling. One hundred permanent maxillary premolars were prepared and divided into 10 groups (n=10) according to the ceramic system (IPS e.Max Press; IPS e.Max CAD; Vita PM9; Vita Mark II; and Vita VM7) and the mechanical cycling factor (with and without [100 N, 2 Hz, 1.2×10(6) cycles]). The inlays were adhesively cemented, and all of the specimens were cut into microbars (1×1 mm, nontrimming method), which were tested under microtensile loading. The failure mode was classified and contact angle, roughness, and microtopographic analyses were performed on each ceramic surface. The mechanical cycling had a significant effect (p=0.0087) on the bond strength between dentin and IPS e.max Press. The Vita Mark II group had the highest bond strength values under both conditions, with mechanical cycling (9.7±1.8 MPa) and without (8.2±1.9 MPa), while IPS e.Max CAD had the lowest values (2.6±1.6 and 2.2±1.4, respectively). The adhesive failure mode at the ceramic/cement interface was the most frequent. Vita Mark II showed the highest value of average roughness. IPS e.max Press and Vita Mark II ceramics presented the lowest contact angles. In conclusion, the composition and manufacturing process of ceramics seem to have an influence on the ceramic surface and resin cement bond strength. Mechanical cycling did not cause significant degradation on the dentin and ceramic bond strength under the configuration used.
Asunto(s)
Cerámica , Recubrimiento Dental Adhesivo , Porcelana Dental , Incrustaciones , Dentina , Humanos , Ensayo de Materiales , Cementos de Resina , Estrés Mecánico , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
The aim of this study was to systematically review the literature to assess the effect of grinding on the mechanical properties, structural stability and superficial characteristics of Y-TZP ceramics. The MEDLINE via PubMed and Web of Science (ISI - Web of Knowledge) electronic databases were searched with included peer-reviewed publications in English language and with no publication year limit. From 342 potentially eligible studies, 73 were selected for full-text analysis, 30 were included in the systematic review with 20 considered in the meta-analysis. Two reviewers independently selected the studies, extracted the data, and assessed the risk of bias. Statistical analyses were performed using RevMan 5.1, with random effects model, at a significance level of 0.05. A descriptive analysis considering phase transformation, Y-TZP grain size, Vickers hardness, residual stress and aging of all included studies were executed. Four outcomes were considered in the meta-analyses (factor: grinding x as-sintered) in global and subgroups analyses (grinding tool, grit-size and cooling) for flexural strength and roughness (Ra) data. A significant difference (p<0.05) was observed in the global analysis for strength, favoring as-sintered; subgroup analyses revealed that different parameters lead to different effects on strength. In the global analysis for roughness, a significant difference (p<0.05) was observed between conditions, favoring grinding; subgroup analyses revealed that different parameters also lead to different effects on roughness. High heterogeneity was found in some comparisons. Generally grinding promotes decrease in strength and increase in roughness of Y-TZP ceramics. However, the use of a grinding tool that allows greater accuracy of the movement (i.e. contra angle hand-pieces coupled to slowspeed turbines), small grit size (<50µm) and the use of plenty coolant seem to be the main factors to decrease the defect introduction and allow the occurrence of the toughening transformation mechanism, decreasing the risk of deleterious impact on Y-TZP mechanical properties.
Asunto(s)
Cerámica/análisis , Ensayo de Materiales , Itrio/análisis , Circonio/análisis , Propiedades de SuperficieRESUMEN
This study aimed to investigate the effects of grinding with diamond burs and low-temperature aging on the mechanical behavior (biaxial flexural strength and structural reliability), surface topography, and phase transformation of a Y-TZP ceramic for monolithic dental restorations. Disc-shaped specimens (Zirlux FC, Ivoclar Vivadent) were manufactured according to ISO 6872 (2008) and divided in accordance with two factors: "grinding - 3 levels" and "LTD - 2 levels". Grinding was performed using a contra-angle handpiece under constant water-cooling with different grit-sizes (extra-fine and coarse diamond burs). LTD was simulated in an autoclave at 134°C, under a pressure of 2 bar, over a period of 20h. Surface topography analysis showed an increase in roughness based on surface treatment grit-size (Coarse>Xfine>Ctrl), LTD did not influence roughness values. Both grinding and LTD promoted an increase in the amount of m-phase, although different susceptibilities to degradation were observed. According to existing literature the increase of m-phase content is a direct indicative of Y-TZP degradation. Weibull analysis showed an increase in characteristic strength after grinding (Coarse=Xfine>Ctrl), while for LTD, distinct effects were observed (CtrlAsunto(s)
Ensayo de Materiales
, Itrio/química
, Circonio/química
, Frío
, Diamante/química
, Microscopía de Fuerza Atómica
, Microscopía Electrónica de Rastreo
, Propiedades de Superficie
, Factores de Tiempo
, Difracción de Rayos X
RESUMEN
The following study aimed to evaluate the effect of grinding and low-temperature aging on the fatigue limit of Y-TZP ceramics for frameworks and monolithic restorations. Disc specimens from each ceramic material, Lava Frame (3M ESPE) and Zirlux FC (Ivoclar Vivadent) were manufactured according to ISO:6872-2008 and assigned in accordance with two factors: (1) "surface treatment"-without treatment (as-sintered, Ctrl), grinding with coarse diamond bur (181µm; Grinding); and (2) "low-temperature aging (LTD)" - presence and absence. Grinding was performed using a contra-angle handpiece under constant water-cooling. LTD was simulated in an autoclave at 134°C under 2-bar pressure for 20h. Mean flexural fatigue limits (20,000 cycles) were determined under sinusoidal loading using stair case approach. For Lava ceramic, it was observed a statistical increase after grinding procedure and different behavior after LTD stimuli (CtrlAsunto(s)
Cerámica/química
, Ensayo de Materiales
, Itrio/química
, Circonio/química
, Propiedades de Superficie
, Temperatura
RESUMEN
This study evaluated the effect of different protocols of low-temperature degradation simulation on the mechanical behavior (structural reliability and flexural strength), the surface topography (roughness), and phase transformation of a Y-TZP ceramic. Disc-shaped specimens (1.2mm×12mm, Lava Frame, 3M ESPE, Seefeld, Germany) were manufactured according to ISO:6872-2008 and divided (n=30) according to the aging protocol executed: "Ctrl" - as-sintered - without any treatment; "Dist Water" - stored at distilled water at 37°C for 365 days; "MC" mechanical cycling into two steps: First - 200N, 2.2Hz for 2.000.000 cycles, Second - 450N, 10Hz for 1.000.000 cycles; "Aut" - steam autoclave at 134°C, 2bar (200kPa) for 20h; "Aut+MC"- Aut and MC methods. Roughness analysis (µm) showed, for Ra parameter, higher statistically significant values for Ctrl 0.68 (0.27), while for Rz parameter, the highest values were observed for Ctrl 4.43(1.53) and Aut 2.24 (0.62). Surface topography analysis showed that none aging method promoted surface alterations when compared to control group. Phase transformation analysis showed that all aging methods promoted an increase in m-phase content (Ctrl: 0.94%, Dist Water: 20.73%, MC: 9.47%, Aut: 53.33% and Aut+MC: 61.91%). Weibull Analysis showed higher statistical characteristic strength values for Aut (1033.36MPa) and Dist Water (1053.76MPa). No aging method promoted deleterious impact either on the biaxial flexural strengths or on the structural reliabilities (Weibull moduli). Also, none of the aging methods promoted reduction of Y-TZP mechanical properties; thus the development of new methodologies and the association between mechanical stimuli and hydrothermal degradation should be considered to better understand the mechanism of low-temperature degradation.
Asunto(s)
Temperatura , Itrio , Circonio , Cerámica , Ensayo de Materiales , Reproducibilidad de los Resultados , Propiedades de SuperficieRESUMEN
OBJECTIVES: The objective of this study was to investigate the effects of treatments of the intaglio surface of Y-TZP frameworks and luting agents on the fatigue resistance of all-ceramic crowns. METHODS: A research design was chosen that attempted to reduce the likelihood of Hertzian cracking and to increase the probability of fracture initiation at the intaglio surface of the framework. Ninety identical preparations were machined in a dentin-like epoxy composite. Each preparation was restored with a Y-TZP framework made by a CAD/CAM system and veneered using feldspathic ceramic. Prior to cementation the intaglio surface of the ceramic was treated using one of four treatments: 1) cleaning with isopropyl alcohol; 2) application of an overglaze; 3) sandblasting with 125 µm aluminum oxide powder; and 4) sandblasting with 30 µm silica powder (CJ). One of three luting cements were used: 1) zinc phosphate; 2) glass ionomer; and 3) adhesive resin cement (PN). All three cements were tested against frameworks that were alcohol cleaned. Only the PN cements were tested against frameworks that had been sandblasted or glazed. Altogether, six groups of 15 specimens each were tested. Fatigue resistance was evaluated using stepwise loads at 1.4 Hz until failure: 5000 cycles at maximum load of 200 N, followed by 10,000 cycles at maximum loads of 800, 1000, 1200, and 1400 N. The cement thickness and failure modes were analyzed using a stereomicroscope and scanning electron microscopy. The results were analyzed using the Kaplan-Meier and Mantel-Cox log rank tests (5%), a one-way analysis of variance, Tukey multiple comparison test, and Weibull nonparametric test. RESULTS: The predominant failure mode was chipping of the veneer. The crowns cemented with the adhesive resin cement exhibited chipping failure at higher mean loads than did crowns cemented with cements that usually do not bond strongly with dentin. When the adhesive cement was used, glazing and sandblasting intaglio framework surface treatments exhibited lower mean loads at chipping than did crowns whose intaglio surface was only cleaned with alcohol. Weibull analysis indicated that all specimens had a high ratio of late-to-early failures. CONCLUSIONS: The fatigue experiment produced a pattern of failures that is very similar to that observed in clinical trials of Y-TZP crowns that are veneered with feldspathic porcelain. Crowns cemented with an adhesive resin cement exhibited chipping at a significantly higher mean load than those cemented with luting cements that do not usually form strong bonds with dentin. When cemented with adhesive resin cement, glazing or sandblasting the intaglio surface of the framework significantly reduced the mean fatigue loads at which chipping of veneers occurred, as compared to crowns whose intaglio surface had only been cleaned with alcohol. For this cement glazing or sandblasting the intaglio surface of the crown is not recommended.
Asunto(s)
Porcelana Dental , Fracaso de la Restauración Dental , Coronas , Diseño de Prótesis Dental , Análisis del Estrés Dental , Ensayo de Materiales , Cementos de ResinaRESUMEN
This study evaluated the effects of low-temperature aging on the surface topography, phase transformation, biaxial flexural strength, and structural reliability of a ground Y-TZP ceramic. Disc-shaped specimens were manufactured and divided according to two factors: "grinding" - without grinding (as-sintered, Ctrl), grinding with an extra-fine diamond bur (25 µm Xfine) and coarse diamond bur (181 µm Coarse); and "low-temperature-aging" (absence or presence). Grinding was performed using a contra-angle handpiece under water-cooling. Aging was performed in an autoclave at 134 °C, under 2 bar, over a period of 20 h. Surface topography analysis showed an increase in roughness based on grit-size (Coarse>Xfine>Ctrl), and aging promoted different effects on roughness (Ctrl Ag
Asunto(s)
Fenómenos Mecánicos , Temperatura , Itrio , Circonio , Transición de Fase , Propiedades de Superficie , Factores de Tiempo , Itrio/química , Circonio/químicaRESUMEN
OBJECTIVE: Optical properties of teeth are mimicked by composite layering techniques by combining a relatively opaque layer (dentin) with more translucent layers (enamel). However, the replacing material cannot always optically imitate the tooth when applied in the same thickness as that of the natural tissues. The natural layering composite system is available in 2 concepts: (1) dentin (D) and enamel (E) have the same shade but with different translucencies; (2) D and E have different shades where E is always the same high translucent shade. The objective was to evaluate the influence of varying thicknesses of E and D composites on the overall color and on the translucency for both concepts. METHODS: For each concept three composite brands were tested; Concept 1: Clearfil Photo Bright (Kuraray), Herculite XRV Ultra (Kerr), Venus Diamond (Heraeus Kulzer); Concept 2: Amaris (VOCO), CeramX Duo (DENTSPLY) and Point4 (Kerr). Two specimens of each shade (A1-A3) per composite were made of standardized thicknesses with a poly-acrylic mold and Teflon cover, making 36 specimens of wedge-like dimension. The L*a*b* values were measured three times against a white and black background (n=216). Student's t-tests revealed significant levels between the average ΔE* values of the 3 areas for each composite. RESULTS: Statistically significant differences (p<0.05) were found for all thicknesses and for all shades between the concepts. Concept 2 showed greater variations in ΔE* with increased thicknesses. SIGNIFICANCE: Concept 2 composites are more sensitive to layer thickness changes, which implicates less predictability in a daily clinical routine.
Asunto(s)
Color , Resinas CompuestasRESUMEN
Orally applied metal alloys can cause undesirable physical effects. A distinction needs to be made in this respect between local and systemic reactions and toxic and immunological reactions. A case is presented which illustrates this problem. In this case, the application of orthodontic appliances was probably the trigger for an exacerbation of nickel allergy. The oral exposure to nickel resulted in hand eczema. The patient was also exposed to nickel by single-unit fixed dental prostheses, a removable dental prosthesis, and food, as a result of which removal of the orthodontic appliances did not result in complete healing. Therefore, the single-unit fixed dental prostheses also had to be removed and food had to be prepared henceforward in nickel free pans.
Asunto(s)
Aleaciones Dentales/química , Aleaciones Dentales/toxicidad , Eccema/inducido químicamente , Aleaciones de Cerámica y Metal/efectos adversos , Eccema/diagnóstico , Femenino , Humanos , Metales/química , Metales/toxicidad , Persona de Mediana Edad , Níquel/química , Níquel/toxicidad , Titanio/química , Titanio/toxicidadRESUMEN
Recently, a crucial role of Th2 responses in nickel allergic contact dermatitis (ACD) was demonstrated. As palladium allergy is an issue of growing interest, the diagnostic potential of Th2 parameters for palladium sensitization was investigated. Palladium (Na(2) [PdCl(4)])-induced lymphocyte proliferation (LPT), Th1 and Th2 cytokine production were correlated with skin test (ST) reactivity in 16 positive and 21 negative controls. Furthermore, the diagnostic potential of these assays was evaluated using receiver operating characteristics (ROC) analysis. For comparison, same experiments were carried out for nickel (NiSO(4)). Correlation coefficients between palladium ST reactivity and IFN-γ, LPT, IL-5, and IL-13 were 0.34, 0.51, 0.69, and 0.78, and overall test accuracies were 68%, 81%, 89%, and 95%, respectively. Both palladium- and nickel-mediated Th2 responses tightly correlate with ST reactivity, supporting recent findings on the crucial role of Th2 involvement in ACD. Therefore, these assays may have great potential as diagnostic tools for future in vitro sensitization testing.
Asunto(s)
Citocinas/biosíntesis , Dermatitis Alérgica por Contacto/diagnóstico , Dermatitis Alérgica por Contacto/inmunología , Paladio/inmunología , Pruebas Cutáneas , Células Th2/inmunología , Humanos , Níquel/inmunología , Curva ROC , Reproducibilidad de los ResultadosRESUMEN
OBJECTIVES: The aim of this study was to test the new resin composite "NECO" as a material for indirect restorations clinically. METHODS: Forty-five patients were selected, of which 12 men and 33 women, with a mean age of 53. A total of 91 post-canine indirect resin composite NECO (Heraeus Kulzer, GmbH) restorations were placed, of which 86 full crowns and 5 onlays. Restorations were cemented with either resin cement (2bond2) or resin modified glass ionomer cement (Fuji Plus). The restorations were evaluated 1-2 weeks (baseline), 6 months, 1, 2, and 3 years after placement. At these recalls, success and survival data of the abutment teeth were documented. Survival was defined as the restoration being in situ, and success as the restoration in situ without complications. RESULTS: After 3 years in service, the restorations showed success and survival rates of 84.8 and 91.6%, respectively. Cementation with Fuji Plus showed a trend (p=0.054) toward higher success (93.1%) and survival (100%) rates compared to cementation with 2bond2 cement which showed success and survival rates of 81.4 and 87.9% respectively. Restorations on vital teeth resulted in success and survival rates of 86.8 and 95.3% respectively, while restorations on endodontically treated teeth showed success and survival rates of 82.6 and 87.5%. This difference was not statistically significant (p=0.296). SIGNIFICANCE: Three-year success and survival rates of NECO restorations were 84.8 and 91.6%, respectively. The design of the preparation and restoration should take the material properties into account in order to enhance the clinical performance.