Silicon-based composites are promising candidates as the next-generation anode materials for high-performance lithium-ion batteries (LIBs) due to their high theoretical specific capacity, abundant reserves, and reliable security. However, expensive raw materials and complicated preparation processes give silicon carbon anode a high price and poor batch stability, which become a stumbling block to its large-scale practical application. In this work, a novel ball milling-catalytic pyrolysis method is developed to fabricate a silicon nanosheet@amorphous carbon/N-doped graphene (Si-NSs@C/NG) composite with cheap high-purity micron-size silica powder and melamine as raw materials. Through systematic characterizations such as XRD, Raman, SEM, TEM and XPS, the formation process of NG and a Si-NSs@C/NG composite is graphically demonstrated. Si-NSs@C is uniformly intercalated between NG nanosheets, and these two kinds of two-dimensional (2D) materials are combined in a surface-to-surface manner, which immensely buffers the stress changes caused by volume expansion and contraction of Si-NSs. Attributed to the excellent electrical conductivity of graphene layer and the coating layer, the initial reversible specific capacity of Si-NSs@C/NG is 807.9 mAh g-1 at 200 mA g-1, with a capacity retention rate of 81% in 120 cycles, exhibiting great potential for application as an anode material for LIBs. More importantly, the simple and effective process and cheap precursors could greatly reduce the production cost and promote the commercialization of silicon/carbon composites.
RESUMEN
Heterostructures with a rich phase boundary are attractive for surface-mediated microwave absorption (MA) materials. However, understanding the MA mechanisms behind the heterogeneous interface remains a challenge. Herein, a phosphine (PH3) vapor-assisted phase and structure engineering strategy was proposed to construct three-dimensional (3D) porous Ni12P5/Ni2P heterostructures as microwave absorbers and explore the role of the heterointerface in MA performance. The results indicated that the heterogeneous interface between Ni12P5 and Ni2P not only creates sufficient lattice defects for inducing dipolar polarization but also triggers uneven spatial charge distribution for enhancing interface polarization. Furthermore, the porous structure and proper component could provide an abundant heterogeneous interface to strengthen the above polarization relaxation process, thereby greatly optimizing the electromagnetic parameters and improving the MA performance. Profited by 3D porous heterostructure design, P400 could achieve the maximum reflection loss of -50.06 dB and an absorption bandwidth of 3.30 GHz with an ultrathin thickness of 1.20 mm. Furthermore, simulation results confirmed its superior ability (14.97 dB m2 at 90°) to reduce the radar cross section in practical applications. This finding may shed light on the understanding and design of advanced heterogeneous MA materials.
RESUMEN
A three-dimensional bubble graphene film, with controllable and uniform macropores and tailorable microstructure, was fabricated by a facile hard templating strategy and exhibit extraordinary electrochemical capacitance with high rate capability (1.0 V s(-1)).