RESUMEN
Ferrite-containing polymer composites are of great interest for the development of radar-absorbing and -shielding materials (RAMs and RSMs). The main objective of RAM and RSM development is to achieve a combination of efficient electromagnetic wave (EMW) absorption methods with advantageous technological and mechanical properties as well as acceptable weight and dimensions in the final product. This work deals with composite RAMs and RSMs containing spinel-structured ferrites. These materials are chosen since they can act as efficient RAMs in the form of ceramic plates and as fillers for radar-absorbing polymer composites (RAC) for electromagnetic radiation (EMR). Combining ferrites with conducting fillers can broaden the working frequency range of composite RAMs due to the activation of various absorption mechanisms. Ferrite-containing composites are the most efficient materials that can be used as the working media of RAMs and RSMs due to a combination of excellent dielectric and magnetic properties of ferrites. This work contains a brief review of the main theoretical standpoints on EMR interaction with materials, a comparison between the radar absorption properties of ferrites and ferrite-polymer composites and analysis of some phenomenological aspects of the radar absorption mechanisms in those composites.
RESUMEN
Binary and ternary composites (CM) based on M-type hexaferrite (HF), polymer matrix (PVDF) and carbon nanomaterials (quasi-one-dimensional carbon nanotubes-CNT and quasi-two-dimensional carbon nanoflakes-CNF) were prepared and investigated for establishing the impact of the different nanosized carbon on magnetic and electrodynamic properties. The ratio between HF and PVDF in HF + PVDF composite was fixed (85 wt% HF and 15 wt% PVDF). The concentration of CNT and CNF in CM was fixed (5 wt% from total HF + PVDF weight). The phase composition and microstructural features were investigated using XRD and SEM, respectively. It was observed that CM contains single-phase HF, γ- and ß-PVDF and carbon nanomaterials. Thus, we produced composites that consist of mixed different phases (organic insulator matrix-PDVF; functional magnetic fillers-HF and highly electroconductive additives-CNT/CNF) in the required ratio. VSM data demonstrate that the main contribution in main magnetic characteristics belongs to magnetic fillers (HF). The principal difference in magnetic and electrodynamic properties was shown for CNT- and CNF-based composites. That confirms that the shape of nanosized carbon nanomaterials impact on physical properties of the ternary composited-based magnetic fillers in polymer dielectric matrix.