RESUMEN
Oxide-derived metals are produced by reducing an oxide precursor. These materials, including gold, have shown improved catalytic performance over many native metals. The origin of this improvement for gold is not yet understood. In this study, operando non-resonant sum frequency generation (SFG) and ex situ high-pressure X-ray photoelectron spectroscopy (HP-XPS) have been employed to investigate electrochemically-formed oxide-derived gold (OD-Au) from polycrystalline gold surfaces. A range of different oxidizing conditions were used to form OD-Au in acidic aqueous medium (H3PO4, pH = 1). Our electrochemical data after OD-Au is generated suggest that the surface is metallic gold, however SFG signal variations indicate the presence of subsurface gold oxide remnants between the metallic gold surface layer and bulk gold. The HP-XPS results suggest that this subsurface gold oxide could be in the form of Au2O3 or Au(OH)3. Furthermore, the SFG measurements show that with reducing electrochemical treatments the original gold metallic state can be restored, meaning the subsurface gold oxide is released. This work demonstrates that remnants of gold oxide persist beneath the topmost gold layer when the OD-Au is created, potentially facilitating the understanding of the improved catalytic properties of OD-Au.
RESUMEN
The large-scale conversion of N2 and H2 into NH3 (refs. 1,2) over Fe and Ru catalysts3 for fertilizer production occurs through the Haber-Bosch process, which has been considered the most important scientific invention of the twentieth century4. The active component of the catalyst enabling the conversion was variously considered to be the oxide5, nitride2, metallic phase or surface nitride6, and the rate-limiting step has been associated with N2 dissociation7-9, reaction of the adsorbed nitrogen10 and also NH3 desorption11. This range of views reflects that the Haber-Bosch process operates at high temperatures and pressures, whereas surface-sensitive techniques that might differentiate between different mechanistic proposals require vacuum conditions. Mechanistic studies have accordingly long been limited to theoretical calculations12. Here we use X-ray photoelectron spectroscopy-capable of revealing the chemical state of catalytic surfaces and recently adapted to operando investigations13 of methanol14 and Fischer-Tropsch synthesis15-to determine the surface composition of Fe and Ru catalysts during NH3 production at pressures up to 1 bar and temperatures as high as 723 K. We find that, although flat and stepped Fe surfaces and Ru single-crystal surfaces all remain metallic, the latter are almost adsorbate free, whereas Fe catalysts retain a small amount of adsorbed N and develop at lower temperatures high amine (NHx) coverages on the stepped surfaces. These observations indicate that the rate-limiting step on Ru is always N2 dissociation. On Fe catalysts, by contrast and as predicted by theory16, hydrogenation of adsorbed N atoms is less efficient to the extent that the rate-limiting step switches following temperature lowering from N2 dissociation to the hydrogenation of surface species.
RESUMEN
Operando probing by x-ray photoelectron spectroscopy (XPS) of certain hydrogenation reactions are often limited by the scattering of photoelectrons in the gas phase. This work describes a method designed to partially circumvent this so called pressure gap. By performing a rapid switch from a high pressure (where acquisition is impossible) to a lower pressure we can for a short while probe a "remnant" of the high pressure surface as well as the time dynamics during the re-equilibration to the new pressure. This methodology is demonstrated using the CO2 and the CO hydrogenation reaction over Rh(211). In the CO2 hydrogenation reaction, the remnant surface of a 2â bar pressure shows an adsorbate distribution which favors chemisorbed CHx adsorbates over chemisorbed CO. This contrasts against previous static operando spectra acquired at lower pressures. Furthermore, the pressure jumping method yields a faster acquisition and more detailed spectra than static operando measurements above 1â bar. In the CO hydrogenation reaction, we observe that CHx accumulated faster during the 275â mbar low pressure regime, and different hypotheses are presented regarding this observation.
RESUMEN
Carbide formation on iron-based catalysts is an integral and, arguably, the most important part of the Fischer-Tropsch synthesis process, converting CO and H2 into synthetic fuels and numerous valuable chemicals. Here, we report an in situ surface-sensitive study of the effect of pressure, temperature, time, and gas feed composition on the growth dynamics of two distinct iron-carbon phases with the octahedral and trigonal prismatic coordination of carbon sites on an Fe(110) single crystal acting as a model catalyst. Using a combination of state-of-the-art X-ray photoelectron spectroscopy at an unprecedentedly high pressure, high-energy surface X-ray diffraction, mass spectrometry, and theoretical calculations, we reveal the details of iron surface carburization and product formation under semirealistic conditions. We provide a detailed insight into the state of the catalyst's surface in relation to the reaction.
RESUMEN
The active chemical state of zinc (Zn) in a zinc-copper (Zn-Cu) catalyst during carbon dioxide/carbon monoxide (CO2/CO) hydrogenation has been debated to be Zn oxide (ZnO) nanoparticles, metallic Zn, or a Zn-Cu surface alloy. We used x-ray photoelectron spectroscopy at 180 to 500 millibar to probe the nature of Zn and reaction intermediates during CO2/CO hydrogenation over Zn/ZnO/Cu(211), where the temperature is sufficiently high for the reaction to rapidly turn over, thus creating an almost adsorbate-free surface. Tuning of the grazing incidence angle makes it possible to achieve either surface or bulk sensitivity. Hydrogenation of CO2 gives preference to ZnO in the form of clusters or nanoparticles, whereas in pure CO a surface Zn-Cu alloy becomes more prominent. The results reveal a specific role of CO in the formation of the Zn-Cu surface alloy as an active phase that facilitates efficient CO2 methanol synthesis.
RESUMEN
The CO hydrogenation reaction over the Rh(111) and (211) surfaces has been investigated operando by X-ray photoelectron spectroscopy at a pressure of 150 mbar. Observations of the resting state of the catalyst give mechanistic insight into the selectivity of Rh for generating ethanol from CO hydrogenation. This study shows that the Rh(111) surface does not dissociate all CO molecules before hydrogenation of the O and C atoms, which allows methoxy and other both oxygenated and hydrogenated species to be visible in the photoelectron spectra.
RESUMEN
Subsurface oxygen has been proposed to be crucial in oxide-derived copper (OD-Cu) electrocatalysts for enhancing the binding of CO intermediates during CO2 reduction reaction (CO2 RR). However, the presence of such oxygen species under reductive conditions still remains debated. In this work, the existence of subsurface oxygen is validated by grazing incident hard X-ray photoelectron spectroscopy, where OD-Cu was prepared by reduction of Cu oxide with H2 without exposing to air. The results suggest two types of subsurface oxygen embedded between the fully reduced metallic surface and the Cu2 O buried beneath: (i)â oxygen staying at lattice defects and/or vacancies in the surface-most region and (ii)â interstitial oxygen intercalated in metal structure. This study adds convincing support to the presence of subsurface oxygen in OD-Cu, which previously has been suggested to play an important role to mitigate the σ-repulsion of Cu for CO intermediates in CO2 RR.
RESUMEN
Heterogeneous catalyst surfaces are dynamic entities that respond rapidly to changes in their local gas environment, and the dynamics of the response is a decisive factor for the catalysts' action and activity. Few probes are able to map catalyst structure and local gas environment simultaneously under reaction conditions at the timescales of the dynamic changes. Here we use the CO oxidation reaction and a Pd(100) model catalyst to demonstrate how such studies can be performed by time-resolved ambient pressure photoelectron spectroscopy. Central elements of the method are cyclic gas pulsing and software-based event-averaging by image recognition of spectral features. A key finding is that at 3.2 mbar total pressure a metallic, predominantly CO-covered metallic surface turns highly active for a few seconds once the O2:CO ratio becomes high enough to lift the CO poisoning effect before mass transport limitations triggers formation of a â5 oxide.
RESUMEN
Performing fundamental operando catalysis studies under realistic conditions is a key to further develop and increase the efficiency of industrial catalysts. Operando X-ray photoelectron spectroscopy (XPS) experiments have been limited to pressures, and the relevance for industrial applications has been questioned. Herein, we report on the CO oxidation experiment on Pd(100) performed at a total pressure of 1 bar using XPS. We investigate the light-off regime and the surface chemical composition at the atomistic level in the highly active phase. Furthermore, the observed gas-phase photoemission peaks of CO2, CO, and O2 indicate that the kinetics of the reaction during the light-off regime can be followed operando, and by studying the reaction rate of the reaction, the activation energy is calculated. The reaction was preceded by an in situ oxidation study in 7% O2 in He and a total pressure of 70 mbar to confirm the surface sensitivity and assignment of the oxygen-induced photoemission peaks. However, oxygen-induced photoemission peaks were not observed during the reaction studies, but instead, a metallic Pd phase is present in the highly active regime under the conditions applied. The novel XPS setup utilizes hard X-rays to enable high-pressure studies, combined with a grazing incident angle to increase the surface sensitivity of the measurement. Our findings demonstrate the possibilities of achieving chemical information of the catalyst, operando, on an atomistic level, under industrially relevant conditions.
RESUMEN
Using grazing incidence X-rays and X-ray photoelectron spectroscopy during the mass transfer limited catalytic oxidation of CO, the long-range surface structure of Pd(100) was investigated. Under the reaction conditions of 50:4 O2 to CO, 300 mbar pressure, and temperatures between 200 and 450 °C, the surface structure resulting from oxidation and the subsequent oxide reduction was elucidated. The reduction cycle was halted, and while under reaction conditions, angle-dependent X-ray photoelectron spectroscopy close to the critical angle of Pd and modeling of the data was performed. Two proposed models for the system were compared. The suggestion with the metallic islands formed on top of the oxide island was shown to be consistent with the data.
RESUMEN
Hard x-ray photoelectron spectroscopy (HAXPES) is establishing itself as an essential technique for the characterisation of materials. The number of specialised photoelectron spectroscopy techniques making use of hard x-rays is steadily increasing and ever more complex experimental designs enable truly transformative insights into the chemical, electronic, magnetic, and structural nature of materials. This paper begins with a short historic perspective of HAXPES and spans from developments in the early days of photoelectron spectroscopy to provide an understanding of the origin and initial development of the technique to state-of-the-art instrumentation and experimental capabilities. The main motivation for and focus of this paper is to provide a picture of the technique in 2020, including a detailed overview of available experimental systems worldwide and insights into a range of specific measurement modi and approaches. We also aim to provide a glimpse into the future of the technique including possible developments and opportunities.
RESUMEN
We demonstrate the emergence and control of magnetic phases between magnetite (Fe3O4), a ferrimagnetic halfmetal, and SrTiO3, a transparent nonmagnetic insulator considered the bedrock of oxide-based electronics. The Verwey transition ( TV) was detected to persist from bulk-like down to ultrathin Fe3O4 films, decreasing from 117 ± 4 K (38 nm) to 25 ± 4 K (2 nm), respectively. Element-selective electronic and magnetic properties of the ultrathin films and buried interfaces are studied by angle-dependent hard X-ray photoelectron spectroscopy and X-ray magnetic circular dichroism techniques. We observe a reduction of Fe2+ ions with decreasing film thickness, accompanied by an increase of Fe3+ ions in both tetrahedral and octahedral sites and conclude on the formation of a magnetically active ferrimagnetic 2 u.c. γ-Fe2O3 intralayer. To manipulate the interfacial magnetic phase, a postannealing process causes the controlled reduction of the γ-Fe2O3 that finally leads to stoichiometric and ferrimagnetic Fe3O4/SrTiO3(001) heterointerfaces.