RESUMEN
We have demonstrated nanofabrication with commercialized cellulose acetate. Cellulose acetate is used for bulk nanofabrication and surface nanofabrication. In bulk nanofabrication, cellulose acetate reacts with an e-beam and permanent patterns are formed in it instead of being transferred to other substrates. We have studied the nano relief modulation performance of cellulose acetate before and after development. The depth of the nanopatterns is magnified after development, and is varied by exposing dosage and line width of the pattern. The thinnest 65 nm wide line is achieved in the bulk fabrication. We also demonstrate a binary phase Fresnel lens array which is directly patterned in a cellulose acetate sheet. Because of its unique mechanical and optical properties, cellulose is a good candidate for a template material for soft imprinting lithography. In the surface nanofabrication, cellulose acetate thin film spin-coated on silicon wafers is employed as a new resist for e-beam lithography. We achieved 50 nm lines with 100 nm pitches, dots 50 nm in diameter, and single lines with the smallest width of 20 nm. As a new resist of e-beam lithography, cellulose acetate has high resolution comparable with conventional resists, while having several advantages such as low cost, long stock time and less harmfulness to human health.
RESUMEN
We provide a 'growing' method for fabricating a microlens array with lateral size of a few microns or less. Instead of using complicated etching techniques, the method forms a spherical profile of the lens using conformal chemical vapor deposition. We have fabricated two lens arrays. One has a pitch of 1200 nm, a circular aperture 1000 nm in diameter and a sag height of 130 nm. The other array has a pitch of 600 nm, and a square aperture of 600 nm × 600 nm, with a fill factor close to 100%. The maximum profile deviation between the fabricated lens and an ideal sphere is about 11% and 14% respectively. The calculation indicates that the curvature difference of the profile of the square lens in the orthogonal and diagonal direction is 5.5%. The roughness of the lens is measured as approximately 6 nm.