Sb4O5I2: Enhancing Birefringence through Optimization of Sb/I Ratio for Alignment of Stereochemically Active Lone Pairs.

Birefringent crystals are the key components of functional optics, contributing significantly to scientific and technological advancements. To enhance birefringence, the presence of stereochemically active lone pairs offers a unique opportunity. In fact, strengthening the stereochemical activity and aligning uniformly lone pairs face tough challenges. Herein, an anisotropic layered crystal, Sb4O5I2, is discovered to exhibit enhanced birefringence. The influence of crystal symmetry on the birefringence of Sb4O5X2 (X = Cl, Br, or I) is found to be minor. Instead, the asymmetric nature of ABUCBs (i.e., cis-X3[SbO3]6- and cis-X3[SbO4]8-) plays a crucial role in enhancing the optical anisotropy. And the orientation of these ABUCBs is equally important. We demonstrate that by adjusting the Sb/I ratio from 5:1 to 2:1, all of the intralayer Sb atoms in Sb5O7I-P63 are forced onto the surface position. This structural adjustment leads to strengthened ionic bonding interactions, enhanced activity of the lone pairs, and uniform alignments of the ABUCBs in Sb4O5I2. Consequently, this results in a 6-fold increase in birefringence.

Room-Temperature High-Performance Thermoelectric Bi0.6 Sb0.4 Te: Elimination of Detrimental Band Inversion in BiTe.

Room-temperature thermoelectric materials are the key to miniaturizing refrigeration equipment and have great scientific and social implications, yet their application is hindered by their extreme scarcity. BiTe exhibiting strong spin-orbit coupling peaks ZT at 600 K. Herein, we discover the synergy effect of Sb doping in BiTe that eliminates the detrimental band inversion and leads to an overlap of conduction band (CB) and valence band that significantly increases the S from 33 to 124 µV K-1 . In addition, this effect enhances the µ from 58 to 92 cm2  V-1 s-1 owing to the sharp increase in the CB slope along the Γ-A in the first Brillouin zone. Furthermore, Sb doping increases the anharmonicity, shortens the phonon lifetime and lowers κlat . Finally, Se/Sb codoping further optimizes the ZT to 0.6 at 300 K, suggesting that Bi0.6 Sb0.4 Te1-y Sey is a potential room-temperature TE material.