Utilizing Rapid Hydrogen Peroxide Generation from 6-Hydroxycatechol to Design Moisture-Activated, Self-Disinfecting Coating.

A coating that can be activated by moisture found in respiratory droplets could be a convenient and effective way to control the spread of airborne pathogens and reduce fomite transmission. Here, the ability of a novel 6-hydroxycatechol-containing polymer to function as a self-disinfecting coating on the surface of polypropylene (PP) fabric was explored. Catechol is the main adhesive molecule found in mussel adhesive proteins. Molecular oxygen found in an aqueous solution can oxidize catechol and generate a known disinfectant, hydrogen peroxide (H2O2), as a byproduct. However, given the limited amount of moisture found in respiratory droplets, there is a need to enhance the rate of catechol autoxidation to generate antipathogenic levels of H2O2. 6-Hydroxycatechol contains an electron donating hydroxyl group on the 6-position of the benzene ring, which makes catechol more susceptible to autoxidation. 6-Hydroxycatechol-coated PP generated over 3000 µM of H2O2 within 1 h when hydrated with a small amount of aqueous solution (100 µL of PBS). The generated H2O2 was three orders of magnitude higher when compared to the amount generated by unmodified catechol. 6-Hydroxycatechol-containing coating demonstrated a more effective antimicrobial effect against both Gram-positive (Staphylococcus aureus and Staphylococcus epidermidis) and Gram-negative (Pseudomonas aeruginosa and Escherichia coli) bacteria when compared to unmodified catechol. Similarly, the self-disinfecting coating reduced the infectivity of both bovine viral diarrhea virus and human coronavirus 229E by as much as a 2.5 log reduction value (a 99.7% reduction in viral load). Coatings containing unmodified catechol did not generate sufficient H2O2 to demonstrate significant virucidal effects. 6-Hydroxycatechol-containing coating can potentially function as a self-disinfecting coating that can be activated by the moisture present in respiratory droplets to generate H2O2 for disinfecting a broad range of pathogens.

Pair of Functional Polyesters That Are Photo-Cross-Linkable and Electrospinnable to Engineer Elastomeric Scaffolds with Tunable Structure and Properties.

A pair of alkyne- and thiol-functionalized polyesters are designed to engineer elastomeric scaffolds with a wide range of tunable material properties (e.g., thermal, degradation, and mechanical properties) for different tissues, given their different host responses, mechanics, and regenerative capacities. The two prepolymers are quickly photo-cross-linkable through thiol-yne click chemistry to form robust elastomers with small permanent deformations. The elastic moduli can be easily tuned between 0.96 ± 0.18 and 7.5 ± 2.0 MPa, and in vitro degradation is mediated from hours up to days by adjusting the prepolymer weight ratios. These elastomers bear free hydroxyl and thiol groups with a water contact angle of less than 85.6 ± 3.58 degrees, indicating a hydrophilic nature. The elastomer is compatible with NIH/3T3 fibroblast cells with cell viability reaching 88 ± 8.7% relative to the TCPS control at 48 h incubation. Differing from prior soft elastomers, a mixture of the two prepolymers without a carrying polymer is electrospinnable and UV-cross-linkable to fabricate elastic fibrous scaffolds for soft tissues. The designed prepolymer pair can thus ease the fabrication of elastic fibrous conduits, leading to potential use as a resorbable synthetic graft. The elastomers could find use in other tissue engineering applications as well.

Acrylate monomer polymerization triggered by iron oxide magnetic nanoparticles and catechol containing microgels.

Phenol and its derivatives are the most used polymerization inhibitors for vinyl-based monomers. Here, we reported a novel catalytic system composed of mussel inspired adhesive moiety, catechol, in combination with iron oxide nanoparticles (IONPs) to generate hydroxyl radical (•OH) at pH 7.4. Catechol-containing microgel (DHM) was prepared by copolymerizing dopamine methacrylamide (DMA) and N-hydroxyethyl acrylamide (HEAA), which generated superoxide (•O2-) and hydrogen peroxide (H2O2) as a result of catechol oxidation. In the presence of IONPs, the generated reactive oxygen species were further converted to •OH, which initiated free radical polymerization of various water-soluble acrylate-based monomers including neutral (acrylamide, methyl acrylamide, etc.), anionic (2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt), cationic ([2-(methacryloyloxy)ethyl]trimethylammonium chloride), and zwitterionic (2-(methacryloyloxy)ethyl]dimethyl-(3-sulfopropyl)ammonium hydroxide) monomers. Compared with the typical free radical initiating systems, the reported system does not require the addition of extra initiators for polymerization. During the process of polymerization, a bilayer hydrogel was formed in situ and exhibited the ability to bend during the process of swelling. The incorporation of IONPs significantly enhanced magnetic property of the hydrogel and the combination of DHM and IONPs also improved the mechanical properties of these hydrogels.

Utilizing Robust Design to Optimize Composite Bioadhesive for Promoting Dermal Wound Repair.

Catechol-modified bioadhesives generate hydrogen peroxide (H2O2) during the process of curing. A robust design experiment was utilized to tune the H2O2 release profile and adhesive performance of a catechol-modified polyethylene glycol (PEG) containing silica particles (SiP). An L9 orthogonal array was used to determine the relative contributions of four factors (the PEG architecture, PEG concentration, phosphate-buffered saline (PBS) concentration, and SiP concentration) at three factor levels to the performance of the composite adhesive. The PEG architecture and SiP wt% contributed the most to the variation in the results associated with the H2O2 release profile, as both factors affected the crosslinking of the adhesive matrix and SiP actively degraded the H2O2. The predicted values from this robust design experiment were used to select the adhesive formulations that released 40-80 µM of H2O2 and evaluate their ability to promote wound healing in a full-thickness murine dermal wound model. The treatment with the composite adhesive drastically increased the rate of the wound healing when compared to the untreated controls, while minimizing the epidermal hyperplasia. The release of H2O2 from the catechol and soluble silica from the SiP contributed to the recruitment of keratinocytes to the wound site and effectively promoted the wound healing.

Biodegradable magnesium materials regulate ROS-RNS balance in pro-inflammatory macrophage environment.

The relationship between reactive oxygen and nitrogen species (ROS-RNS) secretion and the concomitant biocorrosion of degradable magnesium (Mg) materials is poorly understood. We found that Mg foils implanted short term in vivo (24 h) displayed large amounts of proinflammatory F4/80+/iNOS + macrophages at the interface. We sought to investigate the interplay between biodegrading Mg materials (98.6% Mg, AZ31 & AZ61) and macrophages (RAW 264.7) stimulated with lipopolysaccharide (RAW 264.7LPS) to induce ROS-RNS secretion. To test how these proinflammatory ROS-RNS secreting cells interact with Mg corrosion in vitro, Mg and AZ61 discs were suspended approximately 2 mm above a monolayer of RAW 264.7 cells, either with or without LPS. The surfaces of both materials showed acute (24 h) changes when incubated in the proinflammatory RAW 264.7LPS environment. Mg discs incubated with RAW 264.7LPS macrophages showed greater corrosion pitting, while AZ61 showed morphological and elemental bulk product changes via scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX). X-ray photoelectron spectroscopy (XPS) analysis showed a reduction in the Ca/P ratio of the surface products for AZ61 disc incubated with RAW 264.7LPS, but not the Mg discs. Moreover, RAW 264.7LPS macrophages were found to be more viable in the acute biodegradative environment generated by Mg materials, as demonstrated by calcein-AM and cleaved (active) caspase-3 staining (CC3). LPS stimulation caused an increase in ROS-RNS, and a decrease in antioxidant peroxidase activity. Mg and AZ61 were found to change this ROS-RNS balance, independently of physiological antioxidant mechanisms. The findings highlight the complexity of the cellular driven acute inflammatory responses to different biodegradable Mg, and how it can potentially affect performance of these materials.

Catechol-functionalized sulfobetaine polymer for uniform zwitterionization via pH transition approach.

The study aims to develop a modification strategy to facilitate uniform catechol-assisted zwitterionization on nitinol alloy for bio-compatibility and fouling resistance. Catechol-functionalized polysulfobetaine methacrylate (pSBMA/DA) is synthesized via dopamine-initiated photo-polymerization. Under UV irradiation, semiquinone radicals from dopamine (DA) can be generated, and prevented loss of one electron to intramolecular cyclization and intermolecular dimerization in a solution at pH 2. Pseudo-first-order polymerization kinetics, and relations of apparent rate constant and number average molecular weight with the molar ratio of DA in photopolymerization for pSBMA/DA are unveiled. In a solution at pH 3, PSBMA/DA begins aggregation, kept catechol moieties from premature oxidization, and enabled even deposition on the nitinol substrate. After pH regulation to 8.5, pSBMA/DA extends, and concurrently catechol moieties are activated to interact with the nitinol surface via the formation of bidentate binding. X-ray photoelectron spectroscopy (XPS) analysis revealed that a shorter pSBMA/DA chain with higher catechol content provides more anchoring sites to enhance zwitterionic moieties coverage on substrates. Interestingly, atomic force microscopy (AFM) images revealed a smooth and uniform deposition of pSBMA/DA using the pH-transition method. Strong ionic hydration of pSBMA/DA coating on nitinol surface repels non-specific adsorption of bio-foulants, permitting excellent antifouling properties. Zwitterion-modified nitinol achieved a reduction rate of 99.9% against Escherichia coli and Staphylococcus aureus attachment. In addition, pSBMA/DA exhibits a robust antifouling performance to NIH 3T3 mouse fibroblasts in culture media after incubation for 24 h. Overall, the pSBMA/DA coating via pH transition approach opens up a promising strategy to facilitate uniform surface functionalization for antifouling and coating technology.

Thermomagnetic-Responsive Self-Folding Microgrippers for Improving Minimally Invasive Surgical Techniques and Biopsies.

Traditional open surgery complications are typically due to trauma caused by accessing the procedural site rather than the procedure itself. Minimally invasive surgery allows for fewer complications as microdevices operate through small incisions or natural orifices. However, current minimally invasive tools typically have restricted maneuverability, accessibility, and positional control of microdevices. Thermomagnetic-responsive microgrippers are microscopic multi-fingered devices that respond to temperature changes due to the presence of thermal-responsive polymers. Polymeric devices, made of poly(N-isopropylacrylamide-co-acrylic acid) (pNIPAM-AAc) and polypropylene fumarate (PPF), self-fold due to swelling and contracting of the hydrogel layer. In comparison, soft metallic devices feature a pre-stressed metal bilayer and polymer hinges that soften with increased temperature. Both types of microdevices can self-actuate when exposed to the elevated temperature of a cancerous tumor region, allowing for direct targeting for biopsies. Microgrippers can also be doped to become magnetically responsive, allowing for direction without tethers and the retrieval of microdevices containing excised tissue. The smaller size of stimuli-responsive microgrippers allows for their movement through hard-to-reach areas within the body and the successful extraction of intact cells, RNA and DNA. This review discusses the mechanisms of thermal- and magnetic-responsive microdevices and recent advances in microgripper technology to improve minimally invasive surgical techniques.

pH Responsive Antibacterial Hydrogel Utilizing Catechol-Boronate Complexation Chemistry.

Bacteria such as Methicillin-resistant Staphylococcus aureus (MRSA) causes acidic microenvironment during infection. A biomaterial that exhibits tunable antimicrobial property in a pH dependent manner is potentially attractive. Herein, we presented a novel antibacterial hydrogel consisting of pH responsive and reversible catechol-boronate linkage formed between intrinsically bactericidal chlorinated catechol (catechol-Cl) and phenylboronic acid. Fourier transformed infrared spectroscopy (FTIR), oscillatory rheometry, and Johnson Kendall Roberts (JKR) contact mechanics testing confirmed the formation and dissociation of the complex in a pH dependent manner. When the hydrogel was treated with an acidic buffer (pH 3), the hydrogel exhibited excellent antimicrobial property against multiple strains of Gram-positive and negative bacteria including MRSA (up to 4 log10 reduction from 108 colony forming units/mL). At an acidic pH, catechol-Cl was unbound from the phenylboronic acid and available for killing bacteria. Conversely, when the hydrogel was treated with a basic buffer (pH 8.5), the hydrogel lost its antimicrobial property but also became non-cytotoxic. At a basic pH, the formation of catechol-boronate complex effectively reduce the exposure of the cytotoxic catechol-Cl to the surrounding. When further incubating the hydrogel in an acidic pH, the reversible complex dissociated to re-expose catechol-Cl and the hydrogel recovered its antibacterial property. Overall, the combination of catechol-Cl and phenylboronic acid provide a new strategy for designing hydrogels with pH responsive antibacterial activity and reduced cytotoxicity.

Effect of Conductivity on In Situ Deactivation of Catechol-Boronate Complexation-Based Reversible Smart Adhesive.

To reduce the need for elevated electrical potential to deactivate catechol-based smart adhesive and preserve its reversibility, conductive 1-pyrenemethyl methacrylate (PyMA) was incorporated into a catechol and phenylboronic acid-containing adhesive coating immobilized on aluminum (Al) discs. Electrochemical impedance spectroscopy (EIS) indicated that incorporation of 26 mol % of PyMA reduced ionic resistance (Rs) and charge-transfer resistance (Rc) of the coating from over 22 Ω/mm2 to 5.9 and 1.2 Ω/mm2, respectively. A custom-built Johnson-Kendall-Roberts (JKR) contact mechanics test setup was used to evaluate the adhesive property of the coating with in situ applied electricity using a titanium (Ti) sphere both as a test substrate as well as the cathode for application of electricity and the Al disc as the anode. The adhesive coating demonstrated over 95% reduction in the adhesive property when electricity (1-2 V) was applied while the adhesive was in direct contact with the Ti surface. The addition of PyMA enables the deactivation of the adhesive using a voltage as low as 1 V. Both cyclic voltammetry (CV) and attenuated total reflection-Fourier transform infrared (ATR-FTIR) spectra confirmed the formation of catechol-boronate complexation through electrochemical stimulation. Breaking the complex with an acidic buffer (pH 3) recovered the catechol for strong wet adhesion and the coating could be repeatedly deactivated and reactivated using low electrical potential for up to five cycles. Incorporation of both conductive PyMA and boronic acid as the temporary protecting group was required to achieve rapidly switchable adhesive that could be deactivated with low applied voltage.

Electroactive Polymeric Composites to Mimic the Electromechanical Properties of Myocardium in Cardiac Tissue Repair.

Due to the limited regenerative capabilities of cardiomyocytes, incidents of myocardial infarction can cause permanent damage to native myocardium through the formation of acellular, non-conductive scar tissue during wound repair. The generation of scar tissue in the myocardium compromises the biomechanical and electrical properties of the heart which can lead to further cardiac problems including heart failure. Currently, patients suffering from cardiac failure due to scarring undergo transplantation but limited donor availability and complications (i.e., rejection or infectious pathogens) exclude many individuals from successful transplant. Polymeric tissue engineering scaffolds provide an alternative approach to restore normal myocardium structure and function after damage by acting as a provisional matrix to support cell attachment, infiltration and stem cell delivery. However, issues associated with mechanical property mismatch and the limited electrical conductivity of these constructs when compared to native myocardium reduces their clinical applicability. Therefore, composite polymeric scaffolds with conductive reinforcement components (i.e., metal, carbon, or conductive polymers) provide tunable mechanical and electroactive properties to mimic the structure and function of natural myocardium in force transmission and electrical stimulation. This review summarizes recent advancements in the design, synthesis, and implementation of electroactive polymeric composites to better match the biomechanical and electrical properties of myocardial tissue.

Climbing robots in a sticky situation.

Mussel-inspired electro-responsive adhesive hydrogels enable robot climbing on conductive surfaces.

Oxidation Chemistry of Catechol Utilized in Designing Stimuli-Responsive Adhesives and Antipathogenic Biomaterials.

Mussel foot proteins (Mfps) contain a large amount of the catecholic amino acid, DOPA, allowing the marine organism to anchor themselves onto various surfaces in a turbulent and wet environment. Modification of polymers with catechol imparts these materials with a strong, wet adhesive property. The oxidation chemistry and oxidation state of catechol are critical to the design of synthetic adhesives and biomaterials. In this Mini-Review, the effect of catechol oxidation state on adhesion, oxidation-mediated catechol cross-linking, and the generation of reactive oxygen species (ROS) during catechol oxidation are reviewed. Finally, the tuning of catechol oxidation state in designing stimuli-responsive adhesives and the utilization of ROS byproducts for antimicrobial and antiviral applications are reviewed.

Catechol-Based Antimicrobial Polymers.

Catechol is a key constituent in mussel adhesive proteins and is responsible for strong adhesive property and crosslinking formation. Plant-based polyphenols are also capable of chemical interactions similar to those of catechol and are inherently antimicrobial. This review reports a series of catechol-based antimicrobial polymers classified according to their antimicrobial mechanisms. Catechol is utilized as a surface anchoring group for adhering monomers and polymers of known antimicrobial properties onto various types of surfaces. Additionally, catechol's ability to form strong complexes with metal ions and nanoparticles was utilized to sequester these antimicrobial agents into coatings and polymer matrices. During catechol oxidation, reactive oxygen species (ROS) is generated as a byproduct, and the use of the generated ROS for antimicrobial applications was also introduced. Finally, polymers that utilized the innate antimicrobial property of halogenated catechols and polyphenols were reviewed.

Antimicrobial Property of Halogenated Catechols.

Bacterial infection associated with multidrug resistance (MDR) bacteria is increasingly becoming a significant public health risk. Herein, we synthesized a series of halogenated dopamine methacrylamide (DMA), which contains a catechol side chain modified with either chloro-, bromo-, or iodo-functional group. Catechol is a widely used adhesive moiety for designing bioadhesives and coating. However, the intrinsic antimicrobial property of catechol has not been demonstrated before. These halogenated DMA were incorporated into hydrogels, copolymers, and coatings and exhibited more than 99% killing efficiencies against Gram-positive Staphylococcus aureus and Gram-negative Escherichia coli. More importantly, hydrogel containing chlorinated DMA demonstrated broad-spectrum antimicrobial activities towards multiple MDR bacteria, which included methicillin resistant S. aureus (MRSA), vancomycin resistant enterococci (VRE), multi antibiotics resistant Pseudomonas aeruginosa (PAER), multi antibiotics resistant Acinetobacter baumannii (AB) and carbapenem resistant Klebsiella pneumoniae (CRKP). These hydrogels also demonstrated the ability to kill bacteria in a biofilm while exhibiting low cytotoxic. Based on molecular docking and molecular dynamics simulation, Cl-functionalized catechol can potentially inhibit bacterial fatty acid synthesis at the enoyl-acyl carrier protein reductase (FabI) step. The combination of moisture-resistant adhesive property, inherent antimicrobial property, and the versatility of incorporating halogenated DMA into different polymeric materials greatly enhanced the potential for using these monomers for designing multifunctional bioadhesives and coatings.

Controlling the Release of Hydrogen Peroxide from Catechol-Based Adhesive Using Silica Nanoparticle.

Catechol-based bioadhesives generate hydrogen peroxide (H2O2) as a byproduct during the curing process. H2O2 can have both beneficial and deleterious effects on biological systems depending on its concentration. To control the amount of H2O2 released from catechol-containing polyethylene glycol-based adhesive (PEG-DA), adhesive was formulated with silica nanoparticles (SiNP) prepared with increased porosity and acid treatment to increase Si-OH surface content. These SiNP demonstrated increased surface area, which promoted interaction with catechol and resulted in increased cure rate, bulk mechanical properties and adhesive properties of PEG-DA. Most importantly, SiNP demonstrated a 50% reduction in the released H2O2 while improving the cell viability and proliferation of three primary cell types, including rat dermal fibroblasts, human epidermal keratinocytes, and human tenocytes. Additionally, SiNP degraded into soluble Si, which also contributed to increased cell proliferation. Incorporation of porous and acid-treated SiNP can be a useful approach to simultaneously modulate the concentration of H2O2 while increasing the adhesive performance of catechol-based adhesives.

Design of pH-responsive SAP polymer for pore solution chemistry regulation and crack sealing in cementitious materials.

The crack development is considered to be one of the most severe threats to the durability of concrete infrastructure. This study aims to enhance the durability performance of cementitious material with the pH-responsive Superabsorbent Polymer (SAP). The SAP was synthesized with acrylic acid (AA)-methyl acrylate (MA) precursors, and three type samples with different crosslinking levels were prepared. The examination on the pH sensitivity indicated that the swelling capacity of the prepared SAP would first increase and then decrease with solution alkalinity, and the peak swelling potential was achieved around pH value of 12 for all the three type SAP with solution/gel mass ratio of 500. Further examination indicated the alkalinity of the buffer solution was reduced during the adsorption test, which can be caused by the hydrolysis of the amide groups and the crosslinker. Besides that, it was also found the solution/gel ratio and the Ca(OH)2 content could affect the swelling potential of the SAP. After that, the performance tests were conducted for the evaluation of concrete with SAP. A wax-coating protocol for the SAP was designed by using the hot-water method to prevent its swelling during mixing process. It was found that the strength reduction for samples with wax-coated SAP was insignificant compared to that of the control samples. Furthermore, durability tests supported the wax-shell could be broken by the crack propagation in concrete. And further experimental studies are needed to optimize the wax-size and shell thickness for enhanced self-sealing efficiency.

Biomimetic hydrogels with spatial- and temporal-controlled chemical cues for tissue engineering.

Biomimetic hydrogels have emerged as the most useful tissue engineering scaffold materials. Their versatile chemistry can recapitulate multiple physical and chemical features to integrate cells, scaffolds, and signaling molecules for tissue regeneration. Due to their highly hydrophilic nature hydrogels can recreate nutrient-rich aqueous environments for cells. Soluble regulatory molecules can be incorporated to guide cell proliferation and differentiation. Importantly, the controlled dynamic parameters and spatial distribution of chemical cues in hydrogel scaffolds are critical for cell-cell communication, cell-scaffold interaction, and morphogenesis. Herein, we review biomimetic hydrogels that provide cells with spatiotemporally controlled chemical cues as tissue engineering scaffolds. Specifically, hydrogels with temporally controlled growth factor-release abilities, spatially controlled conjugated bioactive molecules/motifs, and targeting delivery and reload properties for tissue engineering applications are discussed in detail. Examples of hydrogels that possess clinically favorable properties, such as injectability, self-healing ability, stimulus-responsiveness, and pro-remodeling features, are also covered.

In Situ Deactivation of Catechol-Containing Adhesive Using Electrochemistry.

Marine mussels secret catechol-containing adhesive proteins that enable these organisms to bind to various surfaces underwater. Synthetic mimics of these proteins have been created to function as adhesives and coatings for a wide range of applications. Here, we demonstrated the use of in situ electrical field stimulation to deactivate the adhesive property of catechol-containing adhesive that is in direct contact with a surface. Johnson-Kendall-Roberts (JKR) contact mechanics test was performed using a titanium (Ti) sphere in the presence of a pH 7.5 aqueous buffer. The Ti sphere also served as a conductive electrode for applying electricity to the adhesive, while a platinum (Pt) wire served as the counter electrode. Work of adhesion (Wadh) decreased with increased levels of applied voltage and current, exposure time to the applied electricity, and salt concentration of the interfacial buffer. Application of 9 V for 1 min completely deactivated the adhesive. UV-vis diffuse reflectance spectra and tracking of catechol oxidation byproduct, hydrogen peroxide, confirmed that catechol was oxidized as a result of applied electricity. Contact mechanics testing further confirmed that the Young's modulus of the adhesive increased by nearly 4 folds at the interface as a result of oxidative cross-linking, even though the modulus of the bulk of the adhesive was unaffected by applied electricity. The accumulation of hydroxyl ions near the cathode increased the local solution pH, which promoted oxidation-induced cross-linking of catechol and subsequently decreased its adhesive property. Tuning adhesive properties through in situ electrochemical oxidation provides on-demand control over the adhesive, which will potentially add another dimension in designing synthetic mimics of mussel adhesive proteins.

Correlating the mass and mechanical property changes during the degradation of PEG-based adhesive.

Change in mechanical property of a degrading adhesive is critical to its performance. However, characterization of degradation behavior is often limited to tracking its mass loss. 4-armed PEG end modified with dopamine (PEG-DA) was used as a model bioadhesive to correlate its change in mass with change in mechanical property. Shear modulus (G) was calculated based on the mass and average molecular weight between crosslinks ( M ¯ c ) of PEG-DA, while the storage modulus (G') was determined by oscillatory rheometry. G decreased slowly within the first week of degradation (10% reduction by week 2), while G' decreased by 60% during the same period. This large discrepancy is due to the partially disconnected and elastically ineffective PEG polymer, which is trapped within the adhesive network. This resulted in minimal mass change and higher calculated G value during the earlier time points. Therefore, tracking mass loss profile alone is inadequate to completely describe the degradation behavior of an adhesive. Additionally, PEG-DA was coated onto magnetoelastic (ME) sensors, and the change in the resonance amplitude of the sensor corresponded well with dry mass loss of PEG-DA. ME sensing provide a non-destructive method to track the mass loss of the coated adhesive.

Iron Magnetic Nanoparticle-Induced ROS Generation from Catechol-Containing Microgel for Environmental and Biomedical Applications.

Reactive oxygen species (ROS) can degrade organic compounds and function as a broad-spectrum disinfectant. Here, dopamine methacrylamide (DMA) was used to prepare catechol-containing microgels, which can release ROS via metal-catechol interaction. A combination of the microgel and iron magnetic nanoparticle (FeMNP) significantly reduced the concentration of four organic dyes (Alizarin Red S, Rhodamine B, Crystal Violet, and Malachite Green) and an antibiotic drug, ciprofloxacin, dissolved in solution. Degradation of dye occurred across a wide range of pH levels (pH 3-9). This simple combination was also antimicrobial against both Escherichia coli and Staphylococcus aureus. Electron paramagnetic resonance spectroscopy (EPR) results indicate that singlet oxygen was generated during the reaction between catechol and FeMNP at both pH 3 and 7.4, which was responsible for the degradation of organic compounds and bactericidal features of the microgel. Unlike autoxidation that only occurs at a neutral to basic pH, FeMNP-induced catechol oxidation generated singlet oxygen over a wide range of pH level. Additionally, catechol chelates heavy metal ions, resulting in their removal from solution and repurposed these metal ions for dye degradation. This multifunctional microgel can potentially be used for environmental applications for the removal of organic pollutants and heavy metal ions from wastewater, as well as reducing bacterial infection in biomedical applications.