PdO-Nanoparticle-Embedded Carbon Nanotube Yarns for Wearable Hydrogen Gas Sensing Platforms with Fast and Sensitive Responses.

Hydrogen (H2) gas has recently become a crucial energy source and an imperative energy vector, emerging as a powerful next-generation solution for fuel cells and biomedical, transportation, and household applications. With increasing interest in H2, safety concerns regarding personal injuries from its flammability and explosion at high concentrations (>4%) have inspired the development of wearable pre-emptive gas monitoring platforms that can operate on curved and jointed parts of the human body. In this study, a yarn-type hydrogen gas sensing platform (HGSP) was developed by biscrolling of palladium oxide nanoparticles (PdO NPs) and spinnable carbon nanotube (CNT) buckypapers. Because of the high loading of H2-active PdO NPs (up to 97.7 wt %), when exposed to a flammable H2 concentration (4 vol %), the biscrolled HGSP yarn exhibits a short response time of 2 s, with a high sensitivity of 1198% (defined as ΔG/G0 × 100%). Interestingly, during the reduction of PdO to Pd by H2 gas, the HGSP yarn experienced a decrease in diameter and corresponding volume contraction. These excellent sensing performances suggest that the fabricated HGSP yarn could be applied to a wearable gas monitoring platform for real-time detection of H2 gas leakage even over the bends of joints.

Bidirectional Core Sandwich Structure of Reduced Graphene Oxide and Spinnable Multiwalled Carbon Nanotubes for Electromagnetic Interference Shielding Effectiveness.

Thin and flexible electromagnetic shielding materials have recently emerged because of their promising applications in drones, portable electronics, military defense facilities, etc. This research develops an electromagnetic interference (EMI) shielding material by a bidirectional lattice sandwich structure (BLSS), which is formed by liquid crystalline graphene oxide (LCGO) and an orthogonal pattern of spinnable multiwalled (OPSM) nanotubes in consideration of the movement of electromagnetic waves. The average EMI shielding effectiveness (SE) of the developed material with 0.5 wt % reduced LCGO (r-LCGO) and an OPSM nanotube composed of 64 layers was approximately 66.1 dB in the X-band frequency range (8.2-12.4 GHz, wavelength: 3.5-2.5 cm), which corresponds to a shielding efficiency of 99.9999%. Also, its absorption effectiveness is 99.7% of the total EMI SE, indicating that it has a remarkable ability to prevent secondary damage induced by EM reflection. The specific EMI SE (SSE/t) of the composite material considering the contribution of thickness (t) ranged from 21 953 to 2259 dB cm2/g.

Electrodeposition of α-MnO2/γ-MnO2 on Carbon Nanotube for Yarn Supercapacitor.

Yarn supercapacitors have attracted renewed interest as promising energy storage for wearable devices due to their lightweight, long cycling lifetime and excellent weavability. There has been much effort to fabricate high performance yarn supercapacitor by depositing pseudo-capacitive materials on the outer surface of the carbon fibers. However, a key challenge still remains to achieve high capacitance and high mass loading without sacrificing the cycling stability. Herein, we perform a phase-controlled of MnO2 at various deposition temperatures with ultrahigh mass loading of 11 mg/cm2 on a MWNT sheets and fabricate it to yarn structure to achieve high capacitance without decreasing in the electrochemical performance. The structure of optimized sample (MnO2/CNTs-60, deposition at 60 °C) consists of the composite of primary α-MnO2 nanosheets and secondary γ-MnO2 nanoparticles. The heteronanostructures of MnO2 provide facile ionic and electric transport in the yarn electrode, resulting in improvement of electrochemical performance and cycling stability. The MnO2/CNTs-60 yarn electrode with ultrahigh mass loading delivers a high areal capacitance of 3.54 F/cm2 at 1 mA/cm2 and an excellent rate capability. Finally, the MnO2/CNTs-60 device exhibits an outstanding high areal energy density of 93.8 µWh/cm2 at the power density of 193 µW/cm2, which is superior to previously reported symmetric yarn supercapacitors.

Highly twisted supercoils for superelastic multi-functional fibres.

Highly deformable and electrically conductive fibres with multiple functionalities may be useful for diverse applications. Here we report on a supercoil structure (i.e. coiling of a coil) of fibres fabricated by inserting a giant twist into spandex-core fibres wrapped in a carbon nanotube sheath. The resulting supercoiled fibres show a highly ordered and compact structure along the fibre direction, which can sustain up to 1,500% elastic deformation. The supercoiled fibre exhibits an increase in resistance of 4.2% for stretching of 1,000% when overcoated by a passivation layer. Moreover, by incorporating pseudocapacitive-active materials, we demonstrate the existence of superelastic supercapacitors with high linear and areal capacitance values of 21.7 mF cm-1 and 92.1 mF cm-2, respectively, that can be reversibly stretched by 1,000% without significant capacitance loss. The supercoiled fibre can also function as an electrothermal artificial muscle, contracting 4.2% (percentage of loaded fibre length) when 0.45 V mm-1 is applied.

Carbon nanotubes-elastomer actuator driven electrothermally by low-voltage.

Electroactive polymers (EAPs) have attracted attention in many fields such as robotics, sensors devices and biomedical devices. However, the practical application of these actuators has still problems due to incomplete reversibility and high applied voltage. In order to overcome these problems, in this study, we have shown actuator based on phase transition that is consisted of the carbon nanotubes yarn infiltrated with the mixture of elastomer and methanol. Our electrothermally driven hybrid coiled yarn muscle provides a work capacity of 0.49 kJ kg-1 and a tensile contraction of 30.5% within ∼3 s on an applied stress of 3.1 MPa at an applied DC voltage of 5 V. The maximum work capacity is under isobaric 23.4 MPa, which is 110 times that of typical mammalian skeletal muscles. This actuator may serve as a promising candidate for the practical use in soft robotics.

Magnetic torsional actuation of carbon nanotube yarn artificial muscle.

Magnetically driven torsional actuation of a multiwalled carbon nanotube (MWNT) yarn was realized by first biscrolling NdFeB magnetic particles into helical yarn corridors to make a magnetic MWNT yarn. The actuating device comprised a pristineMWNT yarn that was connected to the magnetic MWNT yarn, with a paddle attached between these yarns. The application of a magnetic field reversibly drove torsional actuation of up to 80° within ∼0.67 seconds. This magnetic actuator was remotely powered, and its actuation stroke was the same when the muscle array was at 20 °C and at -100 °C.

Weavable asymmetric carbon nanotube yarn supercapacitor for electronic textiles.

Asymmetric supercapacitors are receiving much research interests due to their wide operating potential window and high energy density. In this study, we report the fabrication of asymmetrically configured yarn based supercapacitor by using liquid-state biscrolling technology. High loading amounts of reduced graphene oxide anode guest (90.1 wt%) and MnO2 cathode guest (70 wt%) materials were successfully embedded into carbon nanotube yarn host electrodes. The resulting asymmetric yarn supercapacitor coated by gel based organic electrolyte (PVDF-HFP-TEA·BF4) exhibited wider potential window (up to 3.5 V) and resulting high energy density (43 µW h cm-2). Moreover, the yarn electrodes were mechanically strong enough to be woven into commercial textiles. The textile supercapacitor exhibited stable electrochemical energy storage performances during dynamically applied deformations.

Buckling Structured Stretchable Pseudocapacitor Yarn.

Cable-type stretchable electrochemical pseudocapacitors based on multi-walled carbon nanotube (MWCNT) sheets and two different metal oxide nanopowders (NP), i.e., MnO2 and RuO2 are developed using a newly-devised dry painting method to mechanically fix the NP to the elastic rubber-based MWCNT electrode substrate, resulting in a porous buckling structured pseudocapacitor yarn. Highly stretchable stylene-ethylene/butylene-stylene (SEBS) is used as the supporting elastomeric core for wrapping with the MWCNT sheets and the electroactive NP. The dry painting can successfully deposit NP on the soft SEBS surface, which is normally an unfavorable substrate for coating alien materials. The resulting yarn-type pseudocapacitor, composed of eight-layered MWCNT sheets, three-layered RuO2, and two-layered MnO2, showing a diameter of approximately 400 µm with a porous buckling structure, records a specific capacitance of 25 F g-1. After being stretched by 200% in strain with no sacrifice of the porous buckling structure, the cable-type stretchable electrochemical pseudocapacitor yarn retains its electrical capacity, and is potentially applicable to energy storage devices for wearable electronics.