Slow magnetic relaxation in mononuclear octa-coordinate Fe(II) and Co(II) complexes from a Bpybox ligand.

Two 3d transition metal mononuclear complexes, [(FeL2)(ClO4)2]2·CH3CN (1) and (CoL2)(ClO4)2·2CH3CN (2), have been prepared from a rigid tetradentate bpybox (L = 6,6'-bis(2,5-dihydrooxazol-4-yl)-2,2'-bipyridine) ligand. Single crystal X-ray diffraction analyses together with the help of calculations show that both compounds are octa-coordinate. Direct current magnetic studies reveal their significant magnetic anisotropy. Impressively, field-induced relaxation of magnetism is observed in the two complexes and the apparent anisotropy barriers are 14.1 K for 1 and 21.6 K for 2, respectively. Theoretical calculations reveal that two Fe(II) centers in 1 have small negative D values of -4.897 and -4.825 cm-1 and relatively small E values of 0.646 and 0.830 cm-1, indicating a uniaxial magnetic anisotropy. In contrast, the D and E values in the Co(II) center of 2 are 46.42 cm-1 and 11.51 cm-1, featuring a rhombic anisotropy. This work demonstrates that field-induced slow magnetic relaxation in 3d transition metal complexes with high coordination numbers can be manipulated through rigid ligand design.

Comparison of the degradations of diphenamid by homogeneous photolysis and heterogeneous photocatalysis in aqueous solution.

In this work, the homogeneous and heterogeneous degradations of diphenamid (DPA) in aqueous solution were conducted by direct photolysis with UVC (254nm) and by photocatalysis with TiO(2)/UVA (350nm), and the experimental results were compared. It was found that the homogeneous photolysis by UVC irradiation alone was quite efficient to degrade DPA up to 100% after 360min, but was very inefficient to mineralize its intermediates in terms of dissolved organic carbon reduction of only 8%. In contrast, the heterogeneous photocatalysis with TiO(2)/UVA showed relatively a lower degree of DPA degradation (51%), but a higher degree of its mineralization (11%) after 360min. These results reveal that the photocatalysis process has relatively poor selectivity to degrade different compounds including various intermediates from the DPA degradation, which is beneficial to its mineralization. In addition, over 20 intermediates were identified by LC-MS and (1)H NMR analyses. Based on the identified intermediates, the reaction mechanisms and the detailed pathways of the DPA degradation by photolysis and photocatalysis were proposed, and are presented in this paper.

Effects of structure of anodic TiO(2) nanotube arrays on photocatalytic activity for the degradation of 2,3-dichlorophenol in aqueous solution.

In this study titanium dioxide nanotube (TNT) arrays were prepared by an anodic oxidation process with post-calcination. The morphology and structure of the TNT films were studied by field-emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Photocatalytic activity of the TNT films was evaluated in terms of the degradation of 2,3-dichlorophenol in aqueous solution under UV light irradiation. The effects of the nanotube structure including tube length and tube wall thickness, and crystallinity on the photocatalytic activity were investigated in detail. The results showed that the large specific surface area, high pore volume, thin tube wall, and optimal tube length would be important factors to achieve the good performance of TNT films. Moreover, the TNT films calcined at 500 degrees C for 1h with the higher degree of crystallinity exhibited the higher photocatalytic activity than other TNT films calcined at 300 and 800 degrees C. Consequently, these results indicate that the optimization of TiO(2) nanotube structures is critical to achieve the high performance of photocatalytic reaction.

Effects of dissolved oxygen, pH, and anions on the 2,3-dichlorophenol degradation by photocatalytic reaction with anodic TiO(2) nanotube films.

In this study, the highly-ordered TiO(2) nanotube (TNT) arrays on titanium sheets were prepared by an anodic oxidation method. Under UV illumination, the TNT films demonstrated the higher photocatalytic activity in terms of 2,3-dichlorophenol (2,3-DCP) degradation in aqueous solution than the conventional TiO(2) thin films prepared by a sol-gel method. The effects of dissolved oxygen (DO) and pH on the photocatalytic degradation of 2,3-DCP were investigated. The results showed that the role of DO in the 2,3-DCP degradation with the TNT film was significant. It was found that 2,3-DCP in alkaline solution was degraded and dechlorinated faster than that in acidic solution whereas dissolved organic carbon removal presented an opposite order in dependence of pH. In the meantime, some main intermediate products from 2,3-DCP degradation were identified by a (1)H NMR technique to explore a possible degradation pathway. A major intermediate, 2-chlororesorcinol, was identified from the 2,3-DCP decomposition as a new species compared to the findings in previous reports. Photocatalytic deactivation was also evaluated in the presence of individual anions (NO(3)(-), Cl(-), SO(4)(2-), and H(2)PO(4)(-)). The inhibition degree of photocatalytic degradation of 2,3-DCP caused by these anions can be ranked from high to low as SO(4)(2-)>Cl(-)>H(2)PO(4)(-)>NO(3)(-). The observed inhibition effect can be attributed to the competitive adsorption and the formation of less reactive radicals during the photocatalytic reaction.